Production technology of super stain-resistant waterborne compound coating

A production process and composite coating technology, which is applied in the direction of coating, etc., can solve the problems of affecting the urban appearance, affecting the appearance of the building, and the structure is not compact, and achieves the effects of small water absorption, improved economic benefits, and good stain resistance

Inactive Publication Date: 2013-10-09
仪征市通发建筑养护材料厂
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the exterior walls of buildings are decorated with coatings. The current coating film structure is not dense, the water repellency is poor, and the antifouling property is poor. to have a certain impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production technology of super stain-resistant waterborne compound coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] 1. Preparation:

[0015] rutile nano-TiO 2 Process it until the average particle size is 80nm, and then use it.

[0016] Weigh 12kg of styrene-acrylic emulsion, 2.6kg~3.0kg of nano-TiO 2 , 2.2 kg SiO 2 , 0.5 kg inorganic antibacterial and antifungal agent, 1.2 kg negative ion generating powder, 0.2 kg cellulose, 2.9 kg AS881 superfine aluminum silicate, 40 kg filler, 0.8kg film-forming aid, 0.6kg dispersant, 0.4kg thickener , 0.5kg stain resistance agent and 0.7kg viscosity stabilizer.

[0017] The raw material inorganic antibacterial antifungal agent contains Ag + and Cu 2+ , Ag + Accounting for 2.8% of the mass of inorganic antibacterial and antifungal agents, Cu 2+ It accounts for 1.7% of the mass of inorganic antibacterial and antifungal agents.

[0018] 2. Processing technology:

[0019] First, the styrene-acrylic emulsion, additives (composed of film-forming additives, dispersants, thickeners, stain-resistant agents and viscosity stabilizers), nano-TiO 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production technology of a super stain-resistant waterborne compound coating, and relates to the technical field of production of a coating for a building wall. The production technology comprises the following steps: firstly, mixing and grinding styrene-acrylic emulsion, an assistant, nano TiO2, SiO2, negative ion powder, cellulose and water; adding a part of AS881 ultra-fine aluminum silicate; adding an inorganic antibacterial and anti-enzyme agent after grinding; adding a filler and another part of AS881 ultra-fine aluminum silicate after mixing; and evenly mixing to form the waterborne compound coating. By adopting the production technology, the problems of unsound coating structure and poor hydrophobicity of the coating structure are avoided; the puzzle of poor stain resistance of the coating is solved; the production technology also has the characteristics of being good in resistance to washing, small in hygroscopicity and good in stain resistance; the coating cost is reduced; the super stain-resistant waterborne compound coating is the coating for inner and outer walls of a building, which is good in super stain resistance, crazing resistance and hydrophobicity, good in ceramic imitating property, and high in hiding rate.

Description

technical field [0001] The invention relates to the technical field of production of coatings for building walls. Background technique [0002] Most of the exterior walls of buildings are decorated with coatings. The current coating film structure is not dense, the water repellency is poor, and the antifouling property is poor. To have a certain impact. Contents of the invention [0003] The object of the invention is to propose a production process of a super-stain-resistant and water-resistant composite coating that is not easily polluted. [0004] In the present invention, styrene-acrylic emulsion, additives, nano-TiO 2 , SiO 2 , Negative ion generating powder, cellulose and water are mixed and ground, then add part of AS881 superfine aluminum silicate, after grinding, add inorganic antibacterial and antifungal agent, after mixing, add filler and another part of AS881 superfine aluminum silicate, mix well , Serve. [0005] Nano-TiO with shielding, absorption and sc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D7/12C09D5/00
Inventor 徐贵才
Owner 仪征市通发建筑养护材料厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products