Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Modifier for regeneration processing of mixed waste plastic tube material and usage method thereof

A technology for processing modifiers and plastic pipes, which is applied in the field of regenerating and processing modifiers for mixed waste plastic pipe materials, can solve the problems of unsubstantially improved processing methods, complex components, poor compatibility, etc., so as to improve the use value, The effect of improving compatibility and improving strength

Inactive Publication Date: 2014-03-26
PLASTIC UNION NEW MATERIAL TECH HUBEI
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the complex composition of mixed waste plastic pipes, poor compatibility during recycling, and no substantial improvement in processing methods, the defects of traditional waste plastic processing methods are still retained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The mixed waste plastic pipe material recycling processing modifier of the present invention, its raw material formula is represented by weight ratio and includes the following components: maleic anhydride 1; chlorinated polyethylene 2; ethylene·vinyl acetate copolymer 3; styrene ·Butadiene·styrene block copolymer 4; styrene 5, for later use; Put the above-mentioned modifier raw material components together into a high-speed mixer at a temperature of 110°C and mix evenly, then discharge and cool for later use.

[0014] The using method of modifying agent of the present invention operates according to the following steps:

[0015] (1) Classify waste mixed plastic pipes to obtain PE, PP, PA, PET, PVC and other mixed waste plastic pipe wool;

[0016] (2) After crushing, cleaning, dehydrating and drying all kinds of mixed waste plastic tubes obtained from the above classification to obtain various mixed waste plastic raw materials, and then testing the mixed waste plastic r...

Embodiment 2

[0020] This embodiment is basically the same as Embodiment 1, the difference is that:

[0021] The components and parts by weight of the mixed waste plastic pipe material recycling processing modifier of the present invention are: maleic anhydride 2; chlorinated polyethylene 2.5; ethylene-vinyl acetate copolymer 3.5; styrene-butadiene · Styrene block copolymer 4.5; Styrene 5.5; Put the above modifier raw material components together into a high-speed mixer with a temperature of 120°C for mixing.

[0022] The method of using the modifier of the present invention: (3) The amount of the modified modifier is 4% of the total weight after mixing, and the temperature is raised to 108°C at room temperature; (4) Use a plastic granulator Granulation was carried out under the temperature condition of 215° C., and the granulation time was 16 minutes.

Embodiment 3

[0024] This embodiment is basically the same as Embodiment 1, the difference is that:

[0025] The components and parts by weight of the mixed waste plastic pipe material recycling processing modifier of the present invention are: maleic anhydride 3.5; chlorinated polyethylene 4; ethylene-vinyl acetate copolymer 5.5; styrene-butadiene · Styrene block copolymer 6.5; Styrene 7; put the above-mentioned modifier raw material components together into a high-speed mixer at a temperature of 118°C for mixing.

[0026] The method of using the modifier of the present invention: (3) The dosage of the prepared modifier is 5% of the total weight after mixing, and the temperature is raised to 107°C at room temperature; (4) Use a plastic granulator Granulate under the temperature condition of 170 DEG C, and the granulation time is 20 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modifier for regeneration processing of mixed waste plastic tube materials. The modifier comprises the following components by weight: 1-6 parts of maleic anhydride, 2-6 parts of chlorinated polyethylene, 3-8 parts of an ethylene-vinyl acetate copolymer, 4-9 parts of a styrene-butadiene-styrene block copolymer and 5-9 parts of styrene. A preparation technology of the modifier is as below: adding raw materials into a high speed feed mixer for uniform mixing, discharging and cooling for standby. A usage method of the modifier for regeneration processing of mixed waste plastic tube materials comprises the following steps: (1) classifying to obtain waste plastic tube materials; (2) crushing, washing, dehydrating, drying, dehumidifying and detecting the mixed waste plastic tube materials; (3) mixing and heating the modifier with the mixed waste plastic raw materials, carrying out a grafting reaction, and cooling for standby; and (4) granulating. The invention has the advantages of simple process, convenient operation, low cost and no pollution, and can be widely used in the field of regeneration processing of waste plastic tubes.

Description

technical field [0001] The invention relates to a recycling processing aid for waste plastics and an application method thereof, in particular to a recycling processing modifier for mixed waste plastic pipe materials and a using method thereof. Background technique [0002] As we all know, the traditional method of recycling waste plastics is generally to reheat and plasticize waste plastics to make them enter a viscous flow state and then pelletize them for utilization. Due to the high uneven heating of waste plastics, this method depolymerizes the macromolecular chains, loses some of the original compatibility of waste plastics, and greatly reduces its physical properties, and heating under the condition of moisture will make the plastics Further aging and degradation, therefore, the waste plastic recycled plastic processed by this method is of poor quality. In recent years, although some enterprises and researchers have added modifiers to waste plastics, the mechanical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/06C08L53/02C08L23/28C08L23/08C08L23/06C08L23/12C08L77/00C08L67/02C08L27/06C08F291/00C08F291/12C08F291/06C08F291/04C08F222/06
Inventor 邓丽邓军邓忠权陈绪煌
Owner PLASTIC UNION NEW MATERIAL TECH HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com