Easy-welding tempering high-strength steel plate for ocean platform and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-strength steel plate and offshore platform technology, applied in the field of low-alloy high-strength welded structural steel manufacturing, can solve the problems of narrow specification range and inability to meet the market demand for thick plates, achieve less precious metal content, improve equipment performance and service life, The effect of reducing production costs
Inactive Publication Date: 2015-01-07
WUYANG IRON & STEEL +1
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] As the amount of high-strength steel in the domestic construction machinery industry gradually increases, some domestic steel manufacturers produce steel plates of this level, but due to the narrow range of specifications, all are below 60mm, which cannot meet the growing market demand for thick plates
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] The composition of the quenched and tempered high-strength steel in this example is as follows: C 0.14%, Si 0.27%, Mn 1.16%, P 0.015%, S 0.001%, Mo 0.41%, Ni 1.2%, Cr 1.04% , Nb 0.024%, V 0.033%, B 0.002%, Ti 0.015%, Al 0.064%, the balance is Fe and unavoidable impurities, rolled into 88mm steel plate.
[0023] Its mechanical properties: yield strength: 820MPa, tensile strength: 880MPa, A is 20%, -27°C impact energy AKV (longitudinal): 119, 129, 159J, -37°C impact energy AKV (longitudinal): 131, 126, 100J.
Embodiment 2
[0025] The composition of the quenched and tempered high-strength steel in this example is as follows: C 0.14%, Si 0.25%, Mn 1.15%, P 0.012%, S 0.002%, Mo 0.43%, Ni 1.25%, Cr 1.03% , Nb 0.027%, V 0.035%, B 0.0023%, Ti 0.019%, Al 0.050%, and the balance is Fe and inevitable inclusions. Ceq is 0.56%, rolled into 88mm steel plate.
[0026]Its mechanical properties: yield strength: 825MPa, tensile strength: 895MPa, A is 18%, -27°C impact energy AKV (longitudinal): 199, 199, 180J, -37°C impact energy AKV (longitudinal): 192, 190, 167J.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an easy-welding tempering high-strength steel plate for an ocean platform and a production method thereof. The easy-welding tempering high-strength steel plate for the ocean platform is prepared by the following chemical compositions in percent by weight: not higher than 0.18 percent of C, 0-0.15 to 0.35 percent of Si, 0.95 to 1.30 percent of Mn, not higher than 0.035 percent of P, not higher than 0.01 percent of S, 1.20 to 1.50 percent of Ni, 1.00 to 1.50 percent of Cr, 0.4 to 0.6 percent of Mo, not higher than 0.05 percent of Nb, 0.03 to 0.08 percent of V, not higher than 0.020 percent of Ti, not higher than 0.003 percent of B, 0.020 to 0.085 percent of Alt, and the balance of Fe and inevitable impurities. The thickness of the easy-welding tempering high-strength steel plate for the ocean platform is from 60 to 100 mm. The easy-welding tempering high-strength steel plate for the ocean platform is prepared by the following method: smelting-vacuum decarburization-LF furnace refining-pouring-cleaning-heating-rolling-water cooling after rolling-tempering-inspection and storage. The easy-welding tempering high-strength steel plate for the ocean platform has an outstanding combination property, is used for engineering machinery, has high surplus amount of impact toughness, can be widely used for engineering supports and other projects needing high-strength steel plates, and has a great application prospect. The easy-welding tempering high-strength steel plate for the ocean platform has simplicity in rolling technology, wide scope of tempering technology and easiness in operation, and is suitable for the production of the steel plant.
Description
technical field [0001] The invention belongs to the field of manufacturing low-alloy high-strength welded structural steel, and in particular relates to an easy-weld quenched and tempered high-strength A517GrQ Modified steel plate for offshore platforms, and also relates to a production method of the easy-weld quenched and tempered high-strength steel plate. Background technique [0002] Traditional quenched and tempered steel has the disadvantages of high carbon content, high alloy content and high carbon equivalent, which bring about high cost and unsatisfactory welding performance. Most of the high-strength steel in the domestic construction machinery industry comes from imports such as American A514Gr.B and DILLMAX690 steel plates produced by German DILLINGER Steel Company. The content of C (0.18%), Cr (1.50%), Ni ( 1.80%) alloy content is higher, and the cost price of steel plate rises. The prices of the above-mentioned imported steels are generally high. [0003] As ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.