Ultraviolet curing acrylic ester composition paint used for ceramic

A technology of acrylate and ultraviolet light, applied in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of low hardness, poor wear resistance and solvent resistance, and achieve good wear resistance

Active Publication Date: 2014-11-19
王帅
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above technical problems, the present application provides a UV-curable acrylate composition coating for ceramics, which solves the technical problems of existing ceramic UV-curable acrylate composition coatings such as glossiness, low hardness, poor wear resistance and solvent resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An ultraviolet curing acrylate composition coating for ceramics, the proportion of raw materials is as follows in parts by weight: 100 parts of polyurethane acrylate; 5 parts of magnesium oxide; 30 parts of polyester acrylate; 1 part of zinc oxide; 80 parts of water; 20 parts of light calcium carbonate; 5 parts of hexamethoxymethylmelamine; 20 parts of quartz powder; 5 parts of dibutyltin dilaurate; 10 parts of sodium hydroxide; 1 part of silane; 1 part of benzoin ether; 25 parts of epoxy acrylate; 3 parts of benzophenone; 50 parts of trimethylolpropane triacrylate.

[0016] After the above raw materials are mixed evenly in a reaction kettle, they are coated on ceramics and irradiated with ultraviolet rays.

[0017] The gloss of the product is 110%-130%, and the hardness is 5-8H; the surface dry time is 25-35s, and the dry time is 20-30min. After soaking in water for 30-50d, there is no foaming or falling off; soaking in saturated calcium hydroxide for 5-15d does not B...

Embodiment 2

[0019] An ultraviolet curing acrylate composition coating for ceramics, the proportion of raw materials is as follows in parts by weight: 100 parts of polyurethane acrylate; 15 parts of magnesium oxide; 40 parts of polyester acrylate; 10 parts of zinc oxide; 100 parts of water; 30 parts of light calcium carbonate; 15 parts of styrene; 40 parts of quartz powder; 15 parts of dibutyltin dilaurate; 20 parts of sodium hydroxide; 5 parts of silane; 10 parts of benzoin ether; 35 parts of epoxy acrylate; 7 parts of ketone; 70 parts of trimethylolpropane triacrylate.

[0020] After the above raw materials are mixed evenly in a reaction kettle, they are coated on ceramics and irradiated with ultraviolet rays.

[0021] The gloss of the product is 120%, and the hardness is 6H; the surface drying time is 30s, and the hard drying time is 25 minutes. After soaking in water for 40 days, there is no foaming and shedding phenomenon; after soaking in saturated calcium hydroxide for 10 days, ther...

Embodiment 3

[0023] An ultraviolet-curable acrylate composition coating for ceramics, the proportion of raw materials is as follows in parts by weight: 100 parts of polyurethane acrylate; 10 parts of magnesium oxide; 35 parts of polyester acrylate; 5 parts of zinc oxide; 90 parts of water; 25 parts of light calcium carbonate; 10 parts of styrene; 30 parts of quartz powder; 10 parts of dibutyltin dilaurate; 15 parts of sodium hydroxide; 3 parts of silane; 5 parts of benzoin ether; 30 parts of epoxy acrylate; 5 parts of ketone; 60 parts of trimethylolpropane triacrylate.

[0024] After the above raw materials are mixed evenly in a reaction kettle, they are coated on ceramics and irradiated with ultraviolet rays.

[0025] The gloss of the product is 130%, and the hardness is 8H; the surface drying time is 25s, and the hard drying time is 20 minutes. After soaking in water for 50 days, there is no foaming or shedding phenomenon; after soaking in saturated calcium hydroxide for 15 days, there i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet curing acrylic ester composition paint used for ceramic. The ultraviolet curing acrylic ester composition paint includes following raw materials: urethane acrylate, magnesium oxide, polyester acrylate, zinc oxide, water, light calcium carbonate, a crosslinking agent, quartz powder, dibutyltin dilaurate, sodium hydroxide, a coupling agent, benzoin ethyl ether, epoxy acrylate, diphenyl ketone and trimethylolpropane triacrylate. The paint is 110%-130% in glossiness, is 5-8 H in hardness, is 25-35 s in a surface drying time and 20-30 min in actual drying time, is free of a blistering and dropping phenomenon after being soaked in water for 30-50 days, is free from blistering and wrinkling after being soaked in a saturated calcium hydroxide solution for 5-15 days, is good in anti-wear performance and can be widely produced and replace conventional materials.

Description

technical field [0001] The application belongs to the field of coatings, and in particular relates to an ultraviolet-curable acrylate composition coating for ceramics. Background technique [0002] Ceramics are various products made of natural clay and various natural minerals as the main raw materials through crushing, kneading, molding and calcination. In the past, people called ceramics made of clay and fired at high temperature in special kilns. Ceramics is the general term for pottery and porcelain. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. It includes various products made of clay or a mixture containing clay through kneading, shaping, and calcination. It ranges from the roughest earthenware to the finest fine pottery and porcelain. Its main raw material is silicate minerals (such as clay, quartz, etc.) taken from nature, so it belongs to the category of "s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D167/06
Inventor 马志明
Owner 王帅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com