Nano-silver honeycomb type purification activated carbon and preparation method thereof

A technology for the preparation of activated carbon and nano-silver, which is applied in chemical instruments and methods, inorganic chemistry, alkali metal compounds, etc., can solve the problems of inaccessibility, lack of activated carbon, and reduced adsorption effect, etc., and achieve good inhibition and killing effects, method Simple and feasible, the effect of improving the adsorption and desorption speed

Active Publication Date: 2015-12-23
台州绿之源环保股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Activated carbon is used in the industrial field for decolorization, refining, and purification of liquid phase adsorption. In terms of gas phase adsorption, powdered and granular activated carbon cannot be in close contact with toxic and harmful substances in the air, thus greatly reducing the adsorption effect.
[0004] On the other hand, the current activated carbon application technology lacks the ability to ensure that activated carbon has a good function of absorbing dirt and has a good killing effect on microorganisms that make people sick, especially the lack of activated carbon used in hospitals and other environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: The weight ratio of the raw materials used is: 35 parts of chemical activated carbon, 27 parts of coal-based granular activated carbon, 40 parts of coconut shell activated carbon; three kinds of activated carbons with different proportions are put into a ball mill for ball milling, and ground into The mesh number is 500 mesh activated carbon powder. Get 102 parts of activated carbon powders that are ground into, 5 parts of nano-silver with a purity of 99%, 1.5 parts of methyl cellulose, and 1.5 parts of talcum powder. Add the above-mentioned raw materials into the mixer in turn, stir and mix evenly to make a mixture. Then put the mixture in a kneader (or mixer), add moderate distilled water, knead for 30 minutes, and knead it into a mud paste in the kneader. Then the mud paste is placed in a vacuum mud mill, and mud is honed into a uniform plasticized mud paste in the vacuum mud mill. Then put the plasticized mud paste in the extrusion molding, and extru...

Embodiment 2

[0028] Embodiment 2: The weight ratio of the raw materials used is: 32 parts of chemical activated carbon, 30 parts of coal-based granular activated carbon, 38 parts of coconut shell activated carbon, three kinds of activated carbons with different proportions are put into the ball mill for ball milling, and ground into The mesh number is 500 mesh activated carbon powder. Then get the activated carbon powder that is ground into, 6 parts of nano-silver with a purity of 99%, 2 parts of methylcellulose, and 2 parts of talcum powder. The above-mentioned raw materials are sequentially added to stirring and mixing, stirring evenly to make a mixture. The rest of the steps are the same as in Example 1, wherein the profile with a moisture content of less than 10% is placed in a furnace for sintering at a sintering temperature of 900° C. for 5 hours.

[0029] The performance of the nano-silver honeycomb type purified activated carbon product: iodine adsorption value 1100-1200mg / g, benz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
iodine adsorption valueaaaaaaaaaa
iodine adsorption valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to nano-silver honeycomb-type purification activated carbon and a preparation method thereof. The nano-silver honeycomb-type purification activated carbon uses the following raw materials in part by weight: 32 to 38 parts of chemical activated carbon, 25 to 30 parts of granular activated carbon from coal, 35 to 42 parts of cocoanut active charcoal, 4 to 6 parts of nano-silver with purity of 99 percent, 1 to 2 parts of methylcellulose and 1 to 2 parts of talcum powder. The method comprises the following steps: carrying out ball milling, mixing the raw materials with uniformly stirring to obtain a product material; carrying out vacuum pugging, extrusion forming, air-drying and sintering to obtain the nano-silver honeycomb-type purification activated carbon. According to the invention, the activated carbon can be guaranteed to have an excellent dirt adsorption function, also can have an excellent effect of killing and inhibiting microorganisms which are pathogenic for people, is suitable for the environment such as a hospital and the like, and also has the advantages of firmness for sizing, durability, simple and practicable method, low pollution control cost, low carbon, energy saving and good treatment effect.

Description

technical field [0001] The invention belongs to a nano-silver honeycomb type purification activated carbon and a preparation method thereof. Background technique [0002] Activated carbon is widely used in various aspects of industrial and agricultural production, such as alkali-free deodorization (refined mercaptan removal), ethylene desalted water (refined packing), catalyst carrier (palladium, platinum, rhodium, etc.), water purification and sewage treatment in the petrochemical industry; Water quality treatment and protection of power plants in the industry; decolorization and refining of chemical catalysts and carriers, gas purification, solvent recovery, and oils in the chemical industry; refining and decolorization of beverages, alcohol, monosodium glutamate mother liquor and food in the food industry; gold in the gold industry Extraction, recovery of tail liquid; sewage treatment, waste gas and harmful gas treatment, gas purification in environmental protection indus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/28B01J20/30
Inventor 刘大敏季小恩颜海军
Owner 台州绿之源环保股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com