Polyamide composite material with high glowing filament temperature and preparation method and application thereof
A flame retardant polyamide and high glow wire technology, applied in the field of modified polymer new materials, can solve the problems of large specific gravity and low tracking index of halogen-based flame retardant polyamide composite materials, and achieve easy industrial production, specific gravity Light, light color effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] 1. Source of raw materials:
[0022] PA6 was purchased from Taiwan Jisheng, the model is TP-4208, and the relative viscosity is 2.4.
[0023] EBS was purchased from Jinyi Chemical Technology, model EBA-60.
[0024] 2. Raw material formula:
[0025] PA6 59.1%, Melamine Cyanurate 15%, EBS 0.3%, Antioxidant 1098 0.3%, Antioxidant 168 0.3%, and Talc 25%.
[0026] 3. Preparation method:
[0027] Add melamine cyanurate, EBS and antioxidant into a high-speed mixer and mix evenly, then take out the mixture. Add PA6 from the main feeding port of the twin-screw extruder, add the mixture at the first side feeding port, and then add talc powder at the second side feeding port, so that all materials are mixed evenly in the twin-screw extruder , extruded, cooled, and pelletized to obtain a high glow wire temperature flame-retardant polyamide composite material; the extrusion temperature from the feed section to the machine head is: 210°C, 230°C, 250°C, 250°C, 240°C, 235°C ℃, 230...
PUM
Property | Measurement | Unit |
---|---|---|
comparative tracking index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com