Cable scarfskin and preparation method thereof

A sheathing and cable technology, applied in the direction of cables, insulated cables, electrical components, etc., can solve the problems of damage to the nose, mouth and throat of on-site personnel, difficulty in escaping from the fire scene, and easy disorientation of victims, etc., to achieve increased high-temperature heat Stability, excellent flexibility, good thermal stability effect

Inactive Publication Date: 2014-04-16
福建福硕线缆股份有限公司
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At the same time, most of the existing cable sheaths contain halides. In a fire, the halogen-containing cables will consume a lot of oxygen and release a lot of smoke, such as carbon monoxide and carbon dioxide, as well as acidic and toxic gases, which will damage the noses, Mouth and throat, the smoke also makes victims easily disoriented and difficult to escape from the scene of the fire, which is the greatest threat to human life in a fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] A method for preparing a cable sheath, comprising the steps of:

[0063] Ingredients: prepare raw materials according to parts by weight;

[0064] Mixing: Add magnesium hydroxide, aluminum hydroxide, silicone and silane into the high-speed mixer and mix for 5-10 minutes, then add ethylene-vinyl acetate copolymer, maleic anhydride grafted ethylene-vinyl acetate copolymer, Maleic anhydride grafted polyethylene, filler, antioxidant 1010, zinc oxide, iron oxide, epoxy soybean oil and toner, mix for 15-20min, then add polyethylene, mix for 15-20min, the high speed The speed of the mixer is 900-1000rpm, and the temperature is 120-150°C;

[0065] Pelletizing: After the raw materials are mixed, they are extruded and pelletized by a twin-screw extruder, and then packed.

Embodiment 1

[0067] A cable sheath, said cable sheath comprises the following materials by weight:

[0068] 80 parts of ethylene-vinyl acetate copolymer,

[0069] 70 parts of magnesium hydroxide,

[0070] 70 parts of aluminum hydroxide,

[0071] 30 parts of maleic anhydride grafted ethylene-vinyl acetate copolymer,

[0072] 30 parts of maleic anhydride grafted polyethylene,

[0073] Zinc borate 20 parts,

[0074] Silicone 5 parts,

[0075] 5 parts of silane,

[0076] Calcium carbonate 40 parts,

[0077] Antioxidant 1010 1 part,

[0078] 1 part zinc oxide,

[0079] 1 part iron oxide,

[0080] 3 parts epoxy soybean oil,

[0081] 2 parts of toner,

[0082] Polyethylene 5 parts,

[0083] The content of vinyl acetate in the ethylene-vinyl acetate copolymer is 25%.

[0084] A method for preparing a cable sheath, comprising the steps of:

[0085] Ingredients: prepare raw materials according to parts by weight;

[0086] Mixing: Add magnesium hydroxide, aluminum hydroxide, silicone a...

Embodiment 2

[0089] A cable sheath, said cable sheath comprises the following materials by weight:

[0090] 120 parts of ethylene-vinyl acetate copolymer,

[0091] 90 parts of magnesium hydroxide,

[0092] 90 parts of aluminum hydroxide,

[0093] 40 parts of maleic anhydride grafted ethylene-vinyl acetate copolymer,

[0094] 40 parts of maleic anhydride grafted polyethylene,

[0095] Zinc borate 30 parts,

[0096] Silicone 8 parts,

[0097] 8 parts of silane,

[0098] Montmorillonite 60 parts,

[0099] Antioxidant 1010 2 parts,

[0100] Zinc oxide 2 parts

[0101] Iron oxide 2 parts,

[0102] 5 parts epoxy soybean oil,

[0103] 3 parts of toner,

[0104] Polyethylene 8 parts,

[0105] The content of vinyl acetate in the ethylene-vinyl acetate copolymer is 30%.

[0106] A method for preparing a cable sheath, comprising the steps of:

[0107] Ingredients: prepare raw materials according to parts by weight;

[0108] Mixing: Add magnesium hydroxide, aluminum hydroxide, silicone,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cable scarfskin which comprises the following materials in parts by weigh: ethylene-vinyl-acetate copolymer, magnesium hydroxide, aluminum hydroxide, maleic anhydride grafted ethylene- vinyl-acetate copolymer, maleic anhydride grafted polyethylene, silicone, silane, fillers, antioxygen 1010, zinc oxide, ferric oxide, epoxidized soybean oil, toner and polyethylene. The cable scarfskin has the characteristics of good flexibility, high impact resistance, high environmental stress resistance, and the like, by compounding EVA and PE. A flaw which can cause crack can not appear. Meanwhile, in order to overcome the defects of flammability, a plurality of auxiliaries, such as aluminum hydroxide and magnesium hydroxide, are added, thereby improving the fire resistance of the cable scarfskin. Materials comprising halide are not added, which makes the cable scarfskin have no halogen. The fillers are added to make the heat stability of the cable scarfskin good. The cable scarfskin can be used at 105 DEG C.

Description

technical field [0001] The invention belongs to the technical field of cable production, in particular to a cable sheath and a preparation method thereof. Background technique [0002] Cable is a general term for items such as optical cables and cables. There are many uses of cables, mainly used for multiple functions such as control installation, connection equipment, power transmission, etc. It is a common and indispensable thing in daily life. [0003] Due to the long-term use, the temperature of the working environment will be very high, so the outer sheath of the cable is required to have the property of high temperature resistance. [0004] At the same time, most of the existing cable sheaths contain halides. In a fire, the halogen-containing cables will consume a lot of oxygen and release a lot of smoke, such as carbon monoxide and carbon dioxide, as well as acidic and toxic gases, which will damage the noses, Mouth and throat, smoke also makes victims easily lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/08C08L23/06C08L83/04C08K13/06C08K9/06C08K3/22C08K3/38C08K5/1515C08K3/26C08K3/34C08K3/36
CPCC08L23/0853C08L2201/02C08L2201/08C08L2201/22C08L2203/202C08L2205/025C08L2205/035H01B3/441H01B7/295C08L51/06C08L23/06C08L83/04C08K13/06C08K9/06C08K2003/2224C08K2003/2227C08K3/38C08K5/1515C08K2003/2296C08K2003/2265
Inventor 陈乃煌陈道铃
Owner 福建福硕线缆股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com