Method for manufacturing tantalum target material

A manufacturing method and technology for tantalum targets, which are applied in the field of tantalum target manufacturing, can solve the problems of serious delamination of tantalum targets and low internal deformation rate of tantalum ingots, so as to reduce process costs, improve internal structure, and avoid cracking. Effect

Active Publication Date: 2015-03-18
KONFOONG MATERIALS INTERNATIONAL CO LTD
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the above problems, the present invention provides a method for manufacturing a tantalum target, so as to overcome the defects of low deformation rate inside the tantalum ingot and serious internal delamination of the obtained tantalum target during the manufacturing process of the existing tantalum target.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing tantalum target material
  • Method for manufacturing tantalum target material
  • Method for manufacturing tantalum target material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] As mentioned in the background technology, based on the metal structure of tantalum metal itself, there will be obvious delamination inside the tantalum target formed by the traditional manufacturing process, which will affect the sputtering rate and stability of the target during the magnetron sputtering process , and thus reduce the film quality of tantalum thin films.

[0047] If the plastic deformation of the tantalum target is realized above the tantalum recrystallization temperature, the internal delamination phenomenon of the tantalum target can be alleviated, but the above-mentioned process requires high processing equipment such as hot rolling equipment, and the process conditions are harsh and difficult to operate. The yield rate of the tantalum target is low, and the above-mentioned process also greatly increases the production cost of the tantalum target.

[0048] For this reason, the present invention provides a method for manufacturing tantalum targets. In...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
recrystallization temperatureaaaaaaaaaa
heightaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for manufacturing a tantalum target material. The method comprises the following steps: firstly, carrying out hot forging on a tantalum ingot and then carrying out first annealing on the hot-forged tantalum ingot to form a first tantalum target material billet; rolling the first tantalum target material billet to form a second tantalum target material billet; and carrying out second annealing on the second tantalum target material billet to obtain the tantalum target material. The tantalum target material formed according to the technical scheme has fine internal grains and uniform internal microstructure and thus the defects such as delamination inside the tantalum target material are effectively avoided, the sputtering rate of the tantalum target material and the quality of the formed tantalum film in the subsequent use process are improved.

Description

technical field [0001] The invention relates to the field of semiconductor sputtering, in particular to a method for manufacturing a tantalum target. Background technique [0002] Tantalum, a metal element, is hard, ductile, and has a small coefficient of thermal expansion, and has extremely high corrosion resistance and toughness. Based on the above advantages, tantalum is widely used in chemical industry, microelectronics, electrical and other industrial fields. [0003] For example, in the field of microelectronics, tantalum is often used to prepare thin-film electrodes and interconnect lines of semiconductor devices. [0004] Specifically, tantalum is applied to the preparation of semiconductor devices by means of magnetron sputtering. The principle is to use physical vapor deposition technology (PVD) to bombard the tantalum target with high-pressure accelerated gaseous ions, so that the tantalum atoms on the tantalum target are sputtered out and deposited on the silic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/34C23C14/14C22F1/18C21D8/00
CPCC22F1/02C22F1/18C23C14/14C23C14/3414
Inventor 姚力军赵凯相原俊夫大岩一彦潘杰王学泽袁海军
Owner KONFOONG MATERIALS INTERNATIONAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com