Aqueous zinc stearate dispersion liquid and preparation method thereof

A water-based dispersion liquid and zinc stearate technology, which is applied in textiles and papermaking, fiber raw material processing, non-fiber pulp addition, etc., can solve the problems of increasing the economic burden of production enterprises, high production costs, and energy consumption, and achieve benefits Industrial application, easy operation, and the effect of reducing production costs

Active Publication Date: 2013-08-28
肇庆市至立自动化科技有限公司
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method is simple, the prepared water-based zinc stearate dispersion has fine particle size and high solid content, but it needs to be heated to raise the temperature, consumes a lot of energy, and the production cost is relatively high, which increases the economic burden of the production enterprise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Add 59kg of deionized water into the reactor, add 1kg of sodium tripolyphosphate, 2kg of Tween 80, 2kg of Span 80 and 35kg of zinc stearate under stirring at a stirring speed of 2000 r / min, and then use a pipeline shear Stir at a high speed of 8000r / min for 20 minutes to completely emulsify and disperse the materials in the reactor; then add 0.1kg of polydimethylsiloxane defoamer and 0.1kg of Kayson preservative, and stir mechanically for 10 minutes The resulting mixture is input into a horizontal sand mill and ground for 10 minutes, and then filtered through a 1000-mesh ultrasonic vibrating sieve to obtain a zinc stearate aqueous solution with a viscosity of 50mPa S, an average particle size of 2.6 μm, and a solid content of 38wt%. Dispersions.

Embodiment 2

[0029] Add 57kg of deionized water in the reactor, add 1kg of sodium pyrophosphate, 5kg of sodium lauryl sulfate and 36kg of zinc stearate under stirring at a stirring speed of 2000 r / min, and then use a pipeline shear to 8500r / min Stir at a stirring speed of min for 30 minutes at high speed to completely emulsify and disperse the materials in the reactor; The mixture was input into a horizontal sand mill and ground for 12 minutes, and then filtered through a 1000-mesh ultrasonic vibrating sieve to obtain a zinc stearate aqueous dispersion with a viscosity of 62mPa·S, an average particle size of 3 μm, and a solid content of 40wt%.

Embodiment 3

[0031] Add 49kg of deionized water to the reactor, add 3kg of sodium polyacrylate, 8kg of fatty alcohol polyoxyethylene ether and 40kg of zinc stearate under stirring at a stirring speed of 2000 r / min, and then use a pipeline shearer to 9000r / min Stir at a stirring speed of min for 40 minutes at a high speed to completely emulsify and disperse the materials in the reactor; then add 0.1kg of self-emulsifying silicone oil defoamer and 0.1kg of dichlorodimethylhydantoin preservative, and mechanically stir for 15 minutes The resulting mixture is input into a horizontal sand mill and ground for 15 minutes, and then filtered through a 1000-mesh ultrasonic vibrating sieve to obtain a zinc stearate aqueous solution with a viscosity of 75mPa S, an average particle size of 3.8 μm, and a solid content of 45wt%. Dispersions.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous zinc stearate dispersion liquid. The aqueous zinc stearate dispersion liquid is prepared from the following components by weight: 35 to 45% of zinc stearate, 4 to 10% of an emulsifier, 1 to 4% of a dispersant, 0.1 to 0.5% of a defoaming agent, 0.1 to 0.3% of an antiseptic and 40.2 to 59.8% of water, wherein the content of the above-mentioned components sums to 100%. The invention further discloses a preparation method for the aqueous zinc stearate dispersion liquid. The aqueous zinc stearate dispersion liquid provided by the invention has the advantages of a small particle size, high solid content, small viscosity, good stability, no toxicity, environment friendliness and an ideal lubrication effect. The preparation method for the aqueous zinc stearate dispersion liquid is simple, easy to operate and beneficial for industrialized application and enables production cost to be reduced.

Description

technical field [0001] The invention relates to a zinc stearate water-based dispersion and a preparation method thereof. The zinc stearate water-based dispersion is mainly used as a rubber release agent, a papermaking coating lubricant, a sensitizer for heat-sensitive paper, and a water-based coating. Auxiliary. Background technique [0002] As a lubricant, zinc stearate is widely used in industries such as rubber, paper making, paint and cosmetics. Since zinc stearate is insoluble in water and is dispersed in the system in the form of particles, the particle size directly affects the dispersion effect of active ingredients. Usually, the particle size is large, difficult to disperse and easy to precipitate, and the use effect is not ideal, so it is generally made into an aqueous dispersion to give full play to its effect. [0003] At present, there are very few manufacturers producing zinc stearate water-based dispersions. Most of the products produced have large particle ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/14C09D7/12
Inventor 杜德光葛巧谊李明李晋张丽旭徐郑兵
Owner 肇庆市至立自动化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com