Pretreatment process for combed polyester cotton bleached cloth

A technology, polyester cotton technology, applied in the field of dyeing and finishing processing, can solve the problems of lack, dullness, thinness, etc., and achieve the effect of improving whiteness, increasing desizing rate, and less damage to strength

Inactive Publication Date: 2013-12-11
如皋市五山漂染有限责任公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, polyester-cotton fabrics will appear thin, dull, lack of plumpness, fluffy and hairy style after being processed by long-carrying conventional processes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] 1) J T / C 65 / 35 is singed on the gas singeing machine, the cloth body temperature is 170°C, and the cloth is dropped after singeing, and the cloth body temperature is 45°C;

[0015] 2) For desizing with amylase, add 2000L 4g of amylase, 3g of NaCl, 3.5g of penetrant per liter of water, keep the temperature of the chemical tank at 50°C, and stack for 12 hours;

[0016] 3) The bleach solution is 0.3 parts of potassium borate; 1 part of diethylenetriaminepentamethylene phosphonic acid; 1.5 parts of acrylic acid maleic acid copolymer; 0.8 parts of 1,5-anhydrous glucitol; 1.5 parts of caprolactam activator; 0.6 parts of acetylethylenediamine; 7 parts of sodium hydroxide; 5 parts of hydrogen peroxide; 1000 parts of water, padding and bleaching solution, the temperature is 30 ° C, steamed for 60 seconds, rinsed and washed;

[0017] 4) The fabric is mercerized in sodium hydroxide solution, and the concentration of sodium hydroxide solution is 220g / L;

[0018] 5) The fabric afte...

Embodiment 2

[0020] 1) J T / C 60 / 40 is singed on the gas singeing machine, the cloth body temperature is 175°C, and the cloth is dropped after singeing, and the cloth body temperature is 45°C;

[0021] 2) For desizing with amylase, add 2000L 5g of amylase, 4g of NaCl, 3.5g of penetrant per liter of water, keep the temperature of the chemical tank at 50°C, and stack for 12 hours;

[0022] 3) The bleach solution is 0.3 parts of potassium borate; 1 part of diethylenetriaminepentamethylene phosphonic acid; 1.8 parts of acrylic acid maleic acid copolymer; 0.8 parts of 1,5-anhydrous glucitol; 2 parts of caprolactam activator; 0.7 parts of acetylethylenediamine; 6 parts of sodium hydroxide; 6 parts of hydrogen peroxide; 1000 parts of water, padding and bleaching solution, the temperature is 30 ° C, steamed for 60 seconds, rinsed and washed;

[0023] 4) The fabric is mercerized in sodium hydroxide solution, and the concentration of sodium hydroxide solution is 230g / L;

[0024] 5) The mercerized fa...

Embodiment 3

[0026] 1) Gross effect test

[0027] Dye preparation of the test solution: Weigh 1g of reactive red BF-3B dye and fully dissolve it in hot water at 95°C and dilute it to 100cc as a 1% solution.

[0028] Cut the pre-treated test cloth sample into strips of 20cm in the warp direction and 2cm in the weft direction, draw a parallel line with a pencil along the weft direction at a distance of 1cm from one end, and fix the other end of the sample on a horizontal frame for use. It hangs vertically, and the lower end is immersed in the container containing the dye solution, so that the liquid level is exactly aligned with the pencil line. The dye solution rises higher along the warp direction within 10 minutes of measurement, indicating capillary effect.

[0029] 2) Whiteness test

[0030] Measure the whiteness of the pre-treated test cloth samples with computer spectrophotometer CFS57CA, measure the data at three different places of each fabric, and then take the average value, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a pretreatment process for combed polyester cotton bleached cloth. The pretreatment process comprises the procedures of singeing, desizing, bleaching, mercerizing and heat-shaping, wherein during desizing, the enzyme-desizing cold-dwelling process that desizing anzyme and a penetrant are added into the desizing procedure is adopted; in the bleaching procedure, the following materials are adopted: 0.2-0.4 part of potassium borate serves as the bleaching liquor, 0.8-1.2 part(s) of diethylenetriaminepenta acid (DTPMP), 0.8-2 part(s) of acrylic acid maleic acid copolymer, 0.5-1 part of 1, 5-anhydrous glucitol, 1-2 part(s) of caprolactam activator, 0.4-0.7 part of tetraacetylethylenediamine (TAED), 3-8 parts of sodium hydroxide, 3-7 parts of hydrogen peroxide and 900-1000 parts of water. When the pretreatment process is used for processing fabrics, prominent damage to the fabrics is small; as enzyme desizing is adopted, the desizing ration is improved; the bleaching liquor adopted in the bleaching procedure can effectively improve the whitenness of the fabrics; meanwhile, the pretreatment cost is lowered.

Description

technical field [0001] The invention relates to a fabric processing method, in particular to a pretreatment process of combed polyester-cotton bleached cloth, belonging to the technical field of dyeing and finishing. Background technique [0002] Polyester-cotton blended fabric is made of polyester fiber and cotton fiber in a certain proportion. It not only has the advantages of good wrinkle resistance, crispness, elegance, easy drying after washing, no mildew and no moth, etc., but also soft cotton fabric. , air permeability, good moisture absorption, not easy to pilling and other properties, comfortable to wear, economical and affordable, can meet the needs of different consumption levels. The physical and chemical properties of polyester fiber and cotton fiber are different. During dyeing and finishing, both should be considered. When the fiber blending ratio is different, there should be corresponding processes. At present, polyester-cotton fabrics will appear thin, dul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06L1/14D06M16/00D06L3/02D06M11/38D06B7/08D06C7/02D06M101/32D06M101/06D06L4/12D06L4/13
Inventor 戴建
Owner 如皋市五山漂染有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com