Polymer powder for 3D printing and preparation method of polymer powder

A 3D printing and polymer technology, applied in the field of polymer powder and its preparation, can solve the problems of high production cost, unsuitable for preparing human medical implant materials, complex production process, etc., achieve good molding effect, eliminate harm to human body and Environmental hazards and excellent mechanical properties

Inactive Publication Date: 2014-06-25
ZHONGSHAN POLYTECHNIC
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese invention patent "Preparation method of a rapid prototyping material for three-dimensional printing" (CN102093646A) discloses a preparation method of a rapid prototyping material for three-dimensional printing, but its powder material and the main components of the bonding solution are both It is an organic resin, its production process is relatively complicated, the cost is high, and it is not suitable for the preparation of human medical implant materials
In addition, the Chinese invention patent "A Highly Tough and Highly Cohesive 3D Printing Molding Material and Its Preparation Method" (CN103205107A) discloses a molding material and its preparation method. The bond strength of solid parts printed with this material is , firmness, good flexibility, scratch resistance and other properties are ideal, but because the adhesive uses a high-temperature thermal spray system, the production cost is very high, and it is only suitable for printing medical implant materials with very high quality requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer powder for 3D printing and preparation method of polymer powder
  • Polymer powder for 3D printing and preparation method of polymer powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The formula is: comprising the following components by weight, 60 parts of polymethyl methacrylate, 30 parts of starch, 8 parts of methyl cellulose, and 2 parts of superfine silicon dioxide powder.

[0021] Preparation method: Mix 60 parts of polymethyl methacrylate, 30 parts of starch, 8 parts of methyl cellulose and 2 parts of superfine silicon dioxide powder, then fully stir at room temperature until the mixture is uniform to obtain a molding powder Material 1.

Embodiment 2

[0023] The formula is: comprising the following components by weight, 50 parts of polystyrene, 35 parts of maltodextrin, 8 parts of sodium carboxymethyl cellulose, and 7 parts of superfine aluminum oxide powder.

[0024] Preparation method: Mix 50 parts of polystyrene, 35 parts of maltodextrin, 8 parts of sodium carboxymethyl cellulose and 7 parts of superfine aluminum oxide powder, then fully stir at room temperature until the mixture is uniform. Molded powder material 2.

Embodiment 3

[0026] The formula is: comprising the following components by weight, 30 parts of polymethyl methacrylate and 10 parts of polyvinyl alcohol.

[0027] Preparation method: Mix 30 parts of polymethyl methacrylate and 10 parts of polyvinyl alcohol, and then fully stir at room temperature until the mixture is uniform to prepare the molding powder material 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer powder for 3D printing and a preparation method of the polymer powder. The polymer powder comprises the following substances in parts by weight: 30-90 parts of main body molding resin, 10-60 parts of bonding resin, 0-10 parts of composite resin and 0-10 parts of powder leveling agent. The preparation method for preparing the powder comprises: blending the substances at room temperature and then sufficiently stirring till the substances are evenly mixed. The powder can be used for printing human body medical implant materials with good flexibility and medical appliances; when the powder is used for 3D printing, only deionized water is used as bonding solution, so that the process is simple and the cost is low; therefore, the 3D printing environment is environmental friendly and can meet a modern green manufacturing direction.

Description

【Technical field】 [0001] The invention relates to the field of 3D printing molding materials, more specifically a polymer powder for 3D printing and a preparation method thereof. 【Background technique】 [0002] 3D printing (Three Dimensional Printing) technology is a rapid prototyping technology with the fastest development speed and the greatest development potential. It has the advantages of low cost, simple process, quick use, and diversity. It has been widely used in aviation industry, construction Design, preparation of medical devices, automotive industry, etc. At present, the most commonly used 3D printing system is based on jet printing technology. The bonding solution is sprayed out in a dot matrix through the piezoelectric nozzle according to the design data, and the powder material is bonded into a two-dimensional cross-section, and this process is repeated back and forth. Finally, The various sections are bonded and superimposed layer by layer to obtain the requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/12C08L3/02C08L25/06C08L5/00C08L1/26C08L29/04C08K3/36C08K3/22
Inventor 冷小冰
Owner ZHONGSHAN POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com