Modified buckwheat hull foam brick and preparation method thereof

A technology of buckwheat husks and foam bricks, which is applied in the field of building materials, can solve the problems of occupying land resources, inconvenience of production and living, environmental pollution, etc., and achieve the effect of purifying the indoor environment, good thermal insulation, and low cost

Inactive Publication Date: 2015-03-11
HEFEI KANGLING HEALTH TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical properties of waste glass are stable, which not only brings inconvenience to people's production and life, but also pollutes the environment, and the placement of waste glass takes up a lot of land resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Non-limiting examples of the present invention are as follows:

[0022] A modified buckwheat husk foam brick is prepared from the following components by weight (kg):

[0023] Waste glass 55, modified buckwheat husk 25, attapulgite 12, calcium oxide 4, polyethylene glycol 1.5, sodium lauryl sulfate 0.8, potassium fulvic acid 1.5, sodium carboxymethyl cellulose 0.8, linseed oil 7, styrene-acrylic emulsion 1.5, organic silicon quaternary ammonium salt 3, sodium dodecylbenzene sulfonate 0.3, water 55;

[0024] Among them, the modified buckwheat husk is made of the following raw materials in weight (kg):

[0025] Buckwheat husk 35, sorghum husk 8, oxalic acid 4, corn starch 4, calcium chloride 3, calcium sulfate 1.5, triethanolamine 3, water 18;

[0026] The preparation method of modified buckwheat husk:

[0027] Crush buckwheat husks and sorghum husks and mix them evenly with cornstarch, add oxalic acid and water and stir at 80°C for 4 hours, filter and dry, add calcium...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified buckwheat hull foam brick and a preparation method thereof. The foam brick is characterized in that the foam brick is prepared from the raw materials of, by weight, 50-60 parts of waste glass, 20-30 parts of modified buckwheat hull, 10-15 parts of attapulgite, 3-5 parts of calcium oxide, 1-2 parts of polyethylene glycol, 0.5-1 parts of sodium lauryl sulfate, 1-2 parts of potassium fulvate, 0.5-1 parts of sodium carboxymethyl cellulose, 6-8 parts of linseed oil, 1-2 parts of styrene-acrylic emulsion, 2-4 parts of organosilicon quaternary ammonium salt, 0.2-0.4 parts of sodium dodecylbenzene sulfonate, and 50-60 parts of water. According to the foam brick provided by the invention, through improvements in formula and process, the product has the characteristics of good thermal insulation, light weight, high strength, antibacterial property, and mildew resistance. With the method, energy is saved, waste is utilized, and cost is low.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a modified buckwheat hull foam brick and a preparation method thereof. Background technique [0002] Foam brick is a kind of aerated concrete block. After using a foaming agent to physically foam through a foaming machine, the air bubbles are added to the slurry for mixing, pouring, and finally a foam brick with internal pores is obtained. Foam bricks are mainly used for non-load-bearing walls. They have the characteristics of low cost, light weight, and good thermal insulation effects. They have been widely used in industrial and civil buildings and are a wall material with good performance. [0003] Glass materials are indispensable and indispensable materials for people's daily life. The extensive use of glass also leads to the inevitable generation of a large amount of waste glass waste in daily production and life. The chemical properties of waste glass are stable, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/10C04B41/49
Inventor 张百庆韩立平
Owner HEFEI KANGLING HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com