Moisture absorption and sweat releasing antibacterial cotton polyester knitted fabric

A knitted fabric, moisture absorption and perspiration technology, applied in knitting, weft knitting, warp knitting and other directions, can solve the problems of uncomfortable hand feeling, moisture absorption and perspiration effect and antibacterial effect, etc., to achieve comfortable hand feeling and excellent moisture absorption Perspiration and antibacterial properties, degrading effect

Inactive Publication Date: 2014-09-17
JIANGSU JINHONG KNITTING
View PDF6 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the moisture-wicking and antibacterial effects of cotton-polyester knitted fabrics are not very ideal, while cotton-polyester knitted fabrics with better moisture-wicking and antibacterial properties are not very comfortable to the touch.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of moisture-wicking and antibacterial cotton-polyester knitted fabric is made by blending 55 parts by weight of negative ion polyester fiber and 45 parts by weight of cotton fiber;

[0014] Described fabric is through following composite finishing process:

[0015] Put the fabric into the deionized water solution, the bath ratio is 3:10, first add 4.5g / L nano-silver antibacterial agent, 2.3g / L polyvinylpyrrolidone, 2.3g / L polyphenol sulfonic acid condensate, 1.2g / L polyoxygen Ethylene sorbitan fatty acid ester, heat up to 60°C, let stand for 25 minutes; then add 1.2g / L paraffin, 8.9g / L polyester polyether linear block compound, heat up to 70°C, let stand for 25 minutes; Finally, add isopropanolamine to adjust the pH value to 4.0, raise the temperature to 85°C, and let it stand for 35 minutes; wash the fabric for 35 minutes after taking it out, dehydrate it, and dry it at 85°C for 2 hours.

Embodiment 2

[0017] A kind of moisture-wicking and antibacterial cotton-polyester knitted fabric is made by blending 55 parts by weight of negative ion polyester fiber and 45 parts by weight of cotton fiber;

[0018] Described fabric is through following composite finishing process:

[0019] Put the fabric into the deionized water solution, the bath ratio is 3:10, first add 5g / L nano-silver antibacterial agent, 3g / L polyvinylpyrrolidone, 3g / L polyphenol sulfonic acid condensate, 2g / L polyoxyethylene dehydrated sorrel Alcohol fatty acid ester, heat up to 60°C, let stand for 25 minutes; then add 2g / L paraffin, 9g / L polyester polyether linear block compound, heat up to 70°C, let stand for 25 minutes; finally add isopropanolamine Adjust the pH value to 4.0, raise the temperature to 85°C, and let it stand for 35 minutes; wash the fabric for 35 minutes after taking it out, dehydrate, and dry at 85°C for 2 hours.

Embodiment 3

[0021] A kind of moisture-wicking and antibacterial cotton-polyester knitted fabric is made by blending 55 parts by weight of negative ion polyester fiber and 45 parts by weight of cotton fiber;

[0022] Described fabric is through following composite finishing process:

[0023] Put the fabric into the deionized water solution, the bath ratio is 3:10, first add 4g / L nano-silver antibacterial agent, 2g / L polyvinylpyrrolidone, 2g / L polyphenolsulfonic acid condensate, 1g / L polyoxyethylene dehydrated sorrel Alcohol fatty acid ester, heat up to 60°C, let stand for 25 minutes; then add 1g / L paraffin, 8g / L polyester polyether linear block compound, heat up to 70°C, let stand for 25 minutes; finally add isopropanolamine Adjust the pH value to 4.0, raise the temperature to 85°C, and let it stand for 35 minutes; wash the fabric for 35 minutes after taking it out, dehydrate, and dry at 85°C for 2 hours.

[0024]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses moisture absorption and sweat releasing antibacterial cotton polyester knitted fabric. The moisture absorption and sweat releasing antibacterial cotton polyester knitted fabric is formed by blending and weaving, by weight, 55 parts of anionic polyester fibers and 45 parts of cotton fibers, and the fabric is manufactured according to the following composite arranging process: the fabric is placed in deionization aqueous solutions, the bath ratio is 3:10, the 4-5g / L nano-silver antimicrobials, 2-3g / L polyvinylpyrrolidone, 2-3g / L polyphenol sulfonic acid condensation products and 1-2g / L polyoxyethylene sorbitan fatty acid ester are firstly added, and are heated to 60 DEG C, and standing is carried out for 25 minutes; then, the 1-2g / L paraffin and 8-9g / L polyester linear block compounds are added, and are heated to 70 DEG C, and standing is carried out for 25 minutes; finally, isopropanolamine is added to adjust the pH value to be 4.0, the isopropanolamine is heated to 85 DEG C, and standing is carried out for 35 minutes, the fabric is taken out for being washed for 35 minutes by water, water removing is performed, and the fabric is dried for 2 hours at the temperature of 85 DEG C. The cotton polyester knitted fabric is comfortable in hand feeling, and has the excellent moisture absorption and sweat releasing antibacterial performance.

Description

technical field [0001] The invention relates to a moisture-absorbing, sweat-wicking and antibacterial cotton-polyester knitted fabric. Background technique [0002] At present, the moisture absorption and perspiration and antibacterial properties of cotton-polyester knitted fabrics are not ideal, while the cotton-polyester knitted fabrics with good moisture absorption and perspiration and antibacterial properties are not very comfortable to the touch. Contents of the invention [0003] The object of the present invention is to provide a moisture-absorbing, sweat-wicking and antibacterial cotton-polyester knitted fabric, which is comfortable to the touch and has excellent moisture-wicking, sweat-wicking and antibacterial properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of moisture absorption and perspiration antibacterial cotton-polyester knitted fabric, which is made by blending 55 parts by weigh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04B1/14D04B21/00D06M15/356D06M15/53D06M11/83D06M101/32D06M101/06
Inventor 张惠元
Owner JIANGSU JINHONG KNITTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com