Gel injection type profile control agent
A profile control agent and gel-type technology, which is applied in the field of injection gel-type profile control agent, can solve the problems of small profile control radius, influence on profile control effect, and short validity period of profile control, so as to expand the swept volume and improve recovery rate effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] The content of acrylamide is 3.5g / L, then add 0.008g / L of potassium persulfate, 0.015g / L of N,N-methylenebisacrylamide, 40mg / L of 1,1-diphenyl-2 - Trinitrophenylhydrazine and 0.6g / L Tris-HCl buffer solution to obtain the injected gel type profile control agent. The solution was sampled and tested. The viscosity of the profile control agent solution was 200.3mPa.s at 24h, 2134mPa.s after 48h, and 3256mPa.s at 10d. The profile control agent gelled obviously and had good stability .
Embodiment 2
[0015] The content of acrylamide is 5g / L, then add 0.02g / L potassium persulfate, 0.03g / L N, N-methylenebisacrylamide, 20mg / L sodium hypophosphite and 0.5g / L Tris-HCl buffer solution to obtain the injected gel-type profile control agent. The solution was sampled and tested. The viscosity of the profile control agent solution was 350.6mPa.s at 24h, 3689mPa.s after 48h, and 3876mPa.s at 10d. The profile control agent gelled obviously and had good stability .
Embodiment 3
[0017] The content of acrylamide is 4g / L, then add 0.01g / L of sodium persulfate, 0.02g / L of N-methylolacrylamide, 0.5g / L of Tris-HCl buffer to obtain the injection gel type Profile control agent. The solution was sampled and tested. The viscosity of the profile control agent solution was 1600.6mPa.s at 24h, 2420mPa.s after 48h, and 3476mPa.s at 10d. The profile control agent gelled obviously and had good stability .
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com