Core/shell type tetragonal titanium oxide particle water dispersion, making method, UV-shielding organic silicone coating composition and coated article

A tetragonal system, titanium oxide technology, applied in titanium compounds, chemical instruments and methods, coatings, etc., can solve the problem of unknown method of coating thickness and so on

Active Publication Date: 2014-02-12
SHIN ETSU CHEM IND CO LTD
View PDF15 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no method is known to control the thickness of the coating at a level precise enough to eliminate the crushing and sieving steps

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Core/shell type tetragonal titanium oxide particle water dispersion, making method, UV-shielding organic silicone coating composition and coated article
  • Core/shell type tetragonal titanium oxide particle water dispersion, making method, UV-shielding organic silicone coating composition and coated article
  • Core/shell type tetragonal titanium oxide particle water dispersion, making method, UV-shielding organic silicone coating composition and coated article

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0099] The second embodiment is a method for preparing an aqueous dispersion of core / shell tetragonal titanium oxide particles in which tin and manganese are solid-solution bound, the method comprising steps (A)-(D) described in detail below.

[0100] Step (A)

[0101] In step (A), an aqueous dispersion of tetragonal titanium oxide nanoparticles in which tin and manganese are bound in solid solution is firstly prepared. There is no particular limitation on the technique for preparing the aqueous dispersion. In a preferred procedure, starting materials including titanium compounds, tin compounds, manganese compounds, alkaline substances and hydrogen peroxide are reacted in an aqueous dispersion medium to form a solution of peroxytitanate containing tin and manganese, for which A hydrothermal reaction is carried out to obtain an aqueous dispersion of tetragonal titanium oxide nanoparticles in which tin and manganese are solid-solution bound.

[0102] The preceding stage of t...

Embodiment

[0197] Examples and comparative examples are given below by way of illustration and not limitation.

[0198] All parts are by weight unless otherwise indicated. The reactants were purchased from chemical suppliers including Wako Pure Chemical Industries, Ltd. (abbreviated as Wako) and Shin-Etsu Chemical Co., Ltd. (abbreviated as Shin-Etsu).

[0199] Preparation of Titanium Oxide Dispersion

Synthetic example 1

[0201] Preparation of titanium oxide dispersion (i) (relative to 100 mol% titanium, 4 mol% tin and 0.5 mol% manganese)

[0202] To 66.0 g of a 36% by weight titanium (IV) chloride aqueous solution (TC-36 manufactured by Ishihara Sangyo Kaisha, Ltd.) were added 1.8 g of tin (IV) chloride pentahydrate (Wako) and 0.12 g of chlorine Manganese(II) tetrahydrate (Wako). They were mixed well and diluted with 1,000 g of deionized water. To this metal salt aqueous solution mixture, 300 g of 5% by weight ammonia water (Wako) was gradually added to neutralize and hydrolyze to obtain a precipitate of titanium hydroxide containing tin and manganese. The titanium hydroxide slurry was pH 8. The precipitate of titanium hydroxide was deionized by repeated addition of deionized water and decantation. To the deionized titanium hydroxide precipitate containing tin and manganese, 100 g of 30% by weight aqueous hydrogen peroxide (Wako) was gradually added, and stirring was continued at 60° C. for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

Core / shell type tetragonal titanium oxide particles consisting of a nanosized core of tetragonal titanium oxide having tin and manganese incorporated in solid solution and a shell of silicon oxide around the core are dispersed in an aqueous dispersing medium. The cores and the core / shell type titanium oxide particles have an average particle size of @30 nm and @50 nm, respectively. The amount of tin or manganese in solid solution is to provide a molar ratio Ti / Sn or Ti / Mn between 10 and 1,000.

Description

technical field [0001] The present invention relates to an aqueous dispersion of core / shell tetragonal titanium oxide particles, a method for preparing the aqueous dispersion, an ultraviolet-shielding silicone coating composition comprising the aqueous dispersion, and articles coated with the composition. More specifically, it relates to an aqueous dispersion of core / shell type tetragonal titanium oxide particles consisting of a nano-sized core of tetragonal titanium oxide incorporating tin and manganese in solid solution and a shell of silicon oxide; pulverization is not required A method for preparing the aqueous dispersion capable of controlling the thickness of the silica shells with a sieving step; an ultraviolet-shielding silicone coating composition or hardcoat composition comprising the aqueous dispersion, It is capable of forming a cured film satisfying weather resistance and ultraviolet shielding ability and having transparency, scratch resistance and adhesiveness wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12C09D183/04C08J7/04C01G23/00C08J7/043C08J7/046
CPCC01G23/002C01P2002/84C09C1/3684G02B1/105C01P2002/72C01P2004/84C01P2004/64C01P2002/52B82Y30/00C08J7/042C08J2443/04C08J2483/04Y10T428/256C01G23/003C08J7/043C08J7/046C09D183/00C01G23/00G02B1/14
Inventor 增田幸平樋口浩一小森久敏古馆学井上友博荣口吉次
Owner SHIN ETSU CHEM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com