High-strength tear-resistant modified butadiene styrene rubber material

A styrene-butadiene rubber and tear-resistant technology, which is applied in the field of high-strength tear-resistant modified styrene-butadiene rubber materials, can solve the problems of poor tear resistance, fast crack propagation speed, and poor strength of styrene-butadiene rubber materials, and achieves Fast vulcanization speed, low compression set rate, improved aging resistance and anti-oxidation performance

Inactive Publication Date: 2014-12-10
ANHUI ELECTRIC GRP SHARES
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Styrene-butadiene rubber material is currently the largest general-purpose synthetic rubber material. Because of its good wear resistance, aging resistance, and water resistance, it can replace natural rubber materials in most occasions. It is mainly used in the tire industry, auto parts, rubber hoses, In the fields of rubber shoes, wire and cable, etc.; the flex cracking resistance of styrene-butadiene rubber material is better, but the crack growth speed is fast, the tear resistance is poor, and at the same time, the strength of styrene-butadiene rubber material is also poor; therefore, a Styrene-butadiene rubber materials with high strength and strong tear resistance are necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A high-strength, tear-resistant modified styrene-butadiene rubber material, whose raw materials by weight include: 72 parts of styrene-butadiene rubber, 33 parts of natural rubber, 29 parts of neoprene, 35 parts of modified graphene, and 25 parts of white carbon black. , 12 parts carbon black, 20 parts barite powder, silane coupling agent A-1513 parts, sulfur 6.5 parts, accelerator TMTM 2.2 parts, accelerator DM 2 parts, octylated diphenylamine 3 parts, antioxidant BLE 3.3 parts , Antioxidant OD 4.3 parts, coconut oil 3.2 parts, dioctyl phthalate 2.5 parts, naphthenic oil 6 parts, petroleum phenyl sulfonate 1.2 parts, epoxy resin 2.6 parts; styrene butadiene rubber consists of 1 ,3-butadiene and styrene were obtained by copolymerization at a weight ratio of 70:30.

[0017] The preparation method of modified graphene includes: placing 1.9 parts of graphene oxide in 1000 parts of water by weight, performing ultrasonic treatment to obtain a graphene oxide solution with a conc...

Embodiment 2

[0020] A high-strength, tear-resistant modified styrene-butadiene rubber material, whose raw materials by weight include: 65 parts of styrene-butadiene rubber, 45 parts of natural rubber, 26 parts of neoprene, 42 parts of modified graphene, and 20 parts of white carbon black. , Carbon black 16 parts, barite powder 15 parts, silane coupling agent A-1515 parts, sulfur 4.3 parts, accelerator TMTM 2.4 parts, accelerator DM 1.5 parts, octylated diphenylamine 7 parts, antioxidant BLE 2.8 parts , Antioxidant OD 4.6 parts, coconut oil 2.6 parts, dioctyl phthalate 4 parts, naphthenic oil 3 parts, petroleum phenyl sulfonate 1.5 parts, epoxy resin 2.3 parts; styrene butadiene rubber consists of 1 ,3-Butadiene and styrene were obtained by copolymerization at a weight ratio of 74:26.

[0021] The preparation method of modified graphene includes: placing 1.6 parts of graphene oxide in 1200 parts of water by weight, performing ultrasonic treatment to obtain a graphene oxide solution with a conc...

Embodiment 3

[0024] A high-strength, tear-resistant modified styrene-butadiene rubber material, whose raw materials by weight include: 70 parts of styrene-butadiene rubber, 35 parts of natural rubber, 28 parts of neoprene, 36 parts of modified graphene, and 23 parts of white carbon black. , Carbon black 14 parts, barite powder 18 parts, silane coupling agent A-1513 parts, sulfur 6.5 parts, accelerator TMTM 2.2 parts, accelerator DM 2 parts, octylated diphenylamine 3 parts, antioxidant BLE 3.3 parts , Antioxidant OD 4.3 parts, coconut oil 3.2 parts, dioctyl phthalate 2.5 parts, naphthenic oil 6 parts, petroleum phenyl sulfonate 1.2 parts, epoxy resin 2.6 parts; styrene butadiene rubber consists of 1 ,3-butadiene and styrene were obtained by copolymerization at a weight ratio of 72:28.

[0025] The preparation method of modified graphene includes: placing 1.8 parts of graphene oxide in 1100 parts of water by weight, performing ultrasonic treatment to obtain a graphene oxide solution with a conc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength tear-resistant modified butadiene styrene rubber material which comprises the following materials in parts by weight: 65-72 parts of butadiene styrene rubber, 33-45 parts of natural rubber, 26-29 parts of neoprene, 35-42 parts of modified graphene, 20-25 parts of white carbon black, 12-16 parts of carbon black, 15-20 parts of blanc fixe, 3-5 parts of silane coupling agent A-151, 4.3-6.5 parts of sulfur, 2.2-2.4 parts of accelerant TMTM, 1.5-2.0 parts of accelerant DM, 3-7 parts of octylated diphenylamine, 2.8-3.3 parts of antiager BLE, 4.3-4.6 parts of antiager OD, 2.6-3.2 parts of coconut oil, 2.5-4 parts of dioctyl phthalate, 3-6 parts of naphthenic oil, 1.2-1.5 parts of phenyl petroleum sulfonate, and 2.3-2.6 parts of epoxy resin. The high-strength tear-resistant modified butadiene styrene rubber material is high in strength and strong in tear resistance.

Description

Technical field [0001] The invention relates to the technical field of styrene butadiene rubber materials, in particular to a high-strength, tear-resistant modified styrene butadiene rubber material. Background technique [0002] Styrene-butadiene rubber material is currently the largest production of general-purpose synthetic rubber materials. Because of its good wear resistance, aging resistance, water resistance, etc., it can replace natural rubber materials in most occasions. It is mainly used in the tire industry, automotive parts, hoses, Rubber shoes, wires and cables, etc.; styrene butadiene rubber materials have better flexural crack resistance, but they have fast crack propagation speed and poor tear resistance. At the same time, the strength of styrene butadiene rubber materials is also poor; therefore, a Styrene butadiene rubber materials with high strength and strong tear resistance are necessary. Summary of the invention [0003] The technical problems existing in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L7/00C08L11/00C08L63/00C08K13/06C08K9/06C08K9/04C08K3/04C08K3/36C08K3/30C08K3/06C08K5/18C08K5/103C08K5/12C08K5/42
Inventor 吴建杰黄海琴郑有松朱家俊吴松如
Owner ANHUI ELECTRIC GRP SHARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com