Nano-filler modified bi-component polysulfide hollow glass elastic sealant and its preparation method

A nano-filler, elastic sealing technology, applied in chemical instruments and methods, other chemical processes, etc., can solve problems such as insufficient anti-ultraviolet performance, and achieve good anti-ultraviolet performance.

Inactive Publication Date: 2014-08-13
上海渊信建筑材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, polysulfide sealant is the most widely used sealing material for insulating glass in doors and windows. The existing polysulfide sealant for insulating glass still has insufficient UV resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-filler modified bi-component polysulfide hollow glass elastic sealant and its preparation method
  • Nano-filler modified bi-component polysulfide hollow glass elastic sealant and its preparation method
  • Nano-filler modified bi-component polysulfide hollow glass elastic sealant and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The parts taken are parts by weight, 85 parts of liquid polysulfide rubber with an average molecular weight of 4000, 50 parts of phthalates, 100 parts of calcium carbonate, 80 parts of active nano-calcium carbonate, γ-(2,3 propylene oxide ) Add 2.8 parts of propyltrimethoxysilane into the high-speed disperser, heat, stir and vacuumize. When the vacuum degree reaches 0.09Mpa, record the time, stir at a speed of 600-800 rpm for 60 minutes, control the glue temperature below 85°C, transfer the dehydrated material to a hydraulic precision three-roller grinder for grinding, and then transfer to a high-speed Dispersing machine, the speed is controlled at 600 rpm to 800 rpm, stirred and vacuumed for 60 minutes to obtain component A of the nano-filler modified two-component polysulfide hollow glass elastic sealant.

[0014] With 60 parts of active manganese dioxide, 110 parts of phenylalkyl phthalates, 22 parts of carbon black, 5 parts of nano zinc oxide, 5 parts of accelerator...

Embodiment 2

[0016] The parts taken are parts by weight, 50 parts of liquid polysulfide rubber with an average molecular weight of 2400, 50 parts of liquid polysulfide rubber with an average molecular weight of 4000, 45 parts of butyl benzyl phthalate, 80 parts of calcium carbonate, and 100 parts of active nano calcium carbonate 3.1 parts of γ-(2,3 propylene oxide) propyltrimethoxysilane, heating, stirring and vacuumizing. When the vacuum degree reaches 0.09Mpa, record the time, stir at a speed of 600-800 rpm for 60 minutes, control the glue temperature below 85°C, transfer the dehydrated material to a hydraulic precision three-roller grinder for grinding, and then transfer to a high-speed Dispersing machine, the speed is controlled at 600 rpm to 800 rpm, stirred and vacuumed for 60 minutes to obtain component A of the nano-filler modified two-component polysulfide hollow glass elastic sealant.

[0017] With 80 parts of active manganese dioxide, 160 parts of butyl benzyl phthalate, 30 part...

Embodiment 3

[0019] The parts taken are parts by weight, with 115 parts of liquid polysulfide rubber with an average molecular weight of 2400, 35 parts of butyl benzyl phthalate, 95 parts of calcium carbonate, 95 parts of active nano calcium carbonate, γ-(2,3 propylene oxide ) Add 4 parts of propyltrimethoxysilane into the high-speed disperser, heat, stir and vacuumize. When the vacuum degree reaches 0.09Mpa, record the time, stir at a speed of 600-800 rpm for 60 minutes, control the temperature of the glue below 85°C, transfer the dehydrated material to a hydraulic precision three-roller grinder for grinding, and then transfer to a high-speed Dispersing machine, the speed is controlled at 600 rpm to 800 rpm, stirred and vacuumed for 60 minutes to obtain component A of the nano-filler modified two-component polysulfide hollow glass elastic sealant.

[0020] With 100 parts of active manganese dioxide, 180 kilograms of phenyl phthalates, 35 parts of carbon black, 2 parts of nano zinc oxide, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nano-filler modified bi-component polysulfide hollow glass elastic sealant. It is characterized in that the elastic sealant consists of an A component composed of liquid polysulfide rubber, first plasticizer, filler, nano-filler and coupling agent, and a B component composed of oxidizer, second plasticizer, pigment and accelerant. Preparation method of the elastic sealant includes adding the liquid polysulfide rubber, the first plasticizer, the nano-filler, the filler and the coupling agent into high-speed dispersion machine, heating, stirring, vacuumizing, stirring at 600-800 r / min for 180 min when degree of vacuum achieves 9 MPa, and controlling sealant temperature below 85 degrees, to obtain the A component; and uniformly mixing the oxidizer, the second plasticizer, the pigment and the accelerant on tri-roller grinder until obtained mixture is uniform and fine, and degassing, to obtain the B component. The invention has good ultraviolet ray resistance, and has properties satisfying operation requirements of hollow glass.

Description

technical field [0001] The invention relates to an elastic sealing material for the second sealing of hollow glass (energy-saving glass), in particular to a nano-filler modified two-component polysulfide elastic sealant for hollow glass. Background technique [0002] At present, polysulfide sealant is the most widely used sealing material on insulating glass for doors and windows. The existing polysulfide sealant for insulating glass still has insufficient anti-ultraviolet performance. The current formula is mainly composed of the following materials: A component, liquid polysulfide rubber, butyl benzyl phthalate, calcium carbonate; B component, manganese dioxide, carbon black, butyl benzyl phthalate, accelerator and so on. According to the ratio of A:B=10:1, the hollow glass sample is made by mixing evenly. After 14 days of curing under standard conditions, it is placed on the roof. After a year of sunlight, wind and rain, cracks will appear on the surface of the glue. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J181/04C03C27/10C09K3/10
Inventor 刘桂发
Owner 上海渊信建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com