Modified PP automobile wheel casing and preparation method thereof
A modified technology for automobiles, applied in the field of modified PP automobile wheel covers and its preparation, which can solve the problems of low impact strength, tensile strength, elongation at break and Shore hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] 100 parts of PP; 10 parts of SBS; 10 parts of EPDM; 25 parts of LLDPE; 5 parts of LDPE; 20 parts of PET; 0.5 parts of chlorinated polyethylene; 0.2 parts of sodium benzoate; 10 parts of PA6; 1 part of DBP; 1 part of SEP; 15 parts of diatomaceous earth; 25 parts of EPP; 30 parts of calcium carbonate.
[0026] Put PA6, PET, SBS, SEP and sodium benzoate into the reaction kettle and heat to 60°C, dry for 10 hours, then add EPDM, LLDPE, LDPE and EPP, raise the temperature to 80°C, stir for 10 minutes, and the stirring speed is 200 rpm.
[0027] Put the stirred material into a single-screw extruder to extrude and granulate, the barrel temperature is 210°C, 225°C and 240°C, the screw speed is 11r / min, add the remaining raw materials, and plasticize on a double-roller plastic mixer. The temperature is 170°C.
[0028] The tensile strength of the product is 35MPa, the Shore hardness is 94; the elongation at break is 600%, the notched impact strength is 600kJ / m; the heat distorti...
Embodiment 2
[0030] 100 parts of PP; 30 parts of SBS; 30 parts of EPDM; 45 parts of LLDPE; 25 parts of LDPE; 40 parts of PET; 2.5 parts of chlorinated polyethylene; 0.8 parts of sodium benzoate; 20 parts of PA6; 20 parts of DBP; 25 parts of SEP; 35 parts of diatomaceous earth; 45 parts of EPP; 50 parts of calcium carbonate.
[0031] Put PA6, PET, SBS, SEP and sodium benzoate into the reactor and heat to 70°C, dry for 12 hours, then add EPDM, LLDPE, LDPE and EPP, raise the temperature to 90°C, stir for 30min, and the stirring speed is 400 rpm.
[0032] Put the stirred material into a single-screw extruder to extrude and granulate, the barrel temperature is 210°C, 225°C and 240°C, the screw speed is 15r / min, add the remaining raw materials, and plasticize on a twin-roller plastic mixer. The temperature is 190°C.
[0033] The tensile strength of the product is 40MPa, the Shore hardness is 95; the elongation at break is 650%, the notched impact strength is 650kJ / m; the heat distortion tempera...
Embodiment 3
[0035] Weigh 100 parts of PP; 15 parts of SBS; 15 parts of EPDM; 30 parts of LLDPE; 10 parts of LDPE; 25 parts of PET; 1 part of DCP; 0.4 parts of sodium benzoate; ; 5 parts of DBP; 10 parts of SEP; 20 parts of diatomaceous earth; 30 parts of EPP; 35 parts of calcium carbonate.
[0036] Put PA6, PET, SBS, SEP and sodium benzoate into the reactor and heat to 60°C, dry for 10 hours, then add EPDM, LLDPE, LDPE and EPP, raise the temperature to 80°C, stir for 15 minutes, and the stirring speed is 250 rpm.
[0037] Put the stirred material into a single-screw extruder to extrude and granulate, the barrel temperature is 210°C, 225°C and 240°C, the screw speed is 12r / min, add the remaining raw materials, and plasticize on a twin-roller plastic mixer. The temperature is 175°C.
[0038] The tensile strength of the product is 45MPa, the Shore hardness is 96; the elongation at break is 700%, the notched impact strength is 700kJ / m; the heat distortion temperature is 145°C, the elastic mo...
PUM
Property | Measurement | Unit |
---|---|---|
Vicat softening point | aaaaa | aaaaa |
Vicat softening point | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com