Preparation method of coal ash-resin composite material suitable for extrusion molding

A resin composite material, extrusion molding technology, applied in the field of building materials, can solve the problems of low technical content, complex process flow, high application cost, and achieve the effect of low process conditions

Inactive Publication Date: 2013-06-26
SHAANXI UNIV OF TECH
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing fly ash utilization technologies are mainly concentrated in the fields of construction, agriculture, chemical industry, sewage treatment, etc. Most of the applied technologies are not high in technical content, but some technologies with high technical content cannot be used due to high application cost and complicated process flow. widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be described in detail below in conjunction with specific embodiments.

[0012] 1. Materials, Reagents and Equipment

[0013] 1) The materials and reagents used are as follows:

[0014] Fly ash, fine ash, Hanzhong Zinc Industry Co., Ltd.;

[0015] Anhydrous ethanol, chemically pure, Xi'an Miura Fine Chemical Factory;

[0016] Silane coupling agent KH-550, analytically pure, Shanghai Yaohua Chemical Factory;

[0017] Polyvinyl chloride (PVC powder), S-700, Tianjin Polymer Materials Co., Ltd.;

[0018] Dibutyl phthalate (DBP), chemically pure, Xi'an Chemical Pharmaceutical Co., Ltd.;

[0019] Zinc oxide, chemically pure, Shanghai Chemical Reagent Products Factory;

[0020] Calcium stearate, chemically pure, Shanghai Chemical Reagent Products Factory;

[0021] Low-density polyethylene (LDPE), LD150, Yanshan Petrochemical Co., Ltd.;

[0022] Triphenyl phosphate, analytically pure, Tianjin Zhiyuan Chemical Reagent Co., Ltd.;

[0023] Ethyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a coal ash-resin composite material suitable for extrusion molding. The method comprises the following steps of: surface modification of coal ash; preparation of the coal ash-resin composite material; and extrusion molding of the coal ash-resin composite material, wherein the temperatures of three-sectional screws are 165 DEG C, 185 DEG C and 180 DEG C respectively; the temperature of a nozzle is 180 DEG C; the rotating speed of the screw is 10-15rpm (revolutions per minute); and a sample is obtained after being cooled by water. The coal ash-resin composite material suitable for extrusion molding is formed through the following processes: performing surface modification on the coal ash of which the granularity is 200 meshes, and compounding the coal ash subjected to surface modification with resins of polrvinyl chloride (PVC), low-density polyethylene (LDPE) and the like, and assistants such as chlorinated polyethylene (CPE), ethylene-vinyl acetate (EVA), triphenyl phosphate and calcium stearate.

Description

technical field [0001] The invention relates to building material technology, in particular to a method for preparing a fly ash-resin composite material suitable for extrusion molding. Background technique [0002] The fly ash component contains a large amount of SiO 2 and Al 2 o 3 , has high industrial reuse value. The fine ash particle size of fly ash produced by Hanzhong Zinc Industry Co., Ltd. is above 200 mesh, accounting for 90%. After surface modification, it can form a good interface with resin, which can be used for the development of fly ash-resin composite materials . Fly ash-resin composite materials can be used in door and window frames, building decoration, wall sound insulation and insulation layers, etc., which can not only bring economic benefits to enterprises, but also protect the ecological environment and generate social benefits. [0003] The existing fly ash utilization technologies are mainly concentrated in the fields of construction, agricultur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/06C08L23/08C08L33/04C08L23/28C08K13/06C08K9/06C08K9/04C08K3/36C08K3/22C08K5/12C08K5/098C08K5/09C08K5/523B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895B29C2948/92904
Inventor 董金虎
Owner SHAANXI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com