Method for preparing nitrogen and potassium containing super absorbent resin by utilizing carboxymethyl sunflower disc

A technology of carboxymethyl sunflower and superabsorbent resin, which is applied in the field of superabsorbent resin, can solve the problems that superabsorbent resin is difficult to popularize and apply, use a large amount, increase the synthesis cost of superabsorbent resin, etc., and achieve low synthesis cost and high water absorption rate. Faster, omitting the effect of acidification and washing process

Inactive Publication Date: 2014-10-08
INNER MONGOLIA UNIVERSITY
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Among the above-mentioned types, the main hydrophilic monomer used is acrylic acid. In the past, the amount of hydrophilic monomer used in the synthesis of superabsorbent resins was very large, which greatly increased the synthesis cost of superabsorbent resins, resulting in It is difficult to popularize and apply superabsorbent resins, and domestic high-quality superabsorbent resin products mostly rely on imports, so research new methods or develop new varieties to produce high-quality superabsorbent resin products, and improve domestic superabsorbent resin products in the world. Market share is very important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing nitrogen and potassium containing super absorbent resin by utilizing carboxymethyl sunflower disc
  • Method for preparing nitrogen and potassium containing super absorbent resin by utilizing carboxymethyl sunflower disc
  • Method for preparing nitrogen and potassium containing super absorbent resin by utilizing carboxymethyl sunflower disc

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1: Weigh 2.5g of carboxymethyl sunflower discs, measure 25ml of deionized water, and fully stir the above materials. Weigh 5.67g of potassium hydroxide, measure 20ml of deionized water, and prepare a potassium hydroxide solution. Under the conditions of ice-water bath cooling and stirring, 14.6g (13.9ml) of acrylic acid was neutralized with the prepared potassium hydroxide solution. Weigh 2.92g of acrylamide and 10ml of deionized water to prepare a solution. Add 60mg of potassium persulfate initiator, 45mg of N,N'-methylenebisacrylamide crosslinking agent, prepared acrylamide solution and neutralized acrylic acid and its potassium salt solution in the reaction bottle, Stir at room temperature for half an hour to make it evenly mixed. At the same time, the heating rate is controlled, so that the temperature of the water bath is raised slowly, so that the reaction is fully carried out, and the stirring is stopped when the polymerization temperature is reached. ...

Embodiment 2

[0019] Example 2: Weigh 2.5g of carboxymethyl sunflower discs, measure 25ml of deionized water, and fully stir the above materials. Weigh 7g of potassium hydroxide, measure 20ml of deionized water, and prepare a potassium hydroxide solution. Under the conditions of ice-water bath cooling and stirring, 15g (14.3ml) of acrylic acid was neutralized with the prepared potassium hydroxide solution. Weigh 5g of acrylamide and 10ml of deionized water to prepare a solution. Add 75mg of potassium persulfate initiator, 35mg of N,N'-methylenebisacrylamide crosslinking agent, the prepared acrylamide solution and the neutralized acrylic acid and its potassium salt solution in the reaction bottle, under nitrogen protection , and stirred at room temperature for half an hour to make it evenly mixed. At the same time, the heating rate is controlled, so that the temperature of the water bath is raised slowly, so that the reaction is fully carried out, and the stirring is stopped when the polym...

Embodiment 3

[0020] Example 3: Weigh 2.5g of carboxymethyl sunflower discs, measure 25ml of deionized water, and fully stir the above materials. Weigh 7.15g of potassium hydroxide, measure 20ml of deionized water, and prepare a potassium hydroxide solution. Under the conditions of ice-water bath cooling and stirring, 13.1 g (12.5 ml) of acrylic acid was neutralized with the prepared potassium hydroxide solution. Weigh 4.4 g of acrylamide, measure 10 ml of deionized water, and prepare a solution. Add 60mg of potassium persulfate initiator, 35mg of N,N'-methylenebisacrylamide crosslinking agent, the prepared acrylamide solution and the neutralized acrylic acid and its potassium salt solution in the reaction bottle, under the protection of nitrogen , and stirred at room temperature for half an hour to make it evenly mixed. At the same time, the heating rate is controlled, so that the temperature of the water bath is raised slowly, so that the reaction is fully carried out, and the stirring ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing nitrogen and potassium containing super absorbent resin by utilizing a carboxymethyl sunflower disc. The method for preparing the nitrogen and potassium containing super absorbent resin by utilizing the carboxymethyl sunflower disc is characterized by comprising the following steps: mixing a certain amount of sodium hydroxide solution with sunflower disc powder in a three-opening bottle, soaking, so that the sunflower disc is fully swelled; dropwise adding the sodium hydroxide solution into the mixture, stirring for 1 hour in a water bath kettle at the temperature of 30 DEG C, then dropwise adding a sodium monochloroacetate solution in reaction mixture, carrying out reaction for 2 hours, then pouring the mixture after reaction is finished into a stainless steel disc, carrying out reaction in a drying oven, washing with 70% ethyl alcohol after drying is finished, then drying, and smashing, so that the carboxymethyl sunflower disc is obtained; uniformly mixing acrylic acid and potassium acrylate, acrylamide, the carboxymethyl sunflower disc, potassium persulphate, N,N'-methylene bisacrylamide and deionized water, protecting by adopting nitrogen, heating in water bath and stirring, stopping stirring at a polymerization temperature, continuously heating, insulating and carrying out reaction for 2 hours in boiling water bath, stopping introduction of nitrogen, taking out reactants, placing the reactants into a blast drying oven at the temperature of 40-60 DEG C to be dried to constant weight, and smashing, so that the nitrogen and potassium containing super absorbent resin product is obtained.

Description

technical field [0001] The invention relates to a method for synthesizing a superabsorbent resin containing nitrogen and potassium elements by taking carboxymethyl sunflower disc, acrylic acid and acrylamide as main raw materials. The superabsorbent resin prepared by this method has a wide range of uses in many fields, such as improving the soil aggregate structure in agriculture and forestry, increasing the water permeability and air permeability of the soil, improving the moisture retention performance of the soil, and promoting various nutrients in the soil. It can be used as oil field treatment agent, oil-water separation agent, etc. in petrochemical industry, and has achieved great success in the above fields. Background technique [0002] Superabsorbent Resin (SAR), also known as superabsorbent polymer (SAP), super absorbent, etc., it is a kind of resin containing a large amount of -OH, -COOH, -COONa, -CONH 2 It is a new type of functional polymer material with strong...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F251/02C08F220/56C08F220/06C08F222/38
Inventor 温国华郭玉婷王晓莉付渊陈超柳青韩宗壮杨永启张雨亭刘广华孙萌
Owner INNER MONGOLIA UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com