Manufacturing method for five-layer stainless steel-glass fiber reinforced plastic compound heat preservation pipe with pipe joint

A stainless steel pipe, composite thermal insulation technology, applied in the direction of pipes/pipe joints/fittings, pipeline anti-corrosion/rust protection, pipeline protection, etc., can solve the problems of temperature loss, no insulation layer, waste, etc. On-site production, long-life effects

Inactive Publication Date: 2015-03-25
吴汉超
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, due to the simple manufacturing method of the composite pipes produced by existing manufacturers, such as welded steel pipes with seams, the oxygen supply protection and internal and external protection are not achieved during the welding process, and the joints are often opened and welded, and the pipes are broken, which cannot meet the user's requirements, resulting in many Big waste and legal disputes. Secondly, there is no insulation layer, which causes temperature loss during the process of conveying the medium, which is not environmentally friendly and energy-saving.
Thirdly, domestic ordinary stainless steel sheets are used, which have low strength, low hardness, and are not resistant to tensile force. The pipeline will break and crack during use, making it impossible to construct and manufacture on-site

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] The technical solution adopted by the present invention to solve the technical problem is that the production method is as follows: the first step is to prepare the metal pipe body, using a stainless steel thin plate strip with a wall thickness of 0.6-1.0mm, through automatic pipe making equipment, and using an argon arc welding machine Welding, adding argon gas internal protection and molding to make stainless steel pipes, use the edge trimmer to cut the mouths of both ends of the stainless steel pipes and remove the burrs, take the stainless steel pipe joints with the same inner diameter as the stainless steel pipes for use The equipment aligns the stainless steel pipe joint with the mouth of the stainless steel pipe so that the inner diameters of the two are even. The welding joint formed by the stainless steel pipe joint and the mouth of the stainless steel pipe is protected by argon, and then welded together by argon arc welding. , the first layer of the composite p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method for a five-layer stainless steel-glass fiber reinforced plastic compound heat preservation pipe with a pipe joint. The manufacturing method includes the steps that firstly, a stainless steel sheet band with the wall thickness of 0.6-1.0 mm is manufactured into a stainless steel pipe through a full-automatic pipe manufacturing device and welded through an argon welder under protection of injected argon; secondly, the metal pipe obtained in the first step is fixed to rotary shafts of rotary devices, pipe openings in the two ends of the metal pipe are fixed to the rotary shafts of the rotary devices on the two sides respectively when the metal pipe is machined, and the metal pipe can rotate normally by adjusting the rotary shafts; thirdly, alkali-free glass fiber twistless roving is standby on a winding device, the outer wall of the metal pipe to be machined is evenly coated with a layer of unsaturated polyurethane resin, and one end of a piece of alkali-free glass fiber twistless roving is evenly wound around the metal pipe; fourthly, heat preservation foaming is carried out; fifthly, waterproof treatment is carried out. The manufacturing method has the advantages that the process is simple, the service life of the compound pipe is long, internal corrosion prevention and external corrosion prevention are achieved at a time, and the pipe is high in strength and hardness and resistant to abrasion, scaling, high temperature and aging.

Description

technical field [0001] The invention relates to a method for manufacturing a five-layer stainless steel-glass reinforced plastic composite thermal insulation pipe with pipe joints. Background technique [0002] At present, due to the simple manufacturing method of the composite pipes produced by existing manufacturers, such as welded steel pipes with seams, the oxygen supply protection and internal and external protection are not achieved during the welding process, and the joints are often opened and welded, and the pipes are broken, which cannot meet the user's requirements, causing many problems. Big waste and legal disputes. Secondly, there is no insulation layer, which causes temperature loss during the process of conveying the medium, which is not environmentally friendly and energy-saving. Thirdly, domestic ordinary stainless steel sheets are used, which have low strength, low hardness, and are not resistant to tensile force. The pipeline will break and crack during u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F16L9/147F16L58/00
CPCF16L9/147F16L58/00
Inventor 吴汉超
Owner 吴汉超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products