Water-based inorganic resin and preparation method thereof

An inorganic resin, water-based technology, used in anti-corrosion coatings, alkali metal silicate coatings, coatings, etc., can solve the problems of poor water resistance of paint film, high cost of lithium silicate, insoluble in water, etc., to improve hardness, Excellent salt spray resistance and long-term corrosion resistance

Inactive Publication Date: 2014-02-26
WUXI HUHUANG PAINT
View PDF3 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Sodium silicate is easily soluble in water, and the water resistance of the paint film is poor; potassium silicate is soluble in water, and the price is moderate; lithium silicate is expensive, and it is not suitable for dissolving in water, and the concentration is low
Products obtained by simple mixing have poor stability, poor adhesion, or certain problems in water resistance and flexibility.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based inorganic resin and preparation method thereof
  • Water-based inorganic resin and preparation method thereof
  • Water-based inorganic resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Resin formula (by weight):

[0022]

[0023] (2) Preparation method:

[0024] Reserve 5.0wt% of the formula amount of deionized water for use, and add the rest of the deionized water into the dispersion kettle, start stirring at 600-800r / min, add potassium silicate, silica sol, and lithium silicate in the formula amount, and continue stirring ;Continue to stir for 5 minutes after the addition, then slowly add the coupling agent in the formula dropwise, drop it within 15-20 minutes, reduce the stirring speed, keep stirring at 400-500r / min for 2 hours, stop the machine, and stand still for 24 hours Above, under the condition of 400-500r / min, slowly add the emulsion in the formula, the reserved 5wt% deionized water and the additives and stabilizers in the formula, and keep stirring for 1 hour, and use a 150-mesh silk filter cloth Filtration, sampling and testing, packaging.

Embodiment 2

[0026] (1) Resin formula (by weight):

[0027]

[0028] (2) Preparation method:

[0029] Reserve 5.0wt% of the formula amount of deionized water for use, and add the rest of the deionized water into the dispersion kettle, start stirring at 600-800r / min, add potassium silicate, silica sol, and lithium silicate in the formula amount, and continue stirring ;Continue to stir for 5 minutes after the addition, then slowly add the coupling agent in the formula dropwise, drop it within 15-20 minutes, reduce the stirring speed, keep stirring at 400-500r / min for 2 hours, stop the machine, and stand still for 24 hours Above, under the condition of 400-500r / min, slowly add the emulsion in the formula, the reserved 5wt% deionized water and the additives and stabilizers in the formula, and keep stirring for 1 hour, and use a 150-mesh silk filter cloth Filtration, sampling and testing, packaging.

Embodiment 3

[0031] (1) Resin formula (by weight):

[0032]

[0033] (2) Preparation method:

[0034] Reserve 5.0wt% of the formula amount of deionized water for use, and add the rest of the deionized water into the dispersion kettle, start stirring at 600-800r / min, add potassium silicate, silica sol, and lithium silicate in the formula amount, and continue stirring ;Continue to stir for 5 minutes after the addition, then slowly add the coupling agent in the formula dropwise, drop it within 15-20 minutes, reduce the stirring speed, keep stirring at 400-500r / min for 2 hours, stop the machine, and stand still for 24 hours Above, under the condition of 400-500r / min, slowly add the emulsion in the formula, the reserved 5wt% deionized water and the additives and stabilizers in the formula, and keep stirring for 1 hour, and use a 150-mesh silk filter cloth Filtration, sampling and testing, packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Modulusaaaaaaaaaa
Proportionaaaaaaaaaa
Login to View More

Abstract

The invention discloses water-based inorganic resin and a preparation method thereof. The preparation method comprises the following steps: carrying out hydrolysis reaction on a formula amount of potassium silicate, silica sol and lithium silicate under the effect of a coupling agent, and after reaction is stable, adding elastic emulsion so as to adjust the flexibility, thus obtaining the water-based inorganic resin with excellent properties. The water-based inorganic resin prepared by the method is environment-friendly, odorless, non-toxic, non-ignitable and unexplosive, and has very excellent salt fog resistance, permanent corrosion resistance, high hardness, strong adhesive force and heat and humidity resistance, and therefore, the water-based inorganic resin has wide development space in numerous heavy corrosion protection fields and atmosphere and ocean steel structure heavy corrosion protection fields.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based inorganic resin and a preparation method thereof. Background technique [0002] In recent years, as people pay more and more attention to environmental protection, high-performance water-based product resins have been extensively researched and developed. [0003] The water-based inorganic resins currently researched and developed include silica sol sodium water glass, potassium sodium water glass, lithium water glass, or a mixture of several types. Sodium silicate is easily soluble in water, and the paint film has poor water resistance; potassium silicate is soluble in water, and the price is moderate; lithium silicate is expensive, and it is not suitable for water solubility, and the concentration is low. The products obtained by simple mixing have poor stability, poor adhesion, or certain problems in water resistance and flexibility. Contents of the invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/04C09D1/00C09D5/08
Inventor 牛清平廖文建胡胜初
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com