Surface-treated modified calcium carbonate and preparation method thereof

A surface treatment, calcium carbonate technology, applied in the direction of inorganic pigment treatment, chemical instruments and methods, dyeing low molecular organic compound treatment, etc., can solve the problems of poor compatibility, different interface properties, material mechanical properties decline, etc., to achieve compatibility Good sex and strong binding effect

Active Publication Date: 2015-07-01
CHIZHOU CELT NANO TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because its surface is hydrophilic, oleophobic and easy to agglomerate, its interface properties are different from those of organic polymers, and its compatibility is poor. Direct or excessive filling will easily lead to a decrease in the mechanical properties of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface-treated modified calcium carbonate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] specific implementation plan

[0014] The present invention will be described in detail below through specific examples.

[0015] A surface-treated modified calcium carbonate prepared from the following raw materials in parts by weight (kg): calcium carbonate 85, glyceryl tristearate 1, polyaspartic acid 1.5, rosin resin 3, nylon 664, Palmitic acid 1, crushed palm fiber 2, mullite 2, hydroxypropyl cellulose 1, titanate coupling agent TC-WT0.8, modified titanium dioxide 2.5;

[0016] The modified titanium dioxide is made of the following raw materials in parts by weight (kg): nano titanium dioxide 50, mica powder 2, pulverized zeolite molecular sieve 4, ferrocene 5, mineral fiber 3, sodium pyrophosphate 2, pure acrylic emulsion 3, ring Butyl oxyoleate 3, phosphate ester 2, water 50; the preparation method is to first add pure acrylic emulsion, nano-titanium dioxide, mica powder, crushed zeolite molecular sieve, mineral fiber, and water to form a suspension, and then imm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a surface-treated modified calcium carbonate. The invention is characterized in that the surface-treated modified calcium carbonate is prepared from the following raw materials in parts by weight: 85-90 parts of calcium carbonate, 1-2 parts of glyceryl tristearate, 1.5-2.5 parts of polyaspartic acid, 3-5 parts of rosin resin, 4-6 parts of nylon 66, 1-1.5 parts of palmitic acid, 2-3 parts of pulverized monkey grass, 2-3 parts of mullite, 1-2 parts of hydroxypropyl cellulose, 0.8-1 part of titanate coupling agent TC-WT and 2.5-3.5 parts of modified titanium dioxide. The calcium carbonate surface is modified by the high-molecular polymer, so that the calcium carbonate has the high-molecular polymer layer; the calcium carbonate has many active groups, and thus, has favorable compatibility with many substances. For example, the unsaturated double bond can generate crosslinking reaction with the film-forming matters in the rubber, plastic and paint to generate very strong binding force, and the use of abundant calcium carbonate as the filler can not lower the properties of the product.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a surface-treated modified calcium carbonate and a preparation method thereof. Background technique [0002] Due to its good stability, pure color, low wear, easy processing, non-toxicity, wide range of sources, low price and many other advantages, calcium carbonate is often used to fill plastics, rubber and other materials to increase capacity, increase and reduce production costs. However, because its surface is hydrophilic and oleophobic and is easy to agglomerate, it has different interfacial properties with organic polymers and poor compatibility. Direct or excessive filling will easily lead to a decrease in the mechanical properties of the material. Through modification, its surface properties can be improved, and the comprehensive properties such as dispersibility, compatibility with the polymer interface and mechanical strength of the material can be improved. Contents...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/02C09C3/06C09C3/08C09C3/10
Inventor 顾庆雷徐宇坤顾宗军高健健倪伯祥张长来曹继勇徐建林陶沈杰张小桐
Owner CHIZHOU CELT NANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com