In-bath crease-resisting agent used in polyester fiber fabric, and preparation method thereof

A technology of polyester fiber and anti-wrinkle agent, which is applied in the field of anti-wrinkle agent in a bath for polyester fiber fabric and its preparation, can solve the problems of fluffy softness, inability to improve antistatic performance, complicated production process, and stiff fabric feel. , to achieve good antistatic properties and hydrophilic properties, excellent comfort, and improve the effect of anti-wrinkle effect

Active Publication Date: 2013-09-25
DUPLUS CHEM OF ZHANGJIAGANG CITY
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, existing anti-wrinkle agents such as polyacrylamide usually only have an anti-wrinkle effect. Using common anti-wrinkle agents as anti-wrinkle agents for polyester fabrics will make the fabric feel stiff after dyeing, and properties such as fluffy softness and antistatic properties cannot be improved. , but must be completed through further finishing, making the production process complicated and costly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • In-bath crease-resisting agent used in polyester fiber fabric, and preparation method thereof
  • In-bath crease-resisting agent used in polyester fiber fabric, and preparation method thereof
  • In-bath crease-resisting agent used in polyester fiber fabric, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of anti-wrinkle agent in bath for polyester fiber fabric, it is prepared by following steps:

[0023] (1) Weigh 800 grams of polyethylene glycol (PEG4000), 150 grams of ethylene glycol, 125 grams of dihydroxypolyether, 140 grams of dimethyl terephthalate, and 150 grams of amino-terminated double-header silicone, 50g of 3-piperazinepropylmethyldimethoxysilane, 10g of magnesium acetate;

[0024] (2) Put the above materials into the reaction kettle, raise the temperature to 140°C and keep it for 180 minutes, then continue to raise the temperature to 220°C and keep it for 60 minutes. Then carry out polymerization at a vacuum degree of -0.08MPa and a temperature of 240°C to form a polyester polyether silicone oil block copolymer, and discharge after cooling down to 190°C;

[0025] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), sorbitan monostearate and water in a weight ratio of 2:2:96 to obtain the polyester fiber fabric bath Ant...

Embodiment 2

[0027] A kind of anti-wrinkle agent in bath for polyester fiber fabric, it is prepared by following steps:

[0028] (1) Weigh 900 grams of polyethylene glycol (PEG2000), 140 grams of ethylene glycol, 140 grams of dihydroxypolyether, 165 grams of dimethyl terephthalate, and 180 grams of amino-terminated double-header silicone, 3-piperazinepropylmethyldimethoxysilane 60g, zinc acetate 6g;

[0029] (2) Put the above materials into the reaction kettle, raise the temperature to 150°C and keep it for 180 minutes, then continue to raise the temperature to 230°C and keep it for 60 minutes. Then carry out polymerization, carry out polymerization at a vacuum degree of -0.08MPa, and a temperature of 260°C to generate a polyester polyether silicone oil block copolymer, and discharge after cooling down to 200°C;

[0030] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), sorbitan monostearate and water in a weight ratio of 3:2:95 to obtain the polyester fib...

Embodiment 3

[0032] A kind of anti-wrinkle agent in bath for polyester fiber fabric, it is prepared by following steps:

[0033] (1) Weigh 700 grams of polyethylene glycol (PEG2000), 125 grams of ethylene glycol, 125 grams of dihydroxypolyether, 130 grams of dimethyl terephthalate, and 150 grams of amino-terminated double-header silicone, 50 grams of 3-piperazinepropylmethyldimethoxysilane, 10 grams of calcium acetate;

[0034] (2) Put the above materials into the reaction kettle, raise the temperature to 170°C and keep it for 180 minutes, continue to raise the temperature to 220°C and keep it for 60 minutes, then carry out polymerization at a vacuum degree of -0.09MPa and a temperature of 250°C to form Polyester polyether silicone oil block copolymer, discharge after cooling down to 200°C;

[0035] (3) Mix the polyester polyether silicone oil block copolymer obtained in step (2), sorbitan monostearate and water in a weight ratio of 5:3:92 to obtain the polyester fiber fabric bath Anti-w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an in-bath crease-resisting agent used in polyester fiber fabric, and a preparation method thereof. The agent comprises the following components, by weight: 2-5% of a polyester-polyether-silicon oil block copolymer, 1-5% of sorbitan monostearate, and balance of water. The polyester-polyether-silicon oil block copolymer is prepared from the raw materials of, by weight: 120-160 parts of polyethylene glycol, 18-30 parts of glycol, 15-25 parts of dihydroxy polyether, 20-28 parts of dimethyl terephthalate, 10-30 parts of an amino-terminated double-head sealant organosilicon, 5-10 parts of 3-piperazine propyl dimethoxysilane, and 0.2-2 parts of metal acetate. With the in-bath crease-resisting agent provided by the invention, good crease-resisting effect of the polyester fiber fabric is provided, and excellent fluffy and soft texture, good antistatic property, and good hydrophilic smoothness are provided with dyed polyester fiber fabric. Dyed polyester fiber or fabric thereof can be provided with excellent comfortableness without other finishing.

Description

technical field [0001] The invention relates to an in-bath anti-wrinkle agent, in particular to an in-bath anti-wrinkle agent for polyester fabrics and a preparation method thereof. Background technique [0002] As we all know, polyester fiber has poor fluffy softness, moisture absorption and perspiration, antistatic performance and easy decontamination performance. Therefore, the textiles processed with polyester fibers have poor wearability, are easy to stick to dirt, and are prone to static electricity. This will undoubtedly cause certain harm to human health. In order to overcome the shortcomings of polyester fiber and to meet the increasingly high requirements of the market for textiles, polyester fiber must be finished in order to improve its performance. [0003] It is also known that in the dyeing process of polyester fiber fabrics, in order to avoid wrinkles in the dyeing and post-treatment process of the fabric and effectively prevent wrinkles, an anti-wrinkle ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/647D06M13/224C08G77/46D06M101/32
Inventor 陈金辉吴玉春方玉琦王宇飞陈秋坤
Owner DUPLUS CHEM OF ZHANGJIAGANG CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com