Environment-friendly plastic material

A technology of environmentally friendly plastics and raw materials, applied in the field of plastic materials, can solve problems such as fast decomposition rate, oxidation resistance, weak impact resistance, strong water absorption, etc., to improve tensile strength and elongation at break, and improve wear resistance Effect of improving tear performance and impact resistance

Active Publication Date: 2014-10-08
汕头市纳川塑胶制品有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The accumulation of waste plastic products mixed in the soil will affect the absorption of nutrients and water by crops, resulting in reduced crop production and affecting agricultural development
Due to its extremely difficult to decompose, landfill treatment will not only occupy a large amount of land, but the occupied land will not be restored for a long time, which will affect the sust...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly plastic material
  • Environment-friendly plastic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of environment-friendly plastic material that the present invention proposes, its raw material comprises by weight: 20 parts of polycaprolactone PCL, 70 parts of modified poly-beta-hydroxybutyric acid PHB, 13 parts of peanut protein powder, 1.8 parts of jute fiber, wood 3 parts of fiber, 1.3 parts of silane coupling agent KH580, 2 parts of sodium lactate, 1.6 parts of sodium diacetate, 2 parts of diisononyl phthalate DINP, 7 parts of epoxy tall oleate, 2 parts of oxidized starch , 23 parts of nano-silica, 6 parts of light calcium carbonate, 5 parts of sepiolite powder, 10101 parts of antioxidants, wherein the modified poly-β-hydroxybutyrate PHB is poly-β-hydroxybutyrate PHB and high cis It is obtained by blending and modifying butadiene rubber;

[0015] During the preparation process, the silane coupling agent KH580 was added to jute fiber and wood fiber and stirred at a stirring speed of 30rpm for 6min, then peanut protein powder was added and stirred at a stirr...

Embodiment 2

[0017] A kind of environment-friendly plastic material proposed by the present invention, its raw material comprises by weight: 24 parts of polycaprolactone PCL, 66 parts of modified poly-beta-hydroxybutyric acid PHB, 16 parts of peanut protein powder, 1.6 parts of jute fiber, wood 3.4 parts of fiber, 1.15 parts of silane coupling agent KH580, 2.7 parts of sodium lactate, 1.3 parts of sodium diacetate, 2.16 parts of diisononyl phthalate DINP, 5.4 parts of butyl epoxy tallate, 3.6 parts of oxidized starch , 21 parts of nano-silica, 7.3 parts of light calcium carbonate, 3.1 parts of sepiolite powder, 10101.3 parts of antioxidants, of which the modified poly-β-hydroxybutyrate PHB is poly-β-hydroxybutyrate PHB and high cis Butadiene rubber is obtained by blending and modifying at a weight ratio of 1:1.5;

[0018] During the preparation process, the silane coupling agent KH580 was added to jute fiber and wood fiber and stirred at a stirring speed of 34rpm for 4.5min, then peanut pr...

Embodiment 3

[0020] A kind of environment-friendly plastic material that the present invention proposes, its raw material comprises by weight: 25 parts of polycaprolactone PCL, 65 parts of modified poly-beta-hydroxybutyric acid PHB, 18 parts of peanut protein powder, 1.5 parts of jute fiber, wood 4 parts of fiber, 1.1 parts of silane coupling agent KH580, 3 parts of sodium lactate, 1.1 parts of sodium diacetate, 2.2 parts of diisononyl phthalate DINP, 5 parts of epoxy tall oleate, 4 parts of oxidized starch , 20 parts of nano-silica, 8 parts of light calcium carbonate, 3 parts of sepiolite powder, 10101.4 parts of antioxidants, of which the modified poly-β-hydroxybutyrate PHB is poly-β-hydroxybutyrate PHB and high cis Butadiene rubber is obtained by blending and modifying at a weight ratio of 2:1;

[0021]During the preparation process, the silane coupling agent KH580 was added to jute fiber and wood fiber and stirred at a stirring speed of 33rpm for 5.6min, then peanut protein powder was ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly plastic material which comprises the following raw materials in parts by weight: 20-25 parts of polycaprolactone PCL, 65-70 parts of modified poly-beta-hydroxybutyric acid PHB, 13-18 parts of peanut protein flour, 1.5-1.8 parts of jute fiber, 3-4 parts of wood fiber, 1.1-1.3 parts of a silane coupling agent KH, 2-3 parts of sodium lactate, 1.1-1.6 parts of sodium diacetate, 2-2.2 parts of diisononyl phthalate, 5-7 parts of epoxy tall oil acid butyl ester, 2-4 parts of oxidized starch, 20-23 parts of nano white carbon black, 6-8 parts of light calcium carbonate, 3-5 parts of sea-foam stone powder and 1-1.4 parts of an antioxidant 1010, wherein the modified poly-beta-hydroxybutyric acid PHB is prepared by blending and modifying poly-beta-hydroxybutyric acid PHB and high cis-butadiene rubber. The environment-friendly plastic material can be degraded by microbes and is low in decomposition rate, high in oxidation resistance and impact resistance and low in water-absorbing quality.

Description

technical field [0001] The invention relates to the technical field of plastic materials, in particular to an environment-friendly plastic material. Background technique [0002] Plastic materials are widely used, such as toys, plastic bottles, packaging bags, shopping bags, etc. We cannot live without plastics. However, as we all know, ordinary PP / PE plastics are difficult to decompose in the natural environment for hundreds of years, so discarded plastic products - also known as "white garbage" - are recognized as substances that can cause great damage to the environment. The accumulation of waste plastic products mixed in the soil will affect the absorption of nutrients and water by crops, resulting in reduced crop production and affecting agricultural development. Due to its extremely difficult to decompose, landfill treatment will not only occupy a large amount of land, but the occupied land will not be restored for a long time, affecting the sustainable use of land; i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L89/00C08L97/02C08L9/00C08K5/12C08K3/36C08K3/26C08K3/34
Inventor 李元焕
Owner 汕头市纳川塑胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap