Cotton fiber, aloe fiber and viscose fiber blended yarn and yarn spinning process thereof

A viscose fiber and aloe vera fiber technology is applied in the field of spinning, which can solve the problems of poor elastic recovery performance, poor dimensional stability, poor alkali and acid resistance, etc., and achieves the effects of less yarn defects, uniform evenness and good elasticity.

Active Publication Date: 2015-02-25
山东超越纺织有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its modulus is lower than that of cotton, it is easy to deform under a small load, and its elastic recovery performance is poor, so the fabric is easy to elongate and has poor dimensional stability
The chemical composition of viscose fiber is similar to that of cotton, so it is more resistant to alkali than acid, but its resistance to alkali and acid is worse than that of cotton

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cotton fiber, aloe fiber and viscose fiber blended yarn and yarn spinning process thereof
  • Cotton fiber, aloe fiber and viscose fiber blended yarn and yarn spinning process thereof
  • Cotton fiber, aloe fiber and viscose fiber blended yarn and yarn spinning process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. Raw materials: cotton fiber with a fiber content blending ratio of 50%, aloe fiber with 30%, and viscose fiber with 20%. The cotton fiber grade is 230A Xinjiang fine-staple cotton, the aloe fiber specification is 1.67dtex*38mm, and the viscose staple fiber specification is 1.33dtex*38mm. The mixing method of the three-component yarn composed of three kinds of raw materials is strip mixing.

[0024] Yarn gauge: 14.7tex.

[0025] 2. Spinning process flow: FA002A automatic plucking machine --- A035D mixed cotton opener --- FA106 cotton opener --- A092E cotton feeder --- A076E lapping machine --- A186G comb Cotton machine --- aloe vera and viscose drawing frame + combed sliver --- FA311 drawing frame --- THF4433 roving frame --- FA506 spinning frame --- SMARO automatic winding machine.

[0026] 3. Process configuration and production measures of each process.

[0027] 3.1 Start cleaning process. Aloe vera and viscose fibers have no impurities and only a few defects, su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses cotton fiber, aloe fiber and viscose fiber blended yarn and a yarn spinning process thereof. The blended yarn comprises the components by fiber-content blended ratio: 50 percent of cotton fiber, 30 percent of aloe fiber and 20 percent of viscose fiber, and the fibers are spun into the yarn through a blending process. The aloe fiber and the viscose fiber are subjected to coating mixing, and card slivers formed through working procedures such as blowing and cotton carding and cotton-fiber fine combing slivers are subjected to sliver mixing to form the yarn. A compact Siro spinning technique and the reasonable raw material collocation are adopted, so that the problems that the fiber of the aloe fiber is short, the viscose fiber is easy to deform, the elastic recovery properties are poor, the abrasive resistance is poorer, the fiber is not resistant to acid and the like are solved, and the advantages of the aloe fiber, the viscose fiber and the cotton fiber are exerted. A mixing mode of one pre-drawing and three mixing-drawing is adopted, the accurate blending ratio is favored, and the components are uniform. The produced single yarn evenness is uniform, the single yarn strength is high, the neps are less, and the yarn defects are less.

Description

technical field [0001] The invention relates to the technical field of spinning, in particular to a blended yarn of cotton fiber, aloe fiber and viscose fiber and a spinning process thereof. Background technique [0002] With the development of social economy and the improvement of people's living standards, people's consumption concept is constantly updated, and people pay more and more attention to the quality of life and living environment, and the functional requirements for clothing are also getting higher and higher, especially for the health care of clothing. , feel, quality and other aspects of the requirements are also constantly improving. [0003] Aloe is a perennial succulent herb with a long history of cultivation. As a pure natural green plant integrating medicine, beauty, health care, food and ornamental, aloe has long been favored by consumers in developed countries such as Japan and the United States. Constantly sought after, and quickly set off an "aloe ve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04
Inventor 侯芝富徐淑莲潘静吕延敏孟祥华宋圣山郭俊霞王海燕李爱华唐红常江袁贞学高新宋军
Owner 山东超越纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products