Epoxy acrylate composite emulsion and preparation method thereof

A technology of epoxy acrylate and composite emulsion, applied in the direction of coating, can solve the problems of poor environmental protection of coatings, and achieve the effects of strong environmental protection, improved stability and increased cross-linking degree

Active Publication Date: 2015-05-20
HUIZHOU CITY HUIYANG DISTRICT JIATAI PAINT CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional preparation process often uses organic solvents to dissolve epoxy resin, which makes the environmental protection of the coating poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Under the conditions of 75° C. and 750 r / min, 4 parts of sodium dodecyl sulfate (SDS) and 0.5 parts of ammonium persulfate (APS) were stirred in 40 parts of distilled water evenly. Prepare a prepolymer with 20 parts of butyl acrylate (BA) and 10 parts of ethylene-ethyl acrylate (EEA) as raw materials, and react for 2 hours. Add 10 parts of diluted monomer acrylic acid (AA) to dilute the prepolymer for 30min. Raise the temperature to 92°C, increase the speed to 1600r / min, add 3 parts of E-44 type epoxy resin for crosslinking modification, and react for 1.5h. Sodium bicarbonate was added to adjust the pH value of the system to 7, and the reaction was stirred for 30 minutes to obtain an epoxy acrylate composite emulsion.

[0016] The coagulation rate of the emulsion is 8.68%, and the water absorption rate of the emulsion film is 17.21%.

Embodiment 2

[0018] Under the conditions of 75° C. and 750 r / min, 4 parts of sodium dodecyl sulfate (SDS) and 0.5 parts of ammonium persulfate (APS) were stirred in 40 parts of distilled water evenly. Prepare a prepolymer with 20 parts of butyl acrylate (BA) and 10 parts of ethylene-ethyl acrylate (EEA) as raw materials, and react for 2 hours. Add 10 parts of diluted monomer acrylic acid (AA) to dilute the prepolymer for 30min. Raise the temperature to 92°C, increase the speed to 1600r / min, add 4 parts of E-44 type epoxy resin () to carry out crosslinking modification, and react for 1.5h. Sodium bicarbonate was added to adjust the pH value of the system to 7, and the reaction was stirred for 30 minutes to obtain an epoxy acrylate composite emulsion.

[0019] The coagulation rate of the emulsion is 5.89%, and the water absorption rate of the emulsion film is 12.89%.

Embodiment 3

[0021] Under the conditions of 75° C. and 750 r / min, 4 parts of sodium dodecyl sulfate (SDS) and 0.5 parts of ammonium persulfate (APS) were stirred in 40 parts of distilled water evenly. Prepare a prepolymer with 20 parts of butyl acrylate (BA) and 10 parts of ethylene-ethyl acrylate (EEA) as raw materials, and react for 2 hours. Add 10 parts of diluted monomer acrylic acid (AA) to dilute the prepolymer for 30min. Raise the temperature to 92°C, increase the speed to 1600r / min, add 5 parts of E-44 type epoxy resin for cross-linking modification, and react for 1.5h. Sodium bicarbonate was added to adjust the pH value of the system to 7, and the reaction was stirred for 30 minutes to obtain an epoxy acrylate composite emulsion.

[0022] The coagulation rate of the emulsion is 3.02%, and the water absorption rate of the emulsion film is 12.02%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to an epoxy acrylate composite emulsion and a preparation method thereof. The preparation method comprises the following steps: preparing a prepolymer from butyl acrylate (BA) and ethylene-ethyl acrylate (EEA), diluting with an acrylic acid diluter, modifying with epoxy resin (E-44), adding sodium lauryl sulfate (SDS), and regulating the pH value to prepare the epoxy acrylate composite emulsion. The epoxy acrylate composite emulsion has the advantages of low condensation rate, high environment friendliness and favorable water resistance.

Description

technical field [0001] The invention relates to an epoxy acrylate composite emulsion and a preparation method thereof, belonging to the field of chemical industry. technical background [0002] Epoxy resin has excellent adhesion, thermal stability, and chemical resistance, and is mainly used in anti-corrosion coatings, adhesives, and composite materials. Acrylic resin has excellent gloss and outdoor aging resistance, and is widely used in general industrial equipment and automobile industry. But there are also many defects in their water-based coatings, so people try to organically combine the two coatings to form composite emulsions. The preparation of composite emulsion by free radical graft copolymerization of epoxy-acrylate is a relatively common method, and its free radical graft copolymerization mechanism has been confirmed. However, the traditional preparation process often uses organic solvents to dissolve epoxy resins, making the coatings less environmentally frie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/10C09D151/08
Inventor 张明
Owner HUIZHOU CITY HUIYANG DISTRICT JIATAI PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com