High-solid-content quick-drying water-based white primer and preparation method thereof
A water-based white primer, quick-drying technology, applied in the direction of coating, can solve the problems of poor sealing, poor storage stability of white primer, low solid content, etc., to achieve excellent sandability and filling, good Market application value and the effect of low substrate deformation rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] According to Example 1 in Table 1, water, defoamer, dispersant, wetting agent and polyurethane thickener are added to the mixing tank in sequence according to the formula weight ratio, and filler calcium carbonate, kaolin, talcum powder are added after the low-speed dispersion is uniform , and then disperse at high speed for 15min to 30min. After the fineness of the slurry is qualified, add white slurry and emulsion at a medium speed, then add film-forming aids at a uniform speed, stir to adjust the viscosity and pH value, and a high-solid Contains a fast-drying water-based white primer.
Embodiment 2
[0025] Example 2, Example 3 The preparation steps refer to Example 1.
[0026] According to relevant national standards, the basic performance of the high-solid fast-drying water-based white primer of the present invention is tested, and the test results are shown in Table 2.
[0027] Table 2 Basic performance test results of high-solid fast-drying water-based white primer
[0028] Test items Test Results state in container Milky white fluid, no caking Fineness, μm ≤40 Non-volatile matter 52±1 Grinding Easy to sand and smooth Storage stability (50℃, 7d) No abnormalities, no lumps Adhesion (cross-cut method 2mm), grade 1 Drying time 25℃, h <1.5 Viscosity, KU 65
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com