Polysulfonamide permanent flame-retardant heat-insulation warm-keeping fabric sheet and preparation method thereof

A sulfone fiber, permanent technology, applied in the field of sulfone fiber flakes and its preparation, can solve the problems of potential safety hazards, easy falling off, affecting the flame-retardant effect of clothing, etc.

Active Publication Date: 2015-04-29
中芳新材料有限公司 +1
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this flame retardant is easy to fall off when washed, which affects the flame retardant effect of washed clothes and poses a safety hazard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Preparation of flame retardant adhesive solution: 6 kg of ammonium dihydrogen phosphate, a solubilizer composed of 0.5 kg of urea and 0.5 kg of ammonium chloride, added 81 kg of water and stirred evenly to form a flame retardant mixture, added while stirring For 12 kg of acrylate emulsion, add about 0.2 kg of defoamer to eliminate air bubbles, and add an appropriate amount of pH regulator until the flame retardant adhesive solution is neutral.

[0026] (2) 95 kg of PSA fibers and 5 kg of polyester fibers with a melting point of 110°C are evenly opened on the TEMAFA opener.

[0027] (3) The opened fibers are transported to the large bin mixing box by the airflow, and then transported to the coarse opening and loosening box through the corner nail curtain, and then transported to the fine opening and loosening box, and then enter the cotton storage box.

[0028] (4) The fibers of the cotton storage box are transported to the Truetzschler-Erko double-cylinder double-do...

Embodiment 2

[0033] Replace "0.5 kg of urea and 0.5 kg of ammonium chloride solubilizer" in Example 1 with "1 kg of urea", and the others are the same as in Example 1 to obtain the permanent flame-retardant, heat-insulating and warm-keeping polysulfonamide of Example 2 flakes.

Embodiment 3

[0035] Replace "0.5 kg of urea and 0.5 kg of ammonium chloride solubilizer" in Example 1 with "1 kg of ammonium chloride", and the others are the same as in Example 1 to obtain the permanent flame-retardant and insulating sulfonamide of Example 3. Thermal insulation batting.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Basis weightaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polysulfonamide permanent flame-retardant heat-insulation warm-keeping fabric sheet which is prepared from the following raw material components in parts by weight: 90-100 parts of PSA fibers and 0-10 parts of low-melting-point fibers. After being prepared into a fiber net, the raw materials are treated by a flame-retardant adhesive solution to obtain the polysulfonamide permanent flame-retardant heat-insulation warm-keeping fabric sheet. The polysulfonamide permanent flame-retardant heat-insulation warm-keeping fabric sheet has a permanent flame-retardant heat-insulation warm-keeping function, also can be used for guaranteeing the fabric sheet to have a good high-temperature-resistant and flame-retardant effect and a washing-resistant effect, guaranteeing the elasticity and fluffy restoration after washing of the fabric sheet.

Description

technical field [0001] The invention relates to an aramid sulfone fiber flake and a preparation method thereof, in particular to an aramid sulfone fiber permanent flame-retardant, heat-insulating and warm-keeping flake and a preparation method thereof. Background technique [0002] In high temperature, electric arc, steel and other workplaces and ground combat areas, operators need to wear high temperature and flame retardant clothing when working. Especially when the temperature is lower in the peripheral environment or when the weather is cold, in addition to the high-temperature-resistant and flame-retardant clothes of the outer layer, it is also necessary to configure cold-proof clothing for the operating personnel. At present, most of the clothing thermal insulation materials used in the market are polyester spray-bonded cotton, down and other materials, which can also play a good role in thermal insulation. However, these materials have no flame-retardant function, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/02D04H1/4382D04H1/587
Inventor 钱春芳胡征宇沈剑
Owner 中芳新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com