A kind of cotton fiber, viscose fiber blended yarn and its manufacturing method

A technology of viscose fiber and blended yarn, which is applied in the direction of fiber mixing, fiber treatment, textiles and papermaking, etc. It can solve the problems of poor elastic recovery performance, poor size stability, poor alkali and acid resistance, etc., and achieve less yarn defects , Fewer neps, evenness

Active Publication Date: 2016-03-23
ZHEJIANG SHUANGDUN TEXTILE TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its modulus is lower than that of cotton, it is easy to deform under a small load, and its elastic recovery performance is poor, so the fabric is easy to elongate and its dimension stability is poor
The chemical composition of viscose fiber is similar to that of cotton, so it is more resistant to alkali than acid, but its resistance to alkali and acid is worse than that of cotton

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention is preferably specifically described below through examples, but the protection scope of the present invention is not limited thereto.

[0016] 1. Raw materials: cotton fiber with a fiber content blending ratio of 50%, and viscose fiber with a blend ratio of 50%. The cotton fiber grade is grade 2 Xinjiang fine-staple cotton, and the specification of viscose staple fiber is 1.67dtex-38mm.

[0017] 2. Spinning process flow: FA002A automatic plucking machine-A035D mixed cotton opener-FA106 cotton opener-A092E cotton feeder-A076E lapping machine-A186G carding machine-A311 drawing frame-THF4433 Roving frame-FA506 spinning frame-SMARO automatic winding machine.

[0018] 3. Process configuration and production measures of each process.

[0019] 3.1 Carding process.

[0020] Cotton fiber carding process: Raw sliver weight is 18.56g / 5m, adopt the principle of "less grasping, light beating, early fall and less fall" to properly increase the cylinder speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cotton fiber and viscose blended yarn and a spinning technology thereof. The blended yarn comprises cotton fiber and viscose, and the fiber blending ratio of the cotton fiber to the viscose is 1:1; and the fibers are spun into yarns through a blending process. Card slivers formed by the processes such as blowing and carding and cotton fiber combed silvers are subjected to silver blending to form yarns, and a compact Silo spinning technology and the reasonable matching of raw materials are adopted, so that the problems such as the viscose can be deformed easily, has low elastic recovery performance and relatively low wear resistance, and is not acidproof are solved, and the advantages of the viscose and the cotton fiber are exerted. A pre-doubling and mixed doubling mixing mode is adopted, so that the accuracy of the blending ratio and the uniformity of ingredients are facilitated, produced single yarns have uniform yarn levelness and high strength, and few neps and yarn faults are produced.

Description

technical field [0001] The invention relates to the technical field of spinning, in particular to a method for blending cotton fiber and viscose fiber. Background technique [0002] With the development of social economy and the improvement of people's living standards, people's consumption concept is constantly updated, and people pay more and more attention to the quality of life and living environment, and the functional requirements for clothing are also getting higher and higher, especially for the health care of clothing. , feel, quality and other aspects of the requirements are also constantly improving. Viscose fiber refers to a-cellulose extracted from cellulose raw materials such as wood and plant stalks, or artificial fibers made from cotton linters, processed into spinning stock solution, and then wet-spun. Viscose fiber has good hygroscopicity, and the moisture regain is about 13% under general atmospheric conditions. After absorbing moisture, it swells signif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D01G13/00
Inventor 王明龙易建设李琪
Owner ZHEJIANG SHUANGDUN TEXTILE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products