Preparation method of spherical aluminum hypophosphite

A technology of aluminum hypophosphite and sodium hypophosphite, applied in chemical instruments and methods, phosphorus compounds, inorganic chemistry, etc., can solve problems such as the decline of mechanical properties, reduce the decline of mechanical properties, improve flame retardant effect, crystal form regular effect

Active Publication Date: 2015-06-17
JINAN TAIXING FINE CHEM
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the problems of the particle size and crystal form of the above-mentioned aluminum hypophosphite, and provide a method for preparing spherical aluminum hypophosphite, so that the particle size of the synthesized aluminum hypophosphite can reach about 7 microns, and the crystal form is spherical. It avoids problems such as the decline of mechanical properties caused by large particle size and irregular crystal form. At the same time, the addition of seed crystals makes it a phosphorus-nitrogen flame retardant system, which improves the flame retardant effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of spherical aluminum hypophosphite
  • Preparation method of spherical aluminum hypophosphite
  • Preparation method of spherical aluminum hypophosphite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Formula (parts by weight): sodium hypophosphite 90, aluminum sulfate octadecahydrate 110, water 200, melamine cyanurate 5, polyacrylamide 2.5.

[0020] Preparation method: Weigh the raw materials according to the above weight parts, first add water into the reaction vessel as a solvent, start stirring, add aluminum sulfate octadecahydrate and melamine cyanurate into the reaction kettle, add polyacrylamide at the same time, stir evenly and heat up to 60 Add sodium hypophosphite after ℃, stir and heat up to 80 ℃, then start to keep warm, continue stirring for 4 hours, and generate aluminum hypophosphite slurry. The aluminum hypophosphite slurry is press-filtered, dried and pulverized to obtain spherical aluminum hypophosphite with a particle size of 3.8 microns. The electron microscope photograph of this embodiment sees figure 1 .

Embodiment 2

[0022] Formula (parts by weight): sodium hypophosphite 100, aluminum sulfate octadecahydrate 120, water 250, melamine cyanurate 30, sodium dodecylbenzene sulfonate 1.8.

[0023] Preparation method: Weigh the raw materials according to the above parts by weight, first add water into the reaction vessel as a solvent, start stirring, add aluminum sulfate octadecahydrate and melamine cyanurate into the reaction kettle, and add sodium dodecylbenzenesulfonate at the same time, Stir evenly and heat up to 65°C, then add sodium hypophosphite, stir and heat up to 90°C, then start to keep warm, continue stirring for 4.5 hours to generate aluminum hypophosphite slurry. The aluminum hypophosphite slurry is press-filtered, dried and crushed to obtain spherical aluminum hypophosphite with a particle size of 4.7 microns. The electron microscope photograph of this embodiment sees figure 2 .

Embodiment 3

[0025] Formula (parts by weight): sodium hypophosphite 105, aluminum sulfate octadecahydrate 100, water 230, melamine cyanurate 40, citric acid 2.

[0026] Preparation method: Weigh the raw materials according to the above weight parts, first add water into the reaction vessel as a solvent, start stirring, add aluminum sulfate octadecahydrate and melamine cyanurate into the reaction kettle, add citric acid at the same time, stir evenly and heat up to 75°C Then add sodium hypophosphite, stir and heat up to 95°C, then start to keep warm, and continue to stir for 5 hours to generate aluminum hypophosphite slurry. The aluminum hypophosphite slurry is press-filtered, dried and crushed to obtain spherical aluminum hypophosphite with a particle size of 5.4 microns. The electron microscope photograph of this embodiment sees image 3 .

[0027] Comparative example (traditional preparation process)

[0028] First add 250 parts of water into the reaction vessel as a solvent, sta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of spherical aluminum hypophosphite. In the method disclosed by the invention, sodium hypophosphite reacts with aluminum sulfate; meanwhile, melamine cyanurate is added as a seed crystal in the earlier stage of reaction, and different dispersants are added to improve the dispersion effect. The spherical aluminum hypophosphite prepared by the method disclosed by the invention has the characteristics of small particle size, regular crystal form and the like, thus the drop of mechanical properties of plastics after the addition of a flame retardant is reduced. Meanwhile, by adopting the melamine cyanurate seed crystal as a synergist in the flame retardant, the flame retardance effect of aluminum hypophosphite after plastic addition is remarkably improved.

Description

technical field [0001] This product relates to a preparation method of a flame retardant, especially a preparation method of spherical aluminum hypophosphite. Background technique [0002] Aluminum hypophosphite is a phosphorus-containing flame retardant, which has the advantages of good thermal stability, low water solubility, and good flame retardant effect. When used in engineering plastics such as PA6 and PBT, the heat release rate and the heat generated during combustion are drastically reduced. , the amount of carbon formed after combustion increases, and the flame retardant performance reaches the V-0 level of UL94 standard. [0003] The synthesis of aluminum hypophosphite is relatively mature now. Patent 201210302490.1 discloses the preparation scheme of using sodium hypophosphite and aluminum sulfate to synthesize aluminum hypophosphite, but the aluminum hypophosphite prepared by this experimental scheme has disadvantages such as large particle size and irregular c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B25/36C09K21/04
Inventor 张旭毕燕杜庆田孙晓丽
Owner JINAN TAIXING FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More