High-property epichlorohydrin rubber gasket and preparation method thereof

A chlorohydrin rubber and gasket technology, applied in the field of gaskets, can solve the problems of unsatisfactory sealing effect, low strength, poor wear resistance, etc., and achieve the effects of excellent effect, good corrosion resistance and good wear resistance.

Inactive Publication Date: 2013-03-27
ANHUI RONGDA VALVE
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing neoprene gaskets have defects such as unsatisfactory sealing effect, poor wear resistance, and low strength, which are far from meeting the actual requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-property epichlorohydrin rubber gasket and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0015] A kind of high-performance epichlorohydrin rubber gasket, the weight portion of its composition raw material is: chlorohydrin rubber H45 140 parts, Butyl rubber CBK139 12 parts, 15 parts of SG-6 PVC resin, 4 parts of propylene glycol sebacate polyester, 5 parts of acetyl triethyl citrate, 3 parts of dibutyl maleate, bis Isooctyl Thioglycolate 1.6 parts of di-n-octyl tin, 1.8 parts of dibasic lead phosphite, 4 parts of zinc oxide, 1.5 parts of zinc stearate, 36 parts of nano-calcium carbonate, 18 parts of nano-clay, 12 parts of carbon black N220, and quick-pressed carbon black N660 32 parts, 1.8 parts of bis(dioctyloxypyrophosphate) ethylene titanate, 0.8 parts of antioxidant 168, 1.5 parts of 3-aminopropyltrimethoxysilane, 0.6 parts of crosslinking agent TAC, silane coupling 1.5 parts of joint agent KH550, 1 part of accelerator TMTD, 2 parts of accelerator TETD, 0.8 parts of accelerator CBS, 1.5 parts of anti-aging agent TPPD, 2 parts of anti-aging agent NBC, 1.5 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-property epichlorohydrin rubber gasket. The gasket comprises the following raw materials in parts by weight: 135-145 parts of epichlorohydrin rubber H45, 10-15 parts of butyl rubber CBK139, 10-15 parts of SG-6 type PVC (polyvinyl chloride) resins, 3-5 parts of propanediol sebacate polyester, 3-5 parts of acetyl triethyl citrate, 2-4 parts of dibutyl maleate, 1-2 parts of isooctyl dimercaptoacetate di-n-octyl tin and the like. The gasket has the beneficial effects that the gasket has good high temperature resistance, sealability, flame retardance and corrosion resistance and can work in such medias as acid, alkali and oil for a long time; the volume and hardness of the gasket are small in variation; the gasket does not adhere to metal surfaces; and the gasket has small friction coefficient and good abrasion resistance and has the advantages of softness of bonding with sealing surfaces, good weathering aging and ozone aging resistance, durability and the like.

Description

technical field [0001] The invention relates to a sealing gasket, in particular to a high-performance chlorohydrin rubber sealing gasket and a preparation method thereof. Background technique [0002] Chlorohydrin rubber gasket is a material used for sealing inside machinery, equipment, pipelines, etc. Its characteristics are: good heat aging resistance and ozone resistance, flex resistance, good elasticity, oil resistance, solvent resistance, combustion resistance, low air permeability, good adhesion, etc., so the comprehensive performance is better than nitrile rubber and chloroprene Rubber, the price is lower than fluorine rubber and silicone rubber, widely used in defense industry and civilian industry. However, the existing neoprene gasket has defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore research and develop a kind of high-performance chlorohydrin rubber sealing gask...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L71/03C08L23/22C08L27/06C08L67/02C08K13/06C08K9/02C08K3/26C08K3/34C08K3/22C08K3/04B29C35/02
Inventor 胡光荣
Owner ANHUI RONGDA VALVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com