Composite floor paint, preparation method thereof and using method thereof

A floor coating and coating technology, applied in the field of floor coatings, can solve the problems of poor durability, easy pulverization, and easy yellowing, and achieve low volatile organic compound release, good anti-skid and wear resistance, and reduced hazards Effect

Active Publication Date: 2014-01-22
深圳市威尔地坪材料有限公司
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-slip epoxy floor generally uses aggregates such as coarse-grained quartz sand, and then roll-coats a layer of epoxy topcoat on the aggregate layer. The wear of the tires is relatively large, and there will be a large friction sound when the car is running, and this coating is difficult to clean
In addition, because the outdoor durability of epoxy floor coating is poor, it is easy to yellow and powder, so epoxy floor coating is only suitable for indoor use
At present, the polyurethane floor coating used in outdoor parking lots contains a large amount of organic solvents, which will release a large amount of volatile organic compounds during the construction process, which is poor in environmental protection and is not conducive to the health of construction workers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite floor paint, preparation method thereof and using method thereof
  • Composite floor paint, preparation method thereof and using method thereof
  • Composite floor paint, preparation method thereof and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The raw material ratio of epoxy primer, leveling coat, solvent-free epoxy self-leveling paint and polyurethane topcoat is shown in Table 1.

[0037] The raw material ratio of each coating coating in the embodiment 1 of table 1

[0038]

[0039]

[0040] Preparation of epoxy primer: Mix low molecular weight bisphenol A liquid epoxy resin, low molecular weight bisphenol F type liquid epoxy resin and reactive diluent at a speed of 300-500r / min for 10-20min and mix evenly, filter and packed B 4 Components, the solvent-free modified alicyclic amine curing agent is packaged independently to get A 4 components. During construction, put A 4 Component and B 4 The components are mixed and stirred evenly to obtain a solvent-free epoxy primer.

[0041] Preparation of leveling layer coating: Mix low molecular weight bisphenol A type liquid epoxy resin, low molecular weight bisphenol F type liquid epoxy resin and reactive diluent at a speed of 300-500r / min for 10-20min and...

Embodiment 2

[0049] The ratio of raw materials for epoxy primer, leveling coat, solvent-free epoxy self-leveling paint and polyurethane topcoat is shown in Table 2.

[0050] The raw material ratio of each coating coating in table 2 embodiment 2

[0051]

[0052] The preparation methods of the epoxy primer, leveling coating, solvent-free epoxy self-leveling paint and polyurethane topcoat of this embodiment are the same as those described in Example 1.

[0053] The use method of the composite floor coating of this embodiment is basically the same as that described in Example 1, the difference is: the amount of leveling layer paint is 0.5kg / ㎡; the amount of solvent-free epoxy self-leveling paint is 1.5 kg / ㎡, the amount of polyurethane topcoat is 0.15kg / ㎡.

[0054] The performance of the composite floor composed of primer, leveling layer, solvent-free epoxy self-leveling paint layer and polyurethane topcoat layer is shown in Table 4.

Embodiment 3

[0056] The raw material ratio of epoxy primer, leveling coat, solvent-free epoxy self-leveling paint and polyurethane topcoat is shown in Table 3.

[0057] The raw material ratio of each coating coating in table 3 embodiment 3

[0058]

[0059]

[0060] The preparation methods of the epoxy primer, leveling coating, solvent-free epoxy self-leveling paint and polyurethane topcoat of this embodiment are the same as those described in Example 1.

[0061] The use method of the composite floor coating of this embodiment is basically the same as that described in Example 1, the difference is: the amount of leveling layer paint is 0.3kg / ㎡; the amount of solvent-free epoxy self-leveling paint is 1.8 kg / ㎡, the amount of polyurethane topcoat is 0.13kg / ㎡.

[0062] The performance of the composite floor composed of primer, leveling layer, solvent-free epoxy self-leveling paint layer and polyurethane topcoat layer is shown in Table 4.

[0063] Table 4 The performance test data of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of floor paint, and particularly relates to composite floor paint, a preparation method thereof and a using method thereof. The composite floor paint comprises an epoxy primer, leveling blanket paint and surface coating paint. The surface coating paint comprises solvent-free epoxy self-leveling surface paint and polyurethane finish paint. When construction is performed, the epoxy primer, the leveling blanket paint, the solvent-free epoxy self-leveling surface paint and the polyurethane finish paint are painted in order on a pretreated floor. The composite floor paint has a low content of volatile organic compounds, and is suitable for indoor or outdoor floor decorative painting. A composite floor manufactured by the composite floor paint is antiskid, wear resistant, acid and alkali resistant and weather-proof, and is high in hardness, high in bonding strength with a floor base surface.

Description

technical field [0001] The invention relates to the technical field of floor coatings, in particular to a composite floor coating and a preparation method and application method thereof. Background technique [0002] Floor coatings are mainly used in building floor decoration in industrial plants, warehouses, parking lots, shopping malls, sports fields, schools, hospitals and offices. Floor coatings can be divided into epoxy floor coatings, polyurethane floor coatings, vinyl floor coatings, and acrylic floor coatings. [0003] Indoor parking lots often use epoxy floor coatings to coat the building ground of the parking lot, while outdoor parking lots usually use polyurethane coatings to coat the building ground of the parking lot. The floor coating of the driving area and the parking area of ​​the indoor parking lot are different. The parking area is a smooth epoxy floor coating, and the driving area is a non-slip epoxy floor coating. The smooth epoxy floor coating is easy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D175/04C09D7/12E04F15/12B05D7/24
Inventor 李涌钢王刚伟刘槐清洪海诗
Owner 深圳市威尔地坪材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More