Super-hydrophobic artificial marble and preparation method thereof

An artificial marble and super-hydrophobic technology, applied in the field of building materials, can solve the problems of increased cost and complicated process, and achieve the effects of increasing added value, simple preparation process and good hydrophobicity

Active Publication Date: 2015-07-08
宝武环科(湛江)资源循环利用有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But above-mentioned two kinds of methods have all increased the technological process of preparation artificial marble, make craft become loaded down with trivial details, cost must increase to some extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-hydrophobic artificial marble and preparation method thereof
  • Super-hydrophobic artificial marble and preparation method thereof
  • Super-hydrophobic artificial marble and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. Preparation of polyfluorinated bisphenol A epoxy acrylate polymer:

[0031] Mix undecafluoro-n-hexan-1-ol (PFHOL) and dicyclohexylmethane diisocyanate (HMDI) with a molar ratio of 1:2, and react at 60°C for 3-5 hours under nitrogen protection, then add the mixture to dimethyl In methyl formamide (DMF) solution, obtain prepolymer solution until solution is clear and transparent;

[0032] Add bisphenol A epoxy acrylate (ACM) (the molar ratio of ACM to prepolymer is 2.07:1) into the prepolymer mixed solution, and the solid content of the solution after mixing is controlled at 85% (w / v), continue Stirring, under the protection of nitrogen, react at 60°C for 12-24h, and remove the solvent from the obtained mixed solution to obtain a polyfluorine-modified bisphenol A epoxy acrylate polymer for future use. The molecular structural formula of described polyfluorine modified bisphenol A epoxy acrylate polymer is as follows figure 1 shown.

[0033] 2. Preparation of superhy...

Embodiment 2

[0039] 1. Preparation of polyfluorinated bisphenol A epoxy acrylate polymer:

[0040] Mix undecafluoro-n-hexan-1-ol (PFHOL) and polymethylene polyphenyl polyisocyanate (PAPI) with a molar ratio of 1:2, and react at 60°C for 3-5 hours under nitrogen protection, then add the mixture In dimethylformamide (DMF) solution, obtain prepolymer solution until solution is clear;

[0041] Add bisphenol A epoxy acrylate (ACM) (the molar ratio of ACM to prepolymer is 2.07:1) into the prepolymer mixed solution, and the solid content of the solution after mixing is controlled at 85% (w / v), continue Stirring, under the protection of nitrogen, react at 60°C for 12-24h, and remove the solvent from the obtained mixed solution to obtain a polyfluorine-modified bisphenol A epoxy acrylate polymer for future use.

[0042] 2. Preparation of superhydrophobic artificial marble:

[0043] The following raw materials are all calculated in parts by weight:

[0044] Get 10 parts of polyfluorine-modified bis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building materials and particularly relates to super-hydrophobic artificial marble which is composed of following components, by weight: 100 parts of unsaturated polyester resin, 0.5-2 parts of a peroxide-type initiator, 0.1-2 parts of an accelerant, 5-30 parts of vinyl-type resin diluent, 5-30 parts of polyvinyl-type resin assistant crosslinker, 100-500 parts of ore slag micro powder, 10-30 parts of a flame retardant, and 3-15 parts of polyfluoro-modified bisphenol A epoxy acrylate polymer. In the invention, the polyfluoro-modified bisphenol A epoxy acrylate polymer, which has a super-hydrophobic function, is employed as a hydrophobic additive to prepare the artificial marble, so that the artificial marble is excellent in hydrophobic performance. A contact angle between the surface of the super-hydrophobic artificial marble and water is 150-170 degrees so that the surface of the super-hydrophobic artificial marble has an excellent self-cleaning function. In addition, the marble in deep color series is high in strength, is good in waterproof performance and is strong in corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a superhydrophobic artificial marble. Background technique [0002] With the development of my country's iron and steel industry, the discharge of blast furnace slag is increasing day by day. According to recent statistics from China United Iron and Steel Network, my country's crude steel output reached 782 million tons in 2013, and 0.3 to 1.2 tons of blast furnace slag was produced per ton of pig iron, which means that hundreds of millions of tons of blast furnace slag were discharged in 2013. Blast furnace slag powder is a scientific research achievement of iron and steel enterprises. It not only solves the pollution of blast furnace slag waste to the environment, but also uses blast furnace slag powder produced from blast furnace slag as raw material in the cement industry, achieving obvious economic benefits. The present invention intends to study the manufacture ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B18/14
CPCY02W30/91
Inventor 徐莉吴新锋童敏周维张红
Owner 宝武环科(湛江)资源循环利用有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap