Oxygen permeation membrane materials with stable oxygen flux in carbon dioxide-containing atmosphere

A carbon dioxide, oxygen-permeable membrane technology, applied in semi-permeable membrane separation, membrane technology, chemical instruments and methods, etc., can solve problems such as the instability of oxygen-permeable membrane materials, and improve the stability of unstable or H2S and other reducing gases. The effect of stabilizing and stabilizing oxygen flux

Active Publication Date: 2015-04-29
NANJING UNIV OF TECH
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to improve the existing oxygen permeable membrane material in CO 2 The shortcoming of being unstable under the atmosphere provides a class of oxygen permeable membrane materials with stable oxygen flux in the atmosphere containing carbon dioxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oxygen permeation membrane materials with stable oxygen flux in carbon dioxide-containing atmosphere
  • Oxygen permeation membrane materials with stable oxygen flux in carbon dioxide-containing atmosphere
  • Oxygen permeation membrane materials with stable oxygen flux in carbon dioxide-containing atmosphere

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: SrFe 0.8 Cr 0.2 o 3-δ Preparation of Oxygen Permeable Membrane

[0024] SrFe 0.8 Cr 0.2 o 3-δ The specific preparation process of the oxygen permeable membrane diaphragm is mainly divided into two steps: SrFe 0.8 Cr 0.2 o 3- δ Powder preparation and SrFe 0.8 Cr 0.2 o 3-δ Membrane preparation.

[0025] SrFe 0.8 Cr 0.2 o 3-δ The method adopted for the preparation of the powder is EDTA-CA sol-gel combined complexation method. First, by SrFe 0.8 Cr 0.2 o 3-δ Stoichiometric ratio was weighed Sr(NO 3 ) 2 , Fe(NO 3 ) 3 , Cr(NO 3 ) 3Put the particles into a beaker, stir and heat, wait until all the particles are dissolved, add EDTA, CA two complexing agents, and add NH 3 ·H 2 O adjusts the pH of the solution to around 6. Secondly, put the beaker on the heating table and keep stirring until it becomes a sol, and put it in an oven at 250°C for 5 hours to obtain SrFe 0.8 Cr 0.2 o 3-δ precursors. Finally, the SrFe 0.8 Cr 0.2 o 3-δ Put th...

Embodiment 2

[0028] Example 2: SrFe 0.9 W 0.1 o 3-δ Preparation of Oxygen Permeable Membrane

[0029] SrFe 0.9 W 0.1 o 3-δ The specific preparation process of the oxygen permeable membrane diaphragm is mainly divided into two steps:

[0030] SrFe 0.9 W 0.1 o 3-δ Powder preparation and SrFe 0.9 W 0.1 o 3-δ Membrane preparation.

[0031] SrFe 0.9 W 0.1 o 3-δ The method adopted for the preparation of the powder is EDTA-CA sol-gel combined complexation method. First, by SrFe 0.9 W 0.1 o 3-δ Stoichiometric ratio was weighed Sr(NO 3 ) 2 , Fe(NO 3 ) 3 , (NH 4 ) 10 W 12 o 41 Put the particles into a beaker, stir and heat, wait until all the particles are dissolved, add EDTA, CA two complexing agents, and add NH 3 ·H 2 O to adjust the pH of the solution to 6.5. Secondly, put the beaker on the heating table and keep stirring until it becomes a sol, and put it in an oven at 250°C for 3 hours to obtain SrFe 0.9 W 0.1 o 3-δ precursors. Finally, the SrFe 0.9 W 0.1 o 3...

Embodiment 3

[0034] Example 3: CaFe 0.95 Zr 0.05 o 3-δ Preparation of Oxygen Permeable Membrane

[0035] CaFe 0.95 Zr 0.05 o 3-δ The specific preparation process of the oxygen permeable membrane diaphragm is mainly divided into two steps:

[0036] CaFe 0.95 Zr 0.05 o 3-δ Powder preparation and CaFe 0.95 Zr 0.05 o 3-δ Membrane preparation.

[0037] CaFe 0.95 Zr 0.05 o 3-δ The method adopted for the preparation of the powder is EDTA-CA sol-gel combined complexation method. First, by CaFe 0.95 Zr 0.05 o 3-δ Stoichiometric ratio was weighed Ca(NO 3 ) 2 , Fe(NO 3 ) 3 , Zr(NO 3 ) 4 Put the particles into a beaker, stir and heat, wait until all the particles are dissolved, add EDTA, CA two complexing agents, and add NH 3 ·H 2 O to adjust the pH of the solution to 6. Secondly, put the beaker on the heating table and keep stirring until it becomes a sol, and put it in an oven at 250°C for 6 hours to obtain CaFe 0.95 Zr 0.05 o 3-δ precursors. Finally, the CaFe 0.95 Zr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to oxygen permeation membrane materials with stable oxygen flux in a carbon dioxide-containing atmosphere. The oxygen permeation membrane materials are characterized in that the structural general formula is AB1-yMyO3-delta, wherein A is one or a mixture of Sr or Ca in alkali earth metal ions; B refers to the transition metal ion Fe; M refers to one or several in Cr, Mo, Nb, Ti, W or Zr; and y is more than or equal to 0.05 and less than or equal to 0.2. The mixed conductor oxygen permeation membrane materials of the type can simultaneously have a certain oxygen permeation flux and CO2 poisoning resistance in a temperature range of 600-900 DEG C. Therefore, a material with a certain oxygen permeation flux can be provided in the presence of CO2, so that the oxygen permeation membrane can have industrial application values in oxygen-enriched combustion and membrane reactors.

Description

technical field [0001] The invention belongs to the technical field of mixed conductor oxygen-permeable membrane, relates to a kind of oxygen-permeable membrane material with stable oxygen flux in an atmosphere containing carbon dioxide, and is a kind of oxygen-permeable membrane material with certain oxygen flux and anti-CO 2 properties of perovskite materials, specifically related to the CO 2 Under the existing conditions, the perovskite structure can be kept unchanged, and there is also an oxygen-permeable membrane material that can maintain a stable oxygen flux without decreasing. Background technique [0002] Oxygen permeable membrane is a kind of high temperature, especially when the temperature is greater than 700 ° C, it has both electronic and oxygen ion conductivity characteristics, and can be at a certain temperature, when there is oxygen partial pressure on both sides of the dense oxygen permeable membrane, Oxygen will be conducted in the form of oxygen ions thr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D71/02B01D67/00B01D53/22
Inventor 邵宗平张振宝陈登洁
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com