A three-dimensional ordered macroporous fe 2 o 3 Preparation method and application of carbon airgel electrode

A carbon aerogel, three-dimensional ordered technology, applied in the field of water treatment, to achieve the effects of accelerating electrical conductivity, reducing energy consumption, and increasing mass transfer rate

Active Publication Date: 2016-11-09
TONGJI UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, we propose to use CA as the substrate to construct three-dimensional ordered macroporous Fe 2 o 3 novel cathode materials, and so far there are few reports utilizing 3DOM-Fe 2 o 3 Treatment of Wastewater by Heterogeneous Photoelectric Fenton System under Neutral Conditions with / CA Electrocathode

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A three-dimensional ordered macroporous fe <sub>2</sub> o <sub>3</sub> Preparation method and application of carbon airgel electrode
  • A three-dimensional ordered macroporous fe <sub>2</sub> o <sub>3</sub> Preparation method and application of carbon airgel electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 3DOM-Fe 2 o 3 The preparation process of / CA electrode is as follows: figure 2 shown.

[0024] (1) Preparation of bulk CA electrode: Mix resorcinol, formaldehyde, sodium carbonate and water according to the molar ratio of 1:2:100:14.3, pour it into a glass mold, and then put it in a closed container, statically Place the reaction, take out the obtained phenolic resin airgel, and then carry out solvent replacement with an organic reagent with a surface tension less than 30mN / m, the time is 5-7 days, and replace acetone every 1-2 days; the obtained phenolic resin airgel The gel is placed at room temperature for drying. The drying time at room temperature is 5-7 days, and then the temperature is programmed to rise in a tube furnace. The temperature is raised to 800-950°C at a speed of 1.5-3.5°C / min and kept at this temperature for 3- 5h, then cooled to room temperature at the same rate to obtain block carbon aerogel;

[0025](2) Polystyrene hard template self-assembly...

Embodiment 2

[0029] Adopt the 3DOM-Fe that embodiment 1 prepares 2 o 3 / CA Electrode Degradation of Imidacloprid by Electrosorption. The degradation device is based on 3DOM-Fe 2 o 3 The / CA electrode is the cathode, and the BDD electrode is the anode. The voltage provided by the DC stabilized power supply is used to control the constant voltage to 0-0.1V. The process parameters are as follows: the water sample processing volume is 50~150 ml, and the electrode area can be 2~10 cm 2 , the electrode spacing was kept at 1-3 cm, and the working electrode potential was controlled at 0-0.1V. with 0.1M Na 2 SO 4 The 200mg / L imidacloprid of the electrolyte was used as the simulated pesticide wastewater. In the actual application process, the corresponding treatment time is controlled according to the nature of the treated wastewater, the amount of water and the electrode area, so as to meet the final treatment requirements. Utilize the 3DOM-Fe that the inventive method obtains 2 o 3 The / ...

Embodiment 3

[0031] Adopt the 3DOM-Fe that embodiment 1 prepares 2 o 3 / CA Electrode Fenton Degradation of Imidacloprid. The degradation device is based on 3DOM-Fe 2 o 3 The / CA electrode is the cathode, and the BDD electrode is the anode. The voltage provided by the DC stabilized power supply is used to control the constant current density to 5-15mA cm -2 . The process parameters are as follows: the water sample processing volume is 50~150 ml, and the electrode area can be 2~10 cm 2 , the electrode spacing was kept at 1-3 cm, and the working electrode potential was controlled at -10-5 V. with 0.1M Na 2 SO 4 The 200mg / L imidacloprid of the electrolyte was used as the simulated pesticide wastewater. In the actual application process, the corresponding treatment time is controlled according to the nature of the treated wastewater, the amount of water and the electrode area, so as to meet the final treatment requirements. Utilize the 3DOM-Fe that the inventive method obtains 2 o 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and application of a three-dimensional ordered macroporous (3DOM)-Fe2O3 / carbon aerogel (CA) electrode under a neutrality condition. On the surface of a CA electrode, 3DOM-Fe2O3 is deposited on the surface of the CA electrode according to the methods of vertical dipping, solvent evaporation and template calcination, so that the 3DOM-Fe2O3 / CA electrode is obtained. The 3DOM-Fe2O3 / CA electrode can be used for Electro-Fenton cathode rapid degrading of pollutants difficult to biodegrade in wastewater. Compared with the prior art, the preparation method and application of the 3DOM-Fe2O3 / CA electrode have the advantages that CA high in specific area, electrical conductivity and adsorption capacity is selected as a substrate, meanwhile, the CA is loaded with the 3DOM-Fe2O3, solar absorbing photocatalytic performance is achieved, good Electro-Fenton catalytic activity is also achieved, Electro-Fenton and the photocatalysis technology are combined for use, and energy consumption is reduced while Electro-Fenton activity is improved. The method is easy and simple to implement and low in cost, is an efficient and energy-saving new technology, and has high economic and social benefits in the actual application aspect.

Description

technical field [0001] The invention belongs to the technical field of water treatment, in particular to a three-dimensional ordered macroporous Fe 2 o 3 / Carbon airgel electrode (3DOM-Fe 2 o 3 / CA electrode) and its application in photo-assisted electro-Fenton degradation of organic wastewater. Background technique [0002] In recent years, the focus on water pollution and protection has prompted the development of various treatment methods, and electro-Fenton (EF) oxidation technology is one of them. Since this method opens up a green route to electrochemically utilize air as a continuous oxygen supply, it has aroused widespread interest in the industry. Electro-Fenton oxidation is characterized by O 2 H is produced continuously at the cathode through two-electron reduction 2 o 2 , followed by in situ electrochemically generated H 2 o 2 Produce ·OH with Fenton catalyst, which is the main oxidizing species for decomposing pollutants, and it has a high standard elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F1/461C02F1/72C02F1/30C02F101/30
CPCY02W10/37
Inventor 赵红颖彭求胜赵国华
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com