Process for producing medium gauge aluminum foil for 8150 blank

A technology of aluminum foil and blank, applied in the field of 8150 blank production of single-zero aluminum foil, can solve the problems of low tensile strength, low elongation, low yield rate, etc., and achieve the effect of not easy to break, high yield rate, and excellent number of pinholes

Active Publication Date: 2014-04-16
陇西西北铝铝箔有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a process for producing single-zero aluminum foil from 8150 blanks, so as to solve the defects of low tensile strength and low elongation of the existing 1000 series alloy single-zero aluminum foil, which lead to easy cracking during stamping and low yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A process for producing single-zero aluminum foil from 8150 blanks, comprising the following steps:

[0022] (1) Intermediate rolling: the 8150 billet with a thickness of 0.25mm is passed through 0.25mm-0.16mm-0.11mm-0.075mm-0.05mm through the process of low-roughness rolls, low-pass reduction, and high additive content in the intermediate rolling mill. 4 passes make a single-zero aluminum foil blank with a thickness of 0.05㎜; among them, the roll parameters of the four passes of 0.25㎜—0.16㎜—0.11㎜—0.075㎜—0.05㎜ have a convexity of 0.06㎜, a roughness of 0.12~0.14μm, Additive content is 7-9%; other parameters are as follows:

[0023] (a) The rolling speed of 0.25㎜-0.16㎜ pass is controlled at 300m / min~380m / min, the total rolling force is 135~145 tons, the uncoiling tension is 1000~1200㎏, the shape control curve: 15-0, spray The oil flow is controlled at 50% to 60% of the total flow;

[0024] (b) The rolling speed of 0.16㎜—0.11㎜ pass is controlled at 350m / min~380m / min, the...

Embodiment 2

[0033] A process for producing single-zero aluminum foil from 8150 blanks, comprising the following steps:

[0034] (1) Intermediate rolling: the 8150 billet with a thickness of 0.25mm is passed through 0.25mm-0.16mm-0.11mm-0.075mm-0.05mm through the process of low-roughness rolls, low-pass reduction, and high additive content in the intermediate rolling mill. 4 passes to make a single-zero aluminum foil blank with a thickness of 0.05㎜; among them, 0.25㎜-0.16㎜-0.11㎜-0.075㎜-0.05㎜ roll parameters in the four passes have a convexity of 0.06㎜, a roughness of 0.13μm, and additive content 8%; the remaining parameters are as follows:

[0035] (a) The rolling speed of 0.25㎜—0.16㎜ pass is controlled at 350m / min, the total rolling force is 140 tons, the uncoiling tension is 1100㎏, the plate shape control curve is 15-0, and the spray oil flow rate is controlled at 55% of the total flow rate. %;

[0036] (b) The rolling speed of 0.16㎜—0.11㎜ pass is controlled at 360m / min, the total roll...

Embodiment 3

[0045] A process for producing single-zero aluminum foil from 8150 blanks, comprising the following steps:

[0046](1) Intermediate rolling: the 8150 billet with a thickness of 0.25mm is passed through 0.25mm-0.16mm-0.11mm-0.075mm-0.05mm through the process of low-roughness rolls, low-pass reduction, and high additive content in the intermediate rolling mill. 4 passes to make a single-zero aluminum foil blank with a thickness of 0.05㎜; among them, the roll parameters of the four passes of 0.25㎜—0.16㎜—0.11㎜—0.075㎜—0.05㎜ have a convexity of 0.06㎜, a roughness of 0.14μm, and additive content 9%; the remaining parameters are as follows:

[0047] (a) The rolling speed of 0.25㎜—0.16㎜ pass is controlled at 380m / min, the total rolling force is 145 tons, the uncoiling tension is 1200kg, the plate shape control curve is 15-0, and the spray oil flow rate is controlled at 60% of the total flow rate. %;

[0048] (b) The rolling speed of 0.16㎜—0.11㎜ pass is controlled at 380m / min, the tot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a process for producing medium gauge aluminum foil for an 8150 blank. The defects that existing medium gauge aluminum foil produced by 1000-series alloy is low in tensile strength and ductility, easy to crack in the stamping process and low in yield are overcome. The medium gauge aluminum foil comprises iron, silicon, copper, manganese, titanium, chromium, zinc, cadmium, lithium, lead, magnesium and aluminum. The production process comprises the steps of intermediate rolling, thickness shearing and annealing packaging. The processed medium gauge aluminum foil for an 8150 alloy container is extremely good in tensile strength, ductility and other properties, not easy to crack in the stamping process and high in yield.

Description

technical field [0001] The invention relates to a process for producing single zero aluminum foil from 8150 blank. Background technique [0002] Aluminum is the most abundant metal element in the earth's crust, and its content accounts for about 8.8% of the total mass of the earth's crust. Aluminum in nature exists in the form of compounds, and about 70% of the aluminum in the earth's crust is made of Al 2 o 3 form exists in nature. Aluminum and aluminum alloy products are widely used in the packaging industry, transportation industry, and construction industry, of which the packaging industry accounts for about 18.5%. Aluminum is a good packaging material for food, beverages, medicines, cosmetics and other items. Its uses are becoming more and more extensive, and its consumption is increasing year by year. [0003] China has now become a major producer of primary aluminum and aluminum products, and a net exporter of aluminum processed products. Aluminum processing produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/40B21B37/00B21B37/46B21B37/58
Inventor 董文胜姚学勇常斌
Owner 陇西西北铝铝箔有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap