Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High-strength thermal insulating epoxy resin composition

An epoxy resin and high-strength technology, which is applied in the field of high-temperature-resistant and high-strength thermal insulation materials, can solve the problems of thermal bridge transmission and low strength of thermal insulation materials, and achieve the effects of reducing thermal bridges, significant energy saving effects, and preventing thermal bridges

Inactive Publication Date: 2013-05-22
CEEC SHANXI ELECTRIC POWER EXPLORATION & DESIGN INST
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a high-strength heat-insulating epoxy resin composition, which solves the technical problems that the heat-insulation materials used in the existing heat-transporting pipeline support are not high in strength and easily form heat bridge transfer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength thermal insulating epoxy resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A high-strength heat-insulating epoxy resin composition, based on 100 parts by weight, contains the following substances: 60-80 parts of epoxy resin, 15-30 parts of glass fiber filaments, 2-10 parts of microporous silicic acid Calcium, 1-3 parts of curing agent, 1-3 parts of accelerator.

[0014] The epoxy resin is 65-75 parts, the glass fiber filament is 20-30 parts, the microporous calcium silicate is 5-8 parts, and the curing agent is 2-3 parts. The accelerator is 2-3 parts.

[0015] A preparation method of a high-strength heat-insulating epoxy resin composition, comprising the following steps:

[0016] The first step, based on 100 parts by weight, take 60-80 parts of epoxy resin, 15-30 parts of glass fiber filaments, 2-10 parts of microporous calcium silicate, 1-3 parts of curing agent, 1 - 3 parts of Accelerator;

[0017] The second step is to put 60-80 parts of epoxy resin and 2-10 parts of microporous calcium silicate into the mixer, stir to make it evenly mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength thermal insulating epoxy resin composition used for solving the technical problems that the thermal insulating material used by an existing supporting saddle for a heat transport pipeline is not high in strength and is easily subjected to heat bridge transfer. The composition comprises the following substances based on 100 parts by weight: 60-80 parts of epoxy resin, 15-30 parts of glass fiber yarn, 2-4 parts of microporous calcium silicate, 1-3 parts of curing agent, and 1-3 parts of accelerating agent. A reinforced fiber and an epoxy resin based composite material are presoaked in a proportion, hot-pressed, and then prepared to a platy insulation pad or an insulation pad in a needed shape. The composition disclosed by the invention can be applied to the pipeline supporting saddle to function as a part of a bearing and thermal insulating structure of the pipeline supporting saddle so as to effectively prevent and reduce the occurrence of a heat bridge phenomenon on the supporting saddle for the heat transport pipeline, and the energy-saving effect is obvious.

Description

technical field [0001] The invention relates to a high-temperature-resistant and high-strength heat insulation material with a temperature resistance of 150°C, which is mainly used for heat insulation in the support of directly buried heat transmission pipelines or in the support of overhead heat transmission pipelines, and meets the requirements of sliding heat transmission pipelines. The strength requirements and thermal insulation requirements of the heat insulation material for the support or the fixed support of the heat transmission pipeline. Background technique [0002] At present, the fixed support or sliding support of the heat transfer pipeline that transports steam or hot water is generally made of steel. The steam or hot water in the heat transfer steel pipe transfers heat to the support through the baffle plate and the fixed support on it, forming a thermal bridge transfer and causing heat loss. Since the fixed support of the steam or hot water pipeline must...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/00C08K13/04C08K7/14C08K7/26
Inventor 胡兰青刘冲杨国红贺兴旺梁世俊叶文波曹媛任彩玮马静
Owner CEEC SHANXI ELECTRIC POWER EXPLORATION & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com