Super strength silicate cement adhesive and preparation method thereof

A technology of cement adhesive and portland cement, which is applied in the manufacture of tools, ceramic molding machines, etc., can solve the problems that cannot satisfy the production of high-tonnage suspension porcelain insulators, and achieve good compactness, good durability, and high strength. Effect

Active Publication Date: 2012-10-10
JIANGSU SOUTH PORCELAIN INSULATOR CO LTD
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent 200910010971.3 and Patent 201110190809.1 increase the strength of the adhesive by adding water reducing agents and adjusting the composition of cement, but the maximum compressive strength is only 110MPa, which obviously cannot meet the needs of high-tonnage suspension porcelain insulator production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super strength silicate cement adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: A kind of super-strength Portland cement adhesive, the raw material composition of this adhesive and its weight content ratio are Portland cement 30.5%, quartz sand 35.2%, silicon fume 4.2%, slag 12.7%, powder Coal ash 4.2%, water reducing agent 0.9%, water 12.3%.

[0016] Among them, the cement first meets the requirements of GB175-1999, and the label is not less than 52.5 or 52.5R Portland cement; the particle size of the quartz sand is 80-120 mesh, which meets GB178-1977. The micro-aggregate is a mixture of silicon powder, slag and fly ash, and their average particle size is required to be less than 0.01 μm. The water reducer is a polycarboxylate water reducer. This experiment uses a polycarboxylate high-performance water reducer produced by Suzhou Xingbang Chemical Building Materials Co., Ltd., the model is SUNBO PC-1016, which conforms to JG / T 223-2007 .

[0017] The preparation method of the above-mentioned adhesive is as follows: first mix cement,...

Embodiment 2

[0018] Embodiment 2: basically the same as Embodiment 1, the difference is the raw material ratio of cement: Portland cement 31.4%, quartz sand 34.8%, silicon powder 4.1%, slag 12.2%, fly ash 4.1%, reducing Aqua 0.9%, water 12.5%.

Embodiment 3

[0019] Embodiment 3: basically the same as Embodiment 1, the difference is the raw material ratio of cement: Portland cement 40.0%, quartz sand 26.8%, silicon powder 3.8%, slag 11.6%, fly ash 3.8%, reducing Aqua 1.0%, water 13.0%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Graininessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a super strength silicate cement adhesive and a preparation method thereof. The adhesive is mainly prepared from the following raw materials in percentage by weight: 30 to 40 percent of cement, 25 to 43 percent of quartz sand, 9 to 24 percent of micro aggregates, 0.9 to 2 percent of water reducing agent and 11 to 14 percent of water. The preparation method comprises the following steps of firstly, uniformly mixing the cement, the micro aggregates, the water reducing agent and the quartz sand, then continuously stirring for 4 minutes and immediately forming after taking out the mixture; after the obtained product is formed, placing the obtained product into a curing box at the temperature of 35 DEG C to carry out steaming-curing under the humidity of not lower than 95 percent, demoulding after 4 to 12 hours, and placing a demoulding specimen into hot water at the temperature of 45 to 80 DEG C to carry out curing for 48 to 96 hours; and finally, testing the qualification of the product to obtain the cement adhesive. The cement adhesive disclosed by the invention has the excellent performances of excellent compaction, high strength, excellent durability and the like, is suitable for electrotechnical porcelain products such as a high-tonnage suspension type porcelain insulator and the like and has low cost.

Description

technical field [0001] The present invention relates to a super-strength cement adhesive added with micro-aggregate, specifically, the present invention relates to a silicate used in high-tonnage suspended porcelain insulator porcelain sleeves with excellent properties such as good compactness, high strength and good durability Cement binder. Background technique [0002] At present, the cement adhesive used in various domestic electric porcelain factories has much lower mechanical strength than porcelain parts and metal accessories. The cement adhesive has been paid more and more attention, especially the cement adhesive used for high-tonnage suspension porcelain insulators. mixture. Patent 200910010971.3 and Patent 201110190809.1 increase the strength of the adhesive by adding water reducing agents and adjusting the composition of cement, but the maximum compressive strength is only 110MPa, which obviously cannot meet the needs of high-tonnage suspension porcelain insulat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04B28B11/24
Inventor 杨志峰朱文浩刘少华黄蕴君余翔张超
Owner JIANGSU SOUTH PORCELAIN INSULATOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com