Intelligent aquagel based on cyclodextrin functional groups, and preparation method and application thereof

A functional group, tosyl cyclodextrin technology, applied in the field of intelligent hydrogel, can solve the problems of poor mechanical properties, poor biocompatibility, slow response rate, etc., to improve mechanical properties, fast response, improve Effect of swelling and deswelling kinetics

Inactive Publication Date: 2014-10-08
NANXIONG MATERIAL PRODION BASE OF CHINESE ACADEMY OF SCI GUANGZHOU CHEM +1
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional PNIPAAm hydrogels have shortcomings such as slow response rate, poor mechanical properties, poor biocompatibility, and poor mechanical properties, which limit their practical application in more fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Intelligent aquagel based on cyclodextrin functional groups, and preparation method and application thereof
  • Intelligent aquagel based on cyclodextrin functional groups, and preparation method and application thereof
  • Intelligent aquagel based on cyclodextrin functional groups, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A method for preparing a poly(N-isopropylacrylamide) smart hydrogel based on cyclodextrin functional groups in this embodiment, the specific preparation steps are as follows:

[0048] Weigh 0.4g of N-isopropylacrylamide (NIPAAm), 20mg of GCD and 32mg of BIS, dissolve in 4ml of dimethyl sulfoxide, mix the raw materials uniformly by ultrasonication for 15min, then add 10mg of azobisisobutylcyanide, and then mix thoroughly by ultrasonication for 15min before freezing Thaw cycle to remove oxygen, react at 60°C for 24 hours under the protection of nitrogen, crush the reactor, soak the gel in distilled water for a week, change the water every day, remove unreacted raw materials and obtain poly(N-iso Propylacrylamide) smart hydrogel, cut into 10mm*5mm cylindrical small pieces for later use, recorded as P(NIPAAm-co-GCD) 1 .

Embodiment 2

[0050] A method for preparing a poly(N-isopropylacrylamide) smart hydrogel based on cyclodextrin functional groups in this embodiment, the specific preparation steps are as follows:

[0051] Weigh 0.4g of N-isopropylacrylamide (NIPAAm), 40mg of GCD and 32mg of BIS, dissolve it in 4ml of dimethyl sulfoxide, mix the raw materials uniformly by ultrasonication for 15min, then add 10mg of azobisisobutylcyanide, and then mix thoroughly by ultrasonication for 15min before freezing Thaw cycle to remove oxygen, react at 60°C for 24 hours under the protection of nitrogen, crush the reactor, soak the gel in distilled water for a week, change the water every day, remove unreacted raw materials and obtain poly(N-iso Propylacrylamide) smart hydrogel, cut into 10mm*5mm cylindrical small pieces for later use, recorded as P(NIPAAm-co-GCD) 2 .

Embodiment 3

[0053] A method for preparing a poly(N-isopropylacrylamide) smart hydrogel based on cyclodextrin functional groups in this embodiment, the specific preparation steps are as follows:

[0054] Weigh 0.4g of N-isopropylacrylamide (NIPAAm), 60mg of GCD and 32mg of BIS and dissolve it in 4ml of dimethyl sulfoxide, mix the raw materials uniformly by ultrasonication for 15min, then add 10mg of azobisisobutylcyanide, and then 15min of ultrasonication to fully mix and freeze Thaw cycle to remove oxygen, react at 60°C for 24 hours under the protection of nitrogen, crush the reactor, soak the gel in distilled water for a week, change the water every day, remove unreacted raw materials and obtain poly(N-iso Propylacrylamide) smart hydrogel, cut into 10mm*5mm cylindrical small pieces for later use, recorded as P(NIPAAm-co-GCD) 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of intelligent aquagels, and discloses an intelligent aquagel based on cyclodextrin functional groups, and a preparation method and application thereof. The intelligent aquagel based on cyclodextrin functional groups is prepared by carrying out crosslinking polymerization reaction on previously prepared double-bond modified cyclodextrin and N-isopropyl acrylamide as polymerizable monomers by using N,N- methylene-bis-acrylamide, polyethyleneglycol bis(methyl)acrylate or polycaprolac-bis(methyl)acrylate as a crosslinking agent under the initiation of azodiisobutyl cyanogen. The cyclodextrin functional components containing special cavity structure are introduced to improve the swelling and deswelling dynamics of the aquagel, so that the response speed of the prepared aquagel is obviously enhanced. The aquagel can be used in the fields of drug controlled release and other biomedicines.

Description

technical field [0001] The invention belongs to the technical field of intelligent hydrogel, and in particular relates to an intelligent hydrogel based on a cyclodextrin functional group and its preparation method and application. Background technique [0002] Hydrogels are polymers with three-dimensional crosslinked or interpenetrating networks that can swell in water and absorb large amounts of water without dissolving them. According to the response of hydrogels to external environmental stimuli, they can be divided into traditional hydrogels and intelligent hydrogels. Among them, intelligent hydrogels can also be called stimulus-responsive or sensitive hydrogels. Environmental stimuli can produce hydrogels that respond to environmental stimuli, that is, to a considerable extent, they can sense, process and perform work in response to environmental microphysicochemical stimuli, such as temperature, electric field, magnetic field, light, pH, ionic strength, pressure, etc. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F251/00C08F220/54C08F222/38C08F291/12C08J3/075C08B37/16A61K47/40
Inventor 吕满庚李因文
Owner NANXIONG MATERIAL PRODION BASE OF CHINESE ACADEMY OF SCI GUANGZHOU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com