Cement compound type grinding aid

A compound type and grinding aid technology, applied in the fields of cement compound grinding aid and building materials chemical products, can solve the problems of deteriorating production environment, insignificant grinding aid effect, and high cost of grinding aid, so as to reduce production costs and improve Grinding efficiency, the effect of optimizing cement properties

Active Publication Date: 2013-09-11
湖南润攸科技发展有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solution to this situation is usually to add cement grinding aids. Most of the commercially available liquid grinding aids are composed of pure chemical substances such as triethanolamine and industrial waste. The cost of grinding aids is very high, and it is easy to Flying dust will worsen the production environment, and the grinding aid effect is not obvious, which will affect the performance of cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: The component weight percent of the cement composite grinding aid is 15% of modified triethanolamine, 10% of triethanolamine, 22% of triisopropanolamine, 15% of glycerin, 10% of sodium humate, low molecular weight Fatty salt 1% and clean water 27%.

[0014] After the cement compound grinding aid produced based on this component ratio is added to the material, the strength of the cement is significantly enhanced, the energy consumption is reduced, and the grinding output of the ball mill is increased by more than 15%.

Embodiment 2

[0015] Embodiment 2: The component weight percent of the cement composite grinding aid is 17% of modified triethanolamine, 13% of triethanolamine, 25% of triisopropanolamine, 10% of glycerin, 12% of sodium humate, low molecular weight Fatty salt 1% and clean water 22%.

[0016] After the cement compound grinding aid produced based on this component ratio is added to the material, the strength of the cement is significantly enhanced, the energy consumption is reduced, and the grinding output of the ball mill is increased by 12-15%.

[0017] The cement composite grinding aid of the present invention, its principle is to utilize the performance of its various component raw materials, the adsorption on the surface of solid particles changes the structural properties of the particle surface, reduces the structural properties of the particle surface, reduces the It improves the strength and hardness of the particles, prevents the closure of new cracks, and accelerates the expansion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a cement compound type grinding aid which is high-efficient cement grinding aid integrating grinding and enhancement. The cement compound type grinding aid comprises the following compositions in percentage by weight: 10-20% of modified triethanolamine, 10-15% of triethanolamine, 20-30% of triisopropanolamine, 10-15% of glycerinum, 10-15% of sodium humate, 1% of low-molecular-weight fatty salt and 20-30% of clean water. According to the cement compound type grinding aid, the grinding efficiency of a cement grinding technology and the purification of the working environment in a manufacturing shop can be effectively improved, and the cement compound type grinding aid has the characteristics of lowering the production cost and effectively optimizing the properties of cement.

Description

technical field [0001] The invention relates to building material chemical products, in particular to a cement composite grinding aid, in particular to a high-efficiency cement grinding aid integrating grinding aid and reinforcement. Background technique [0002] Cement is one of the most commonly used building materials and is widely used in civil engineering, hydraulic, national defense and other projects. During the processing of cement, it needs to be ground into powder with a mill. According to the existing cement grinding process, the mill Over-grinding often occurs in the warehouse, resulting in electrostatic adsorption, and the temperature of the clinker entering the mill is extremely high, even reaching 190 degrees. The solution to this situation is usually to add cement grinding aids. Most of the commercially available liquid grinding aids are composed of pure chemical substances such as triethanolamine and industrial waste. The cost of grinding aids is very high a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/12C04B103/52
Inventor 唐智荣
Owner 湖南润攸科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap