Iron ore sinter mixture distribution method

A technology for sintering mixtures and iron ore, which is applied in furnaces, lighting and heating equipment, furnace types, etc., can solve problems such as the inability to effectively realize fuel segregation and difficult control of magnetic field strength, and achieve improved stress conditions and moving rails, Effect of Improving Magnetic Susceptibility

Active Publication Date: 2012-09-19
CENT SOUTH UNIV
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, this device can strengthen particle size segregation and achieve magnetic material segregation at the same time, but it cannot effectively achieve fuel segregation, and there is also the problem that the magnetic field strength of the magnetic system is difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron ore sinter mixture distribution method
  • Iron ore sinter mixture distribution method
  • Iron ore sinter mixture distribution method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] See attached Figure 4 , a distributing device for iron ore sintering mixture in the present invention, comprising a round roller feeder-reflecting plate distributor, the distributing roller in the round roller feeder is provided with a permanent magnet composed of alternating polarities Magnetic system, the reflective plate in the reflective plate distributor is below the horizontal axis of the distribution roller and parallel to the tangent line passing the circumference below the horizontal axis of the distribution roller, and the axis of the reflective plate is in line with the moving direction of the sintering machine trolley The included angle α is 45°; the magnetic system is composed of 6 NdFeB permanent magnets with alternating polarities, and the magnetic field strength formed on the circumferential surface of the distribution roller is 300Gs~2000Gs, and the distribution range on the circumferential surface of the distribution roller is The contact point betwee...

Embodiment 2

[0040] See attached Figure 4 , a distributing device for iron ore sintering mixture in the present invention, comprising a round roller feeder-reflecting plate distributor, the distributing roller in the round roller feeder is provided with a permanent magnet composed of alternating polarities Magnetic system, the reflective plate in the reflective plate distributor is below the horizontal axis of the distribution roller and parallel to the tangent line passing the circumference below the horizontal axis of the distribution roller, and the axis of the reflective plate is in line with the moving direction of the sintering machine trolley The included angle α is 45°; the magnetic system is composed of 6 NdFeB permanent magnets with alternating polarities, and the magnetic field strength formed on the circumferential surface of the distribution roller is 300Gs~2000Gs, and the distribution range on the circumferential surface of the distribution roller is The contact point betwee...

Embodiment 3

[0042] See attached Figure 4 , a distributing device for iron ore sintering mixture in the present invention, comprising a round roller feeder-reflecting plate distributor, the distributing roller in the round roller feeder is provided with a permanent magnet composed of alternating polarities Magnetic system, the reflective plate in the reflective plate distributor is below the horizontal axis of the distribution roller and parallel to the tangent line passing the circumference below the horizontal axis of the distribution roller, and the axis of the reflective plate is in line with the moving direction of the sintering machine trolley The included angle α is 45°; the magnetic system is composed of 6 NdFeB permanent magnets with alternating polarities, and the magnetic field strength formed on the circumferential surface of the distribution roller is 300Gs~2000Gs, and the distribution range on the circumferential surface of the distribution roller is The contact point betwee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Magnetic field strengthaaaaaaaaaa
Magnetic field strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an iron ore sinter mixture distribution method. By adopting a mixture preparation technology of pre-mixing magnetite concentrate and coke powder and a matched mounting mode with a round roller, a magnetic system and a reflecting plate, the particle size segregation, the fuel segregation and the segregation of materials such as the magnetite concentrate and the like in the mixture distribution can be enhanced; the air permeability of a sinter bed can be further improved by enhancing the particle size segregation; through the enhancement of the fuel segregation, the heatdistribution is more reasonable, the uniform-heat sintering is realized, and the fuel usage is reduced; and through the segregation of the magnetite concentrate, the oxidation of the magnetite is sufficiently utilized to release heat, so that the heat accumulation effect is enhanced, and the fuel usage is further reduced. The method disclosed by the invention can comprehensively improve the air permeability, the heat distribution and the heat transfer condition of the sinter bed, reduce the fuel usage and obviously improve the yield and quality indexes of sinter; and the indexes such as the vertical sintering speed, the sintering machine utilization coefficient, the finished sintering product rate, the sinter tumbler strength, the reducing degree and the like can be improved to different degrees.

Description

technical field [0001] The invention discloses a method for distributing iron ore sintering mixture, which belongs to the technical field of sintering processes in the iron and steel metallurgy industry. Background technique [0002] The rapid development of the iron and steel metallurgical industry requires large-scale blast furnaces, and requires sintering production to achieve high-quality, high-yield, and low-consumption goals under the condition of thick material layers. The existing sintering production process usually consists of the following parts: preparation of sintering raw materials, batching, mixing and granulation, distribution, ignition and sintering, cooling of sintered ore, granulation, etc. [0003] The belt-type draft sintering machine is the main equipment of iron ore sintering production, which is widely used in sintering ore production. The effect of the head trolley material distribution will directly affect the production and quality indicators of si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/16F27B21/10
Inventor 李光辉张元波姜涛张树辉范晓慧李骞余正伟郭宇峰杨永斌陈许玲饶明军罗骏朱忠平李珍珍
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap