Chilli sauce packaging composite film and preparation method thereof

A composite film and chili sauce technology, applied in packaging, wrapping paper, household packaging, etc., can solve the problems of packaging contents eroding the glue layer, delamination of the glue layer, affecting the packaging and shelf life of the contents, and achieving good resistance to media. Effect, low cost, make up for the effect of poor processing performance

Active Publication Date: 2015-01-07
HUANGSHAN NOVEL
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chili sauce has the characteristics of sour, spicy and salty. In the traditional process of packaging acid and alkaline products, PET / dry compound / PE structure is usually used, that is, the PET film and PE film are glued together through the glue layer. This structure is easy to appear. The contents of the packaging erode the glue layer, resulting in stratification of the glue layer, which affects the packaging and shelf life of the contents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chilli sauce packaging composite film and preparation method thereof
  • Chilli sauce packaging composite film and preparation method thereof
  • Chilli sauce packaging composite film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] See figure 1 , the small package roll film in the present invention is the composite structure of PET / extruded PE / PE, wherein PET is the thickness of PET film layer 10 is 12 μm, extruded PE is the thickness of functional polyethylene film layer 20 is 15 μm, and PE is PE film Layer 30 has a thickness of 60 μm.

[0049] The formula of PE film layer 30 is as follows:

[0050] Corona layer: 50Kg Yangtze 7042+50Kg2420-H;

[0051] Middle layer: 25Kg1820+25Kg100AC+25kgHTA108;

[0052] Heat seal layer: 50Kg100AC+25KgPL1881G+1.5Kg10090-K+1.0KgAB-20LD+0.2Kg10091-K.

[0053] The thicknesses of the three layers of the corona layer, the intermediate layer and the heat-sealing layer are 20 μm, 20 μm and 20 μm, respectively.

[0054] See figure 2 , the preparation method of the small package roll film in the present invention specifically comprises the following steps:

[0055] 1) Printing process: the PET film is printed by color and multi-color gravure printing through the grav...

Embodiment 2

[0064] See figure 1 , the small packaging film in the present invention is a composite structure of PET / extruded PE / PE, wherein PET is the thickness of the PET film layer 10 is 12 μm, extruded PE is the thickness of the functional polyethylene film layer 20 is 20 μm, and PE is the PE film Layer 30 has a thickness of 80 μm.

[0065] The formula of PE film layer 30 is as follows:

[0066] Corona layer: 50Kg Yangtze 7042+50Kg2420-H;

[0067] Middle layer: 25Kg1820+25Kg100AC+50kgHTA108;

[0068] Heat seal layer: 50Kg100AC+25KgPL1881G+1.5Kg10090-K+1.0KgAB-20LD+0.2Kg10091-K.

[0069] The thicknesses of the three layers of the corona layer, the intermediate layer and the heat-sealing layer are 20 μm, 40 μm and 20 μm, respectively.

[0070] See figure 2 , the preparation method of the small package roll film in the present invention specifically comprises the following steps:

[0071] 1) Printing process: the PET film is printed by color and multi-color gravure printing through...

Embodiment 3

[0080] See figure 1 , the small package roll film in the present invention is the composite structure of PET / extruded PE / PE, and wherein PET is the thickness of PET film layer 10 is 12 μ m, extruded PE is the thickness of functional polyethylene film layer 20 is 18 μ m, and PE is PE film Layer 30 has a thickness of 70 μm.

[0081] The formula of PE film layer 30 is as follows:

[0082] Corona layer: 50Kg Yangtze 7042+50Kg2420-H;

[0083] Middle layer: 25Kg1820+25Kg100AC+75kgHTA108;

[0084] Heat seal layer: 50Kg100AC+25KgPL1881G+1.5Kg10090-K+1.0KgAB-20LD+0.2Kg10091-K.

[0085] The thicknesses of the three layers of the corona layer, the intermediate layer and the heat-sealing layer are 20 μm, 30 μm, and 40 μm, respectively.

[0086] See figure 2 , the preparation method of the small package roll film in the present invention specifically comprises the following steps:

[0087] 1) Printing process: the PET film is printed by color and multi-color gravure printing through...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention specifically relates to a chilli sauce packaging composite film and a preparation method thereof. The packaging composite film is formed by tightly attaching a PET printing thin film layer which is 12 microns thick, a functional polyethylene thin film layer which is 15-20 microns thick and a PE thin film layer which is 60-80 microns thick, wherein the PET printing thin film layer, the functional polyethylene thin film layer and the PE thin film layer are connected in sequence; the functional polyethylene thin film layer is of a double-layer co-extrusion composite structure, and one side, which is adhered to the PET printing thin film layer, of the functional polyethylene thin film layer is provided with an ethylene acrylic acid copolymer layer; one side, which is adhered to the PE thin film layer, of the functional polyethylene thin film layer is provided with a low-density polyethylene and white master batch blending layer; the weight ratio of low-density polyethylene to white master batches is 20 to 3; the thickness ratio of the ethylene acrylic acid copolymer layer to the low-density polyethylene and white master batch blending layer is 2 to 3. The composite film has high performance such as high sealing intensity, low cost, good sealing effect, high sealing flatness and high pollution resistance and also has the advantages of good anti-medium effect, low cost, difficulty in layering and the like.

Description

Technical field [0001] The invention belongs to the technical field of packaging materials, and specifically relates to a chili sauce packaging composite film and a preparation method thereof. Background technique [0002] With the acceleration of the pace of life, the composite film small packaging of chili sauce has been favored by people for its many advantages such as easy portability, beautiful appearance and quick use. Chili sauce has the characteristics of sour, spicy and salty. In the traditional process, when packaging acid-alkaline products, the PET / dry compound / PE structure is usually used, that is, the PET film and the PE film are glued together through a glue layer. This structure is easy to occur. The packaging contents erode the glue layer, causing the glue layer to stratify, thus affecting the packaging and shelf life of the contents. Contents of the invention [0003] One of the objects of the present invention is to provide a packaging composite film for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/08B32B37/00B65D65/40B32B27/32
CPCB32B27/08B32B2250/03B32B2250/24B32B2439/70B65D65/40
Inventor 江继忠鲍祖本潘健汪学文胡继超
Owner HUANGSHAN NOVEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap