A kind of preparation method of carbon dots/chitosan in situ composite material

An in-situ composite material and chitosan technology, applied in the direction of luminescent materials, chemical instruments and methods, electrolytic organic material coating, etc., can solve the problems of prolonging the production cycle, increasing equipment and operation steps, increasing production costs, etc., to achieve Simplified post-processing, a wide range of subsequent applications, and short reaction times

Inactive Publication Date: 2016-06-01
WUHAN UNIV OF TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the blending method is used to prepare carbon dots / chitosan composites, because the blending process requires additional equipment and operating steps, thereby prolonging the production cycle and increasing production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of carbon dots/chitosan in situ composite material
  • A kind of preparation method of carbon dots/chitosan in situ composite material
  • A kind of preparation method of carbon dots/chitosan in situ composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of preparation method of carbon dot / chitosan in situ composite material, it comprises following specific steps:

[0037] 1) Preparation of chitosan solution: Add chitosan to distilled water to obtain a chitosan dispersion with a mass concentration of 2.5g / 100mL, then adjust its pH to 4.86 with 0.8M hydrochloric acid solution, 25 o Under magnetic stirring for 9 hours at C, the chitosan is fully dissolved, and its pH is adjusted to 5.60 with 0.8M sodium hydroxide solution to obtain a chitosan solution;

[0038] 2) Preparation of carbon dots / chitosan in situ composite: Take 12 mL of the chitosan solution obtained in step 1), add it to a beaker, and then put it into a household microwave oven with a power of 700W for microwave reaction; the microwave reaction time is 5 minutes , after the reaction is finished, take out the microwave reaction product after natural cooling, then add 24mL distilled water to the microwave reaction product, 25 o After 10 hours of magneti...

Embodiment 2

[0047] A kind of preparation method of carbon dot / chitosan in situ composite material, it comprises following specific steps:

[0048] 1) Preparation of chitosan solution: Add chitosan to distilled water to obtain a chitosan dispersion with a mass concentration of 3.0g / 100mL, then adjust its pH to 5.00 with 1.0M hydrochloric acid solution, 30 o Under magnetic stirring for 10 hours at C, the chitosan was fully dissolved, and its pH was adjusted to 6.00 with 1.0M sodium hydroxide solution to obtain a chitosan solution;

[0049] 2) Preparation of carbon dots / chitosan in situ composite: Take 15 mL of the chitosan solution obtained in step 1), add it to a beaker, and then put it into a household microwave oven with a power of 700W for microwave reaction; the microwave reaction time is 6 minutes , after the reaction is finished, take out the microwave reaction product after natural cooling, then add 30mL distilled water to the microwave reaction product, 30 o After 12 hours of magn...

Embodiment 3

[0058] A kind of preparation method of carbon dot / chitosan in situ composite material, it comprises following specific steps:

[0059] 1) Preparation of chitosan solution: Add chitosan to distilled water to obtain a chitosan dispersion with a mass concentration of 2.0g / 100mL, then adjust its pH to 4.50 with 0.5M hydrochloric acid solution, 20 o Under magnetic stirring for 8 hours at C, the chitosan was fully dissolved, and its pH was adjusted to 5.50 with 0.5M sodium hydroxide solution to obtain a chitosan solution;

[0060] 2) Preparation of carbon dots / chitosan in situ composite: Take 10 mL of the chitosan solution obtained in step 1), add it to a beaker, and then put it into a household microwave oven with a power of 700W for microwave reaction; the microwave reaction time is 4 minutes , after the reaction is finished, take out the microwave reaction product after natural cooling, then add 20mL distilled water to the microwave reaction product, 20 o After 8 hours of magnet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a carbon dot / chitosan in-situ composite material. The carbon dot / chitosan in-situ composite material is prepared by an in-situ method. The method comprises the following steps: carrying out microwave treatment on a chitosan solution to obtain a carbon dot / chitosan in-situ complex, and preparing the carbon dot / chitosan in-situ complex into the carbon dot / chitosan in-situ composite material. According to the method, a carbon dot / chitosan in-situ composite film material is prepared by a casting and film-forming method, and a carbon dot / chitosan composite coating material is prepared by a controllable electro-deposition method. The preparation method of the carbon dot / chitosan in-situ composite material has the advantages of being simple, convenient to operate, mild in preparation conditions and easy to control; equipment used by the method is simple and convenient, has energy conservation and environment protection effects, and is low in cost; the carbon dot / chitosan composite film material has good application prospects in the fields of fluorescent biological film materials, optical film materials, biological detectors and fluorescent light-emitting materials. The carbon dot / chitosan composite coating material has good application prospects in the fields of surface decoration and surface patterning of metal biological materials, biological electrodes, biological chips and biological devices.

Description

technical field [0001] The invention belongs to the fields of biomedical materials, nanometer materials, polymer materials and electrochemistry, and in particular relates to a preparation method of carbon dot / chitosan in-situ composite material. Background technique [0002] Carbon dots are a new type of quantum dots, and their particle size is generally below 10nm. Compared with traditional quantum dots (such as cadmium sulfide quantum dots), its basic skeleton is carbon, which has the advantages of non-toxicity, high fluorescence stability and photobleaching resistance, adjustable fluorescence wavelength, good water dispersibility, easy functionalization, biophase Excellent properties such as good capacitance [Journal of Materials Chemistry, 2012, 22(46): 24230-24253]. Therefore, since their discovery in 2004, carbon dots have been widely used in many fields such as biomarkers, bioimaging, drug carriers, biosensors, luminescent materials, and photocatalysis. Chitosan is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/08C08K3/04C09K11/65C08J5/18C01B31/02C25D9/02C25D9/08
Inventor 王艺峰王霞耿增华郭雪成郭萌萌熊燕飞
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com