Solvent-free epoxy coating

An epoxy coating, solvent-free technology, applied in the direction of epoxy resin coatings, anti-corrosion coatings, coatings, etc., can solve problems such as non-compliance with environmental protection, and achieve good construction safety and environmental protection, high safety, and components The effect of formulation science

Inactive Publication Date: 2015-05-27
天津可喜涂料有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In addition to the traditional oil-based coatings, phenolic resin coatings and alkyd resin coatings used in the coatings industry, various high-performance epoxy resin coatings, polyurethane coatings, acrylic coatings and inorganic zinc coatings have been developed on the market, but these All kinds of coatings contain a large amount of organic solvents, which do not meet the requirements of environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent-free epoxy coating
  • Solvent-free epoxy coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A solvent-free epoxy coating, the components of the solvent-free epoxy coating and their weight / number ratios are respectively: 200Kg of low molecular weight epoxy resin; 50-60Kg of reactive diluent; 30Kg of coloring pigment; 15Kg of anti-settling agent ; Defoamer 5Kg; Dispersant 3Kg; Low viscosity amine curing agent 5Kg. The low molecular weight epoxy resin is bisphenol F epoxy resin. Low viscosity amine curing agent is a low viscosity phenolic modified amine curing agent.

Embodiment 2

[0015] A solvent-free epoxy coating, the components of the solvent-free epoxy coating and their weight / number ratios are respectively: 300Kg of low molecular weight epoxy resin; 60Kg of reactive diluent; 45Kg of coloring pigment; 20Kg of anti-settling agent; Foaming agent 7Kg; dispersant 9Kg; low viscosity amine curing agent 12Kg. The low molecular weight epoxy resin is bisphenol F epoxy resin. Low viscosity amine curing agent is a low viscosity phenolic modified amine curing agent.

Embodiment 3

[0017] A solvent-free epoxy coating, the components of the solvent-free epoxy coating and their weight / number ratios are respectively: 240Kg of low molecular weight epoxy resin; 55Kg of reactive diluent; 38Kg of coloring pigment; 18Kg of anti-settling agent; Foaming agent 6Kg; dispersant 7Kg; low viscosity amine curing agent 8Kg. The low molecular weight epoxy resin is bisphenol F epoxy resin. Low viscosity amine curing agent is a low viscosity phenolic modified amine curing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a solvent-free epoxy coating which includes following components, by weight: 200-300 parts of low-molecular-weight epoxy resin, 50-60 parts of a reaction active diluent, 30-45 parts of a coloring pigment, 15-20 parts of an anti-settling agent, 5-7 parts of a defoaming agent, 3-9 parts of a dispersing agent and 5-12 parts of a low-viscosity amine curing agent. The epoxy coating is prepared from the low-molecular-weight epoxy resin, the coloring pigment, the additives and the like through high-speed dispersion and grinding. The epoxy coating is a double-component reaction curing anti-corrosion coating with the low-viscosity modified amine as the curing agent. The epoxy coating is scientific in formula, is high in safety and is excellent in construction safety and environmental protection.

Description

technical field [0001] The invention belongs to the field of epoxy paint, in particular to a solvent-free epoxy paint. Background technique [0002] In addition to the traditional oil-based coatings, phenolic resin coatings and alkyd resin coatings used in the coatings industry, various high-performance epoxy resin coatings, polyurethane coatings, acrylic coatings and inorganic zinc coatings have been developed on the market, but these Such coatings contain a large amount of organic solvents, which do not meet the requirements of environmental protection. Contents of the invention [0003] The object of the present invention is to overcome the deficiencies of the prior art and provide a solvent-free epoxy paint, which has scientific components, high safety, good construction safety and environmental protection. [0004] The present invention solves its technical problem and realizes through the following technical solutions: [0005] A kind of solvent-free epoxy coating,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
CPCC09D163/00C09D5/08C09D7/40
Inventor 金淑花
Owner 天津可喜涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com