Environment-friendly ultraviolet light resistant and high-temperature resistant paint for outer walls of buildings

A high-temperature resistant coating and anti-ultraviolet technology, applied in the field of high-temperature resistant coatings and anti-ultraviolet rays for the exterior walls of environmentally friendly buildings, can solve the problems of changes in heat reflection and heat insulation properties, unstable chemical properties, and difficulty in long-term storage, and achieves the goal of making The method is simple, the equipment is simple, and the fluidity is good.

Inactive Publication Date: 2015-07-01
SUZHOU XIANGYUAN SPEICAL FINE CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional reflective insulation materials have certain toxicity, and are not stable in chemical properties, not easy to store for a long time, and the heat reflective insulation performance changes with time and environmental changes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An environment-friendly anti-ultraviolet and high-temperature-resistant coating for exterior walls of buildings, which is composed of component A, component B and component C, and each component is composed of the following substances and contents by weight: 25-35 parts of particic acid ester resin, 20 parts of aromatic mixed solvent, 8-10 parts of nano-scale ceramic powder, 2-4 parts of mica powder, 10-18 parts of diacetone alcohol, 3-8 parts of ethylene glycol monobutyl ether 7-11 parts of 2% by mass cellulose thickener solution, 1.0-1.4 parts of 10% by mass polyphosphate dispersant solution, 1-3 parts of emulsifier, 0.1-0.3 parts of sodium hydroxide , ethanol: 30-50 parts, deionized water: 70-100 parts, titanium dioxide: 140-180 parts; component B contains the following substances and contents in parts by weight: coating curing agent: 3-5 parts , Initiator 0.02~1 part; Dispersant 1; Leveling agent 0.6; Defoamer 0.3; Antifungal agent: 5 ~ 3 parts; Component C is an e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Environment-friendly ultraviolet light resistant and high-temperature resistant paint for outer walls of buildings comprises A compositions, B compositions and a C composition, wherein the A compositions comprise the following substances in parts by weight: 25-35 parts of polyaspartic acid ester resin, 20 parts of an aromatics mixed solvent, 8-10 parts of nano-scale ceramic powder, 2-4 parts of mica powder, 10-18 parts of diacetone alcohol, 3-8 parts of ethylene glycol monobutyl ether, 7-11 parts of a cellulose thickener solution with the mass percent of 2%, 1.0-1.4 parts of a polyphosphate dispersing agent solution with the mass percent of 10%, 1-3 parts of an emulgator, 0.1-0.3 part of sodium hydroxide, 30-50 parts of ethyl alcohol, 70-100 parts of deionized water, 140-180 parts of titanium dioxide; the B compositions comprise the following substances in parts by weight: 3-5 parts of a paint curing agent, 0.02-1 part of an initiator, 1 part of a dispersing agent, 0.6 part of a flatting agent, 0.3 part of an antifoaming agent, 0.3 part of a defoaming agent, 25 parts of a modified ammonia curing agent, 2-4 parts of tetrachloroisophthalonitrile, 3-5 parts of a dry film antiseptic; the C composition is an environment-friendly color mixed-phase inorganic pigment.

Description

technical field [0001] The invention relates to a novel anti-corrosion coating and a preparation method thereof, more specifically, to an anti-ultraviolet and high-temperature-resistant coating for the exterior wall of an environment-friendly building. Background technique [0002] In the prior art, most commonly used building exterior wall coatings are coatings prepared with styrene-acrylic emulsions, pure acrylic emulsions or elastic acrylic emulsions as base materials. Its disadvantages are small cracks after being applied to the wall, poor strength, poor stain resistance and low temperature performance; in addition, due to the presence of styrene in the coating, the smell is quite strong; when the exterior wall is coated, a large amount of smell is emitted in the atmosphere. In addition, the curing time of this type of coating is relatively long. Therefore, it is necessary to pay attention to weather changes when coating, and it cannot be constructed during the continuou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/18
Inventor 周建颜玉荣
Owner SUZHOU XIANGYUAN SPEICAL FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products