Method for preparing rice starch acetate through supported heteropoly acid catalyst

A technology for immobilizing heteropolyacid and starch acetate, applied in the field of starch deep processing, can solve the problems of high environmental harm, low economic benefit, equipment damage, etc. Effect

Active Publication Date: 2014-09-10
广西利佰兴食品集团有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although starch acetate with a high degree of substitution meeting the requirements can be produced, concentrated sulfuric acid will not only degrade the starch, resulting in a low yield, but also cause damage to the equipment and cause great harm to the environment.
In recent years, it has been reported that organic acid, iodine, etc. are used as catalysts to prepare highly substituted acetate starch. Although the yield obtained is high, it is difficult to recover the catalyst and the economic benefit is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing rice starch acetate through supported heteropoly acid catalyst
  • Method for preparing rice starch acetate through supported heteropoly acid catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Use activated carbon with Keggin structure as a carrier, take 9 parts of activated carbon, mix 3 parts of phosphotungstic acid with 60 parts of sulfuric acid solution with a concentration of 1mol / L, heat the activated carbon with it and reflux for 12 hours, place it for one day, and bake it at 140°C dry to obtain the desired solid-supported catalyst.

[0024] Weigh 10 parts of rice starch, add 25 parts of glacial acetic acid, stir at room temperature for 3 minutes to make it evenly mixed, add 3 parts of solid-loaded heteropolyacid and 25 parts of acetic anhydride in a constant temperature water bath at 75°C, and react for 2 hours , suction filtration, the filtrate was poured into 1L distilled water, a large amount of starch was separated out, washed, extracted, vacuum-dried at 40°C, ground and sieved to obtain rice starch acetate with a degree of substitution of 2.51.

Embodiment 2

[0026] Use activated carbon with a Keggin structure as a carrier, take 11 parts of activated carbon, mix 4 parts of phosphomolybdic acid with 50 parts of sulfuric acid solution with a concentration of 0.5mol / L, and heat the activated carbon with it for 12 hours and then place it for one day at 140°C drying to obtain the desired solid-supported catalyst.

[0027] Weigh 10 parts of rice starch, add 27 parts of glacial acetic acid, stir at room temperature for 3 minutes to make it evenly mixed, and add 4 parts of solid-loaded heteropoly acid and 30 parts of acetic anhydride in an environment of constant temperature water bath at 80°C, and react for 2.5 hours , suction filtration, the filtrate was poured into 1L distilled water, a large amount of starch was separated out, washed, extracted, vacuum-dried at 40°C, ground and sieved to obtain rice starch acetate with a degree of substitution of 2.65.

Embodiment 3

[0029] Use activated carbon with a Keggin structure as a carrier, take 12 parts of activated carbon, mix 5 parts of phosphovanadic acid with 60 parts of sulfuric acid solution with a concentration of 1mol / L, heat the activated carbon with it for 12 hours, place it for one day, and bake it at 140°C dry to obtain the desired solid-supported catalyst.

[0030] Weigh 10 parts of rice starch, add 20 parts of glacial acetic acid, stir at room temperature for 3 minutes to make it evenly mixed, and add 3 parts of recovered solid-loaded heteropolyacid and 25 parts of acetic anhydride in an environment of constant temperature water bath at 70°C, and react After 2 hours, filter with suction, pour the filtrate into 1L of distilled water, precipitate a large amount of starch, wash, extract, vacuum-dry at 40°C, grind and sieve to obtain rice starch acetate with a substitution degree of 2.50.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing rice starch acetate through a supported heteropoly acid catalyst. The method mainly comprises the following steps: preparing an activated carbon supported heteropoly acid catalyst; by taking glacial acetic acid as a solvent, taking acetic anhydride as an esterifying agent, reacting at the temperature of 70-80 DEG C for 2-3 hours under the catalytic action of the supported heteropoly acid; performing primary suction filtration, and recovering the supported heteropoly acid; and pouring the filtrate into lots of distilled water for washing, performing secondary suction filtration, obtaining the product, drying in a vacuum environment, grinding, screening, and obtaining high-substitution-degree rice starch acetate which has the substitution degree of over 2.5 and of which the highest substitution degree is 2.7. The method has the characteristics that the reaction efficiency is high, the catalyst can be recovered and repeatedly used, and the method is green and safe.

Description

Technical field: [0001] The invention relates to a method for preparing rice starch acetate with a high degree of substitution using a solid-carried heteropolyacid as a catalyst, and belongs to the field of starch deep processing. technical background: [0002] Rice is my country's largest food source, accounting for about 30% of the world's output, with a total annual output of about 180 million tons. In the rice processing process, due to the existing rice milling technology, it is inevitable to produce broken rice. According to statistics, at least 20 million tons of broken rice are produced every year in my country, and these broken rice are usually used to produce feed, and their economic value is very low. Therefore, the deep processing and utilization of rice starch is of great significance. [0003] Due to its low price, abundant sources, renewable and biodegradable properties, starch has a wide range of uses in many industrial productions. However, natural starch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08B31/04
Inventor 刘忠义包浩彭丽乔丽娟陈婷刘令
Owner 广西利佰兴食品集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap