A kind of polymer structure composite material and preparation method thereof

A composite material and polymer technology, which is applied in the field of polymer structure composite materials and its preparation, can solve the problems of filler agglomeration and waste, and achieve the effects of improved mechanical properties, simple and easy operation, and good monodispersity

Active Publication Date: 2017-08-22
厦门祥福兴科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are many research results at present, the use of fillers is mainly at a relatively high content, which is not only wasteful, but also easily causes the problem of filler agglomeration in composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer structure composite material and preparation method thereof
  • A kind of polymer structure composite material and preparation method thereof
  • A kind of polymer structure composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A method for preparing a polymer structure composite material, realized by the following scheme: Accurately weigh 0.004g of graphene, add acetone and ultrasonically disperse it in 39.996g of epoxy resin, and obtain epoxy resin-graphene by ultrasonic for 2 hours Masterbatch. Weigh 0.1g-7g of the masterbatch, ultrasonically disperse it in 39.9g-30g of epoxy resin to obtain a mixed solution, put the mixed solution together with zirconia balls into a PTFE ball mill tank with a volume of 100ml, each Among them, the mass ratio of zirconia grinding balls to the mixed liquid is 6.25:1, and the diameter of the balls is 1 mm to 4 mm. Put the polytetrafluoroethylene ball mill tank filled with the mixed liquid symmetrically into the planetary ball mill for ball milling at a speed of 300 rpm After 24 hours, a graphene-epoxy resin structure composite material (the obtained filler content is: 0.25-17.5ppm) was obtained.

Embodiment 2

[0044]A method for preparing a polymer structure composite material, realized through the following scheme: Accurately weigh 0.004g of graphene, add acetone and ultrasonically disperse it in 39.996g of epoxy resin, and mix the mixture with zirconia balls after ultrasonication for 30min Put it into a polytetrafluoroethylene ball mill jar with a volume of 100ml. In each portion, the mass ratio of zirconia grinding balls to the mixed solution is 6.25:1, and the diameter of the ball is 1 mm to 4 mm. Put the mixed solution in the polytetrafluoroethylene The ball mill jars were symmetrically placed in a planetary ball mill and ball milled at a speed of 300 rpm for 24 hours to obtain an epoxy resin-graphene masterbatch. Weigh 0.1g-7g of the masterbatch, ultrasonically disperse it in 39.9g-30g of epoxy resin to obtain a mixed solution, put the mixed solution together with zirconia balls into a PTFE ball mill tank with a volume of 100ml, each Among them, the mass ratio of zirconia grin...

Embodiment 3

[0048] A method for preparing a polymer structure composite material is realized through the following scheme: accurately weigh 0.004g of graphene, disperse it in 39.06g of unsaturated resin, and obtain an unsaturated resin-graphene masterbatch by ultrasonication for 2 hours. Weigh 0.1g-7g of masterbatch, ultrasonically disperse in 39.9g-30g of unsaturated resin to obtain a mixed solution, put the mixed solution together with zirconia balls into a PTFE ball mill tank with a volume of 100ml, each Among them, the mass ratio of zirconia grinding balls to the mixed liquid is 6.25:1, and the diameter of the balls is 1 mm to 4 mm. Put the polytetrafluoroethylene ball mill tank filled with the mixed liquid symmetrically into the planetary ball mill for ball milling at a speed of 300 rpm After 24 hours, a graphene-unsaturated resin structure composite material was obtained. (The obtained filler content is: 0.25~17.5ppm).

[0049] The following table 1 is the elastic modulus and tensi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
breaking strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention provides a polymer structure composite material and a preparation method thereof: the mass concentration of the filler in the polymer structure composite material in the polymer matrix is ​​0.1-20 ppm; the filler is graphene, silicon dioxide, carbon nanometer At least one of tubes, carbon black, aluminum oxide, zinc oxide, calcium carbonate, titanium dioxide, talc, and montmorillonite, and the polymer matrix is ​​at least one of epoxy resins and unsaturated resins; the preparation method is as follows : First mix the filler with an appropriate amount of polymer matrix to form a master batch. When there is epoxy resin in the polymer matrix, a polymer medium needs to be added to reduce the viscosity of the polymer matrix; take an appropriate amount of masterbatch, press The mass concentration ratio of the filler in the polymer matrix The masterbatch is diluted into the polymer matrix and mixed evenly to obtain the polymer structure composite material. The polymer structure composite material of the invention has good monodispersity and high mechanical properties; the preparation method is simple and easy to operate, and is easy to be used for industrialized mass production.

Description

[0001] 【Technical field】 [0002] The invention relates to a polymer structure composite material and a preparation method thereof. [0003] 【Background technique】 [0004] Thermosetting resins are a class of polymers with a three-dimensional network structure, usually formed from oligomers or low-molecular compounds containing two or more active functional groups in their molecules through curing and cross-linking reactions in the presence of cross-linking agents or catalysts. Thermosetting resin monomers or prepolymers have excellent flow processing properties, and the cured network structure makes them have excellent physical and mechanical properties, electrical insulation properties, chemical resistance, bonding properties and thermal stability. , Thermosetting resins are widely used in the technical fields of machinery, electronics, aerospace and other fields in the form of adhesives, coatings, potting materials and composite materials. However, due to the high crosslink...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08L101/00C08K3/04C08K3/36C08K3/26C08K7/00C08K3/34C08K3/22
Inventor 陈国华刘莹
Owner 厦门祥福兴科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com