2500 m<3> blast furnace main iron runner castable

A castable and main iron groove technology, applied in the field of refractory castables, to reduce material consumption, solve the problem of iron groove spalling, and have good acid resistance.

Inactive Publication Date: 2012-10-31
HENAN POLYTECHNIC UNIV
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of castable with brown corundum as the main component has poor thermal shock resistance, which is easy to cause thermal spalling and structural spalling, which greatly increases the frequency of repairing iron trenches and brings great hidden dangers to the stable, safe and continuous production of blast furnaces. Improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 2500 m&lt;3&gt; blast furnace main iron runner castable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Use formula 1 to prepare blast furnace main iron trough: mix the ingredients according to formula 1 and stir it with a mixer to make castables, add castables to the mold installed in the main iron trough where molten iron flows, and demould after natural curing for 1 hour to obtain blast furnace main iron trough .

Embodiment 2

[0022] Use formula 2 to prepare the main iron channel of blast furnace: mix the ingredients according to formula 2 and stir them with a mixer to form castables, then add castables to the mold installed in the main iron channel through which molten iron flows, and demould after natural curing for 1 hour to obtain the main iron channel of blast furnace .

Embodiment 3

[0024] Use formula 3 to prepare blast furnace main iron trough: mix ingredients according to formula 3 and stir them into castables with a mixer, add castables to the mold installed in the main iron trough where molten iron flows through, and demould after natural curing for 2 hours to obtain blast furnace main iron trough . The specific performance indicators are shown in the table below

[0025]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a 2500 m<3> blast furnace main iron runner castable and belongs to the field of refractory castables. The 2500 m<3> blast furnace main iron runner castable comprises, by weight, 50-55 parts of special grade alumina, 1-8 parts of mullite hollow spheres, 3-10 parts of zirconium silicate, 10-25 parts of zinc-aluminum spinel powders, 10-15 parts of carbon composite materials, 3-10 parts of aluminum oxide micro powders, 1-2 parts of Guangxi mud, 0.1-0.2 part of sodium tripolyphosphate, 0.05-0.2 part of metal aluminum powders and 4-10 parts of silicon dioxide sol suspension liquids. A blast furnace main iron runner prepared by the castable has the advantages of being good in thermal shock stability, anti-stripping and long in service life.

Description

technical field [0001] The invention relates to a 2500m 3 The utility model relates to a blast furnace main iron trough castable, which belongs to the field of refractory castables. [0002] Background technique [0003] The existing main iron trough castable is ordinary Al 2 o 3 -SiC-C castables, but ordinary Al 2 o 3 -SiC-C main iron trough castables are used in blast furnaces, and the amount of one-time passing iron is 120,000 tons. With the strengthening of smelting, the demand for increasing production is becoming more and more prominent, and the requirements for the amount of iron passing through the main iron channel are becoming more and more stringent. However, due to the poor thermal shock resistance of the iron channel, it is not resistant to erosion, which leads to product peeling, which is the lifespan. The main reason for the shortness. [0004] CN102101782A discloses a castable for main iron trough, said castable is made of alumina, brown corundum, SiC, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 山国强
Owner HENAN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More