Oil resistant rubber material and preparation method thereof

An oil-resistant rubber and fluororubber technology, applied in the polymer field, can solve problems such as poor oil resistance and achieve good sealing effect

Inactive Publication Date: 2015-05-13
LIUZHOU YINGHANG AUTO PARTS
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rubber materials have poor oil resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of oil-resistant rubber material of the present invention is as follows:

[0011] Nitrile rubber 65kg, fluororubber 30kg, octyltin maleate 8kg, glass fiber 2.5kg, stearic acid 1.5kg, light calcium carbonate 0.6kg, magnesium dimethacrylate 4kg, dry oil alkyd resin 2.5kg, Paraffin 1.5kg, dilauryl thiodipropionate 4kg, diacetyl peroxide 1.5kg, zinc oxide 1kg, aluminum oxide 9kg, white carbon black 7kg, antioxidant 1.2kg, sulfur 2kg.

[0012] The preparation method of oil-resistant rubber material of the present invention is as follows:

[0013] The nitrile rubber and fluorine rubber in the formula amount are thinned separately and then mixed evenly and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controlled at 160°C, the vulcanization time is 35 minutes, an...

Embodiment 2

[0015] The formula of oil-resistant rubber material of the present invention is as follows:

[0016] 60kg of nitrile rubber, 35kg of fluororubber, 5kg of octyltin maleate, 2kg of glass fiber, 1kg of stearic acid, 0.5kg of light calcium carbonate, 5kg of magnesium dimethacrylate, 2kg of dry oil alkyd resin, 1kg of paraffin wax, Dilauryl thiodipropionate 3kg, diacetyl peroxide 1kg, zinc oxide 1.2kg, aluminum oxide 8kg, white carbon black 8kg, antioxidant 1.5kg, sulfur 1kg.

[0017] The preparation method of oil-resistant rubber material of the present invention is as follows:

[0018] The nitrile rubber and fluorine rubber in the formula amount are thinned separately and then mixed evenly and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controlled at 150°C, the vulcanization...

Embodiment 3

[0020] The formula of oil-resistant rubber material of the present invention is as follows:

[0021] 70kg of nitrile rubber, 25kg of fluororubber, 10kg of octyltin maleate, 3kg of glass fiber, 2kg of stearic acid, 0.8kg of light calcium carbonate, 3kg of magnesium dimethacrylate, 3kg of dry oil alkyd resin, 2kg of paraffin wax, Dilauryl thiodipropionate 5kg, diacetyl peroxide 2kg, zinc oxide 0.8kg, aluminum oxide 10kg, white carbon black 6kg, antioxidant 0.8kg, sulfur 3kg.

[0022] The preparation method of oil-resistant rubber material of the present invention is as follows:

[0023] The nitrile rubber and fluorine rubber in the formula amount are thinned separately and then mixed evenly and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber, and the mixed rubber is One-stage vulcanization, the vulcanization temperature is controlled at 170°C, the vulcanizati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an oil resistant rubber material. The oil resistant rubber material comprises the following components in parts by weight: 60-70 parts of butadiene-acrylonitrile rubber, 25-35 parts of fluororubber, 5-10 parts of dioctyl tin maleate, 2-3 parts of glass fibers, 1-2 parts of stearic acid, 0.5-0.8 part of light calcium carbonate, 3-5 parts of magnesium dimethacrylate, 2-3 parts of drying oil alkyd resin, 1-2 parts of paraffin, 3-5 parts of dilauryl thiodipropionate, 1-2 parts of diacetyl peroxide, 0.8-1.2 parts of zinc oxide, 8-10 parts of aluminium oxide, 6-8 parts of white carbon black, 0.8-1.5 parts of anti-aging agent and 1-3 parts of sulfur. The invention also provides a preparation method of the oil resistant rubber material. The oil resistant rubber material has good sealability, high temperature resistance and oil resistance and is suitable for sealing automobile gearboxes.

Description

technical field [0001] The invention belongs to the technical field of polymers, and in particular relates to an oil-resistant rubber material. Background technique [0002] Automotive oil seals are precision rubber components with the most complex structure, the highest technical content, and the most widely used rotary seals. Its quality not only affects the sealing performance and service life of the car, but more importantly, affects the driving and safety of the car. The main function of the gearbox oil seal is to prevent lubricating oil from leaking out from the fitting gap between the hole and the shaft, and to prevent dust and impurities from entering the inside. In order to ensure its tightness and working reliability under any working conditions of the car, the oil seal needs to be able to withstand the working conditions of high speed, medium resistance and high and low temperature resistance. Existing rubber materials have poor oil resistance. Contents of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L27/12C08L67/08C08L91/06C08K13/04C08K7/14C08K5/57C08K5/09C08K3/26C08K5/098C08K5/372C08K5/14C08K3/22C08K3/36C08K3/06B29C35/02
CPCC08L9/02B29C35/0233C08L2205/035
Inventor 莫海燕
Owner LIUZHOU YINGHANG AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More